Abstract

Leakage from the top of a fire-extinguisher case, made of 1541 steel tubing and closed by spinning was observed during testing. Three small folds were observed on the surface by visual examination and one was sectioned. A very fine transverse fissure through the section was revealed. Streaks of ferrite were observed by metallographic examination. It was concluded that cracking of the top of the fire-extinguisher case was the result of ferrite streaks formed due to metal overheating. The temperature of the metal was recommended to be controlled so that the spinning operation is done at a lower temperature to avoid formation of ferrite streaks.

You do not currently have access to this chapter.
Don't already have an account? Register

2019. "Cracking of a Fire-Extinguisher Case Because of Overheating", ASM Failure Analysis Case Histories: Processing Errors and Defects