A high-chromium white cast iron shell liner installed in an ore crusher sustained impact damage in the course of operation. Visual-optical examination revealed horizontal cracks on the surface of the liner along with particles that had fractured off. Metallographic examination indicated a heavily deformed surface layer with chip formation at the wear surface. The chemical composition of the liner was found to be Fe-2.74C-0.75Mn-0.55Si-0.51Ni-19.4Cr-1.15M. This alloy is highly resistant to abrasive wear, yet at the same time, prone to chipping because little plastic displacement will occur at the surface. The liner failed as a result of severe abrasion caused by the impact of taconite rock. This was a material-selection problem in that the wrong alloy was used for a condition not anticipated in the original choice.

You do not currently have access to this chapter.
Don't already have an account? Register

2019. "Rapid Wear of Shell Liner Due to Severe Abrasion", ASM Failure Analysis Case Histories: Failure Modes and Mechanisms

Download citation file:


Close
Close Modal
This Feature Is Available To Subscribers Only

Sign In or Create an Account

Close Modal
Close Modal