Abstract

A brittle-like crack propagation caused failure in a rubber office-chair roller. A crack initiated from the inside of the roller and propagated in a discontinuous brittle-like fashion, as indicated from the evolution of concentric fracture striations. Compressive fatigue was a dominant mode of loading. Nevertheless, the fracture surface of the failure-causing crack suggested a tensile-stress component was involved in driving failure.

You do not currently have access to this chapter.
Don't already have an account? Register

2019. "Failure of a Rubber Office-Chair Roller", ASM Failure Analysis Case Histories: Household Products and Consumer Goods