In this article, we report the outcome of an investigation made to uncover the premature fracture of crusher jaws produced in a local foundry. A crusher jaw that had failed while in service was studied through metallographic techniques to determine the cause of the failure. Our investigation revealed that the reason for the fracture was the presence of large carbides at the grain boundaries and in the grain matrix. This led to the formation of microcracks that propagated along the grain boundaries under in-service working forces. It is also believed that the precipitation of carbides at the grain boundaries may have occurred because of improper heat treatment, but not because of a deficiency in composition.

You do not currently have access to this chapter.
Don't already have an account? Register

J.O. Olawale, S.A. Ibitoye, M.D. Shittu, A.P.I. Popoola, A Study of Premature Failure of Crusher Jaws, Handbook of Case Histories in Failure Analysis, Vol 3, Edited By Larry Berardinis, ASM International, 2019, p 172–176, https://doi.org/10.31399/asm.fach.v03.c9001776

Download citation file:


Close
Close Modal

or Create an Account

Close Modal
Close Modal