Abstract

Thermal and transformation stresses, resulting from welding, adding up with operational stresses can result in failure. Examples involving the crankshaft of a shaft-drive to produce artificial waves in a swimming pool, the joint bar of a dredger cast out of a running non-alloyed steel with 39 kg/sq mm tensile strength, which had been strengthened by welding plate strips on both sides had fractured in service; an axle tube out of 40 Mn 4 after DIN 17 200 from a paper fabrication machine, which had three short longitudinal slits distributed uniformly over its surface; welding to repair worn out bearing or fits, and a broken rear axle tube of a bus are described.

You do not currently have access to this chapter.
Don't already have an account? Register

Friedrich Karl Naumann, Ferdinand Spies, 2019. "Fatigue Fracture and Weld", ASM Failure Analysis Case Histories: Failure Modes and Mechanisms

Download citation file:


Close
Close Modal
This Feature Is Available To Subscribers Only

Sign In or Create an Account

Close Modal
Close Modal