Fractures and a crack occurred in a length of excavator boom rope. Failure took place at regions where local corrosion was evident. Microscopic examination of longitudinal sections disclosed that the majority of the cracks were broad, these being typical of corrosion-fatigue fissures. In addition, cracking took the form more typical of a fatigue crack and appeared to have originated at a stress-raiser introduced by a corrosion pit on the surface of the wire. The tendency for corrosion-fatigue cracking or the formation of pits from which fatigue cracks can develop can he reduced, if not prevented, in wire ropes by regular attention to lubrication.

You do not currently have access to this chapter.
Don't already have an account? Register

2019. "Corrosion Fatigue Cracking of Wire Ropes", ASM Failure Analysis Case Histories: Construction, Mining, and Agricultural Equipment

Download citation file:


Close
Close Modal
This Feature Is Available To Subscribers Only

Sign In or Create an Account

Close Modal
Close Modal