Abstract

Two 20 MW turbines suffered damage to second-stage blades prematurely. The alloy was determined to be a precipitation-hardening nickel-base superalloy comparable to Udimet 500, Udimet 710, or Rene 77. Typical protective coatings were not found. Test results further showed that the fuel used was not adequate to guarantee the operating life of the blades due to excess sulfur trioxide, carbon, and sodium in the combustion gases, which caused pitting. A molten salt environmental cracking mechanism was also a factor and was enhanced by the working stresses and by the presence of silicon, vanadium, lead, and zinc. A change of fuel was recommended.

You do not currently have access to this chapter.
Don't already have an account? Register

Antonio F. Iorio, Juan C. Crespi, 1993. "Failure Analysis of Turbine Blades", Handbook of Case Histories in Failure Analysis, Khlefa A. Esaklul

Download citation file:


Close
Close Modal
This Feature Is Available To Subscribers Only

Sign In or Create an Account

Close Modal
Close Modal