Abstract

Several glass wool insulation sections from a heat-treat furnace showed visible, but only cosmetic discoloration. EDS showed the presence of silicon, aluminum, and oxygen in the nondiscolored region, and these elements are consistent with glass wool. Relatively high levels of chromium and nickel were detected in the discolored area, along with lower amounts of iron, manganese, sodium, calcium, cobalt, and sulfur, in addition to the surrounding glass wool elements. Results of this limited evaluation showed the discoloration was caused by the presence of elevated levels of chromium, nickel, and aluminum. The visual appearance, along with the EDS findings, suggested these elements were present in the form of oxides. These oxides were likely deposited from adjacent structural components of the furnace, which had oxidized during operation.

You do not currently have access to this chapter.
Don't already have an account? Register

S.J. Suess, 2019. "Discoloration of Furnace Insulation", ASM Failure Analysis Case Histories: Steelmaking and Thermal Processing Equipment

Download citation file:


Close
Close Modal
This Feature Is Available To Subscribers Only

Sign In or Create an Account

Close Modal
Close Modal