Three ASME SA106 grade B carbon steel feed water piping reducers from a pressurized water reactor showed indications of flaws near welds during ultrasonic testing. Further examination and testing indicated that the cracks resulted from a low-cycle corrosion fatigue phenomenon.

You do not currently have access to this chapter.
Don't already have an account? Register

Carl J. Czajkowski, 1993. "Cracking in a Reducing Pipe From a Pressurized Water Reactor", Handbook of Case Histories in Failure Analysis, Khlefa A. Esaklul