Abstract

A nylon oil-lubricated driving gear showed pitting upon visual inspection. The pitting produced numerous surface microcracks. Further investigation (visual inspection and 37x images) supported the conclusion that failure occurred in association with large-scale fragmentation (frictional wear). No recommendations were made.

Abstract

A polyoxymethylene gear wheel that had been in operation in a boiler room failed. Investigation (visual inspection and 305x images) supported the conclusion that failure was due to postcrystallization causing considerable shrinkage. Breakdown along the crystalline superstructure started mainly at the mechanically stressed tooth flanks. In addition, oil vapors, humidity, and other degradative agents could also have contributed to the observed failure. No recommendations were made.

You do not currently have access to this chapter.
Don't already have an account? Register

Wear: Plastic Wear Failure, ASM Failure Analysis Case Histories: Failure Modes and Mechanisms, ASM International, 2019

Download citation file:


Close
Close Modal

or Create an Account

Close Modal
Close Modal