Nickel-based Alloy 617B (DIN 2.4673) and Alloy C-263 (DIN 2.4650) with high creep strength and good fabricability are promising material candidates for the design of next generation coal-fired “Advanced Ultra-Super-Critical A-USC” power plants with advanced steam properties and thus higher requirements on the material properties. Microstructural studies of the precipitation hardened alloy C-263 were performed with Electron Microscopy (TEM) with respect to their strengthening precipitates like carbides and intermetallic gamma prime. Specimens were subjected to different ageing treatments at elevated temperatures for different times. The microstructural results of the investigated nickel alloy C-263 are presented and discussed with respect to their correlation with required properties for A-USC, e.g. the mechanical properties, the creep resistance and the high temperature stability and compared to Alloy 617B. The manufacturing procedure for the prematernal and forgings as well as for thin walled tube components for A-USC power plants is presented.

Austenitic and super-austenitic stainless steels are a critical component of the spectrum of high temperature materials. With respect to power generation, alloys such as Super 304H and NF709 span a gap of capability between ferritic and martensitic high chromium steels and nickel-based alloys in boiler tube applications for both conventionally fired boilers and heat-recovery steam generators (HRSG). This research explores a wrought version of a cast austenitic stainless steel, CF8C-Plus or HG10MNN, which offers promise in creep strength at relatively low cost. Various manufacturing techniques have been employed to explore the impact of wrought processing on nano-scale microstructure and ultimately performance, especially in high temperature creep. Transmission electron microscopy has been used to quantify and characterize the creep-strengthening particles examining the relationship between traditional melting and extrusion as compared to powder metallurgy.

The paper deals with microstructural evolution in the AISI 316LN + 0.1 wt.% Nb steel during long-term creep exposure at 600 and 625°C. The following minor phases formed: Z-phase (NbCrN), M 23 C 6 , M6X (Cr3Ni2SiX type), η-Laves (Fe2Mo type) and σ-phase. M6X gradually replaced M 23 C 6 carbides. Primary Z-phase particles were present in the matrix after solution annealing, while secondary Z-phase particles formed during creep. Precipitation of Z-phase was more intensive at 625°C. The dimensional stability of Z-phase particles was excellent and these particles had a positive effect on the minimum creep rate. However, niobium also accelerated the formation and coarsening of σ-phase, η-Laves and M6X. Coarse particles, especially of σ-phase, facilitated the development of creep damage, which resulted in poor long-term creep ductility.

ASME Grade 91 steel seam-welded elbow pipe, which has been used in a USC plant (A-Plant) for about 6 × 10 4 h, was investigated to clarify the microstructure and remaining creep life of the material at long-term region. SEM and TEM observations were conducted on specimens cut from the welded portions of the intrados and extrados of the elbow, and the number density of creep voids in fine-grained HAZ was measured in the wall-thickness direction. Then, creep rupture tests were performed to examine the remaining life of each portion of the base metal and welded joint. On the basis of the results, it was suggested that the microstructural changes were small and that the cumulative creep damage was also small for the elbow pipe during its use at the USC plant for about 6 × 10 4 h. The present result was compared with the result of an investigation on Grade 91 steel elbow used in another USC plant (B-Plant) for about 5 × 10 4 h. The A-Plant material had a creep life about ten times longer than that of the B-Plant material for not only the base metals but also the welded joint. Through the comparison of the investigation results, it was suggested that the difference in the creep deformation property between the base metals of the elbows was the main reason for the difference in their creep lives.

In the present study a creep resistant, ferritic steel, based on the chemical composition of Crofer 22 H, was analysed regarding microstructure and particle evolution. Because of the preceding hot-rolling process formation of sub-grain structures was observed, which disappears over time. Additionally formation of particle-free zones close to high angle grain boundaries was observed. These zones are considered to be responsible for long-term material failure by lacking particle hardening and thus a concentration of deformation. Therefore in-depth analyses by transmission and scanning electron microscopy were performed to investigate dislocation behaviour in these areas

Inconel alloy 740H is designated for boiler sueprheater/reheater tubes and main steam/header pipes application of advanced ultra-supercritical (A-USC) power plant at operating temperatures above 750°C. Microstructure evolution and precipitates stability in the samples of alloy 740H after creep-rupture test at 750°C, 800°C and 850°C were characterized in this paper by scanning electron microscopy, transmission electron microscopy and chemical phase analysis in details. The phase compositions of alloy 740H were also calculated by thermodynamic calculation. The research results indicate that the microstructure of this alloy keeps good thermal stability during creep-rupture test at 750°C, 800°C and 850°C. The precipitates are MC, M 23 C 6 and γ′ during creep-rupture test. The temperature of creep test has an important effect on the growth rate of γ′ phase. No harmful and brittle σ phase was found and also no γ′ to η transformation happened during creep. Thermodynamic calculations reveal almost all the major phases and their stable temperatures, fractions and compositions in the alloy. The calculated results of phase compositions are consistent with the results of chemical phase analysis. In brief, except of coarsening of γ′, Inconel alloy 740H maintains the very good structure stability at temperatures between 750°C and 850°C.

The objective of this study was to determine the typical range of weld metal cooling rates and phase transformations during multipass gas-tungsten arc (GTA) welding of Grade 23 (SA-213 T23) tubing, and to correlate these to the microstructure and hardness in the weld metal and heat affected zone (HAZ). The effect of microstructure and hardness on the potential susceptibility to cracking was evaluated. Multipass GTA girth welds in Grade 23 tubes with outside diameter of 2 in. and wall thicknesses of 0.185 in. and 0.331 in. were produced using Grade 23 filler wire and welding heat input between 18.5 and 38 kJ/in. The weld metal cooling histories were acquired by plunging type C thermocouples in the weld pool. The weld metal phase transformations were determined with the technique for single sensor differential thermal analysis (SS DTA). The microstructure in the as-welded and re-heated weld passes was characterized using light optical microscopy and hardness mapping. Microstructures with hardness between 416 and 350 HV 0.1 were found in the thick wall welds, which indicated potential susceptibility to hydrogen induced cracking (HIC) caused by hydrogen absorption during welding and to stress corrosion cracking (SSC) during acid cleaning and service.

Recovery of microstructure and void formation were investigated in creep-ruptured specimens of ASME Gr. T91 steels to understand the cause of loss of creep rupture ductility in the long-term creep condition and its heat-to-heat variation. The specimens studied were two heats (MGA, MGC) of Gr. T91 steels creep-ruptured at 600 °C under the stress conditions of 160-80 MPa. The reduction of area at rupture (RA) was 55% for MGA, but 83% for MGC in the long-term condition (under the creep stress of 80 MPa), while RA was higher than 80 % for the two heats in the short-term conditions (under the creep stresses above 100 MPa). In both heats, equiaxed grains were observed in the vicinity of ruptured surface in the long-term condition, indicating that recovery and recrystallization occurred extensively in the creep condition, while grains were elongated in the short-term conditions. In the uniformly deformed regions with a small area reduction in the long-term crept specimens, recovered and recrystallized grains were observed in the limited region close to high angle grain boundaries in MGA, while they were extended into grain interiors in MGC. In the long-term creep conditions two types of voids were observed: fine ones with a diameter below 1 μm and coarse ones with a diameter from 2 μm up to 50 μm. Fine creep voids were found to grow with necking in MGA while they neither nucleated nor grew with necking in MGC. Coarse creep voids increased in size and in number with necking in both heats and were larger and denser in MGA than in MGC.

The recently developed 12%Cr steel VM12-SHC is characterized by very good creep properties at temperatures up to 620°C. This new material development exhibits an excellent oxidation resistance in steam atmospheres at the typical application temperature but also at temperatures up to 650°C. In comparison to the existing 9% Cr grades T/P91 and T/P92, VM12-SHC steel opens due to its excellent oxidation behavior, new possibilities for its application as a heat exchanger boiler component. It was found that outside its application temperature range VM12-SHC also shows, as all 9-12%Cr steels, the appearance of the so called Z-phase. This effect was investigated to understand its influence on creep properties of this class of ferritic/martensitic steels aiming at controlling the microstructure stabilities for future grade developments. Creep testing has been carried out in the temperature range between 525°C and 700°C. Selected crept specimens have been investigated using light optical microscopy, SEM with EDX and TEM. In this study, the oxidation behavior of a number of typical martensitic 9-12%Cr steels was compared with the newly developed 12% Cr steel VM12-SHC. The compositions and morphologies of oxide scales formed after 5000 h exposure steels in simulated steam environments as function of temperature were characterized by light optical metallography and scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDX).

Research on low-alloyed, heat-resistant 12Cr2MoWVTiB steel, implemented in China to power plants in 50’s last century, was performed to investigate a possibility of its application for pressure elements of boilers, in particular for membrane walls. The microstructure of the as-received 12Cr2MoWVTiB tube, investigated by light microscopy, scanning- and transmission electron microscopy, consists of ferritic grains with some bainite areas between them as well as primary carbides (MC) and secondary carbides (VC, M 23 C 6 , M 6 C) formed during tempering of the steel. Results of mechanical tests of 12Cr2MoWVTiB welded joints (butt- and fillet welded joints) as well as microstructure analyses of are satisfactory.

The goal of improving the efficiency of pulverized coal power plants has been pursued for decades. The need for greater efficiency and reduced environmental impact is pushing utilities to ultra supercritical conditions (USC), i.e. steam conditions of 760°C and 35 MPa. The long-term creep strength and environmental resistance requirements imposed by these conditions are clearly beyond the capacity of the currently used ferritic steels and other related alloys. Consequently, new materials based on austenitic stainless steels and nickel-base superalloys are being evaluated as candidate materials for these applications. In the present work, the nickel-base superalloys CCA617, Haynes 230 and Inconel 740, and an austenitic stainless steel Super З04H, were evaluated. The materials were aged for different lengths of time at temperatures relevant to USC applications and the corresponding microstructural changes were characterized by x-ray diffraction, optical, scanning and transmission electron microscopy, with particular attention being given to the structure, morphology and compositions of phases (including γ, γ’, carbides, ordered phases, etc.) and the nature, density and distribution of dislocations and other defects. The results are presented and discussed in light of accompanying changes in microhardness.

Tempered martensitic 9-12%Cr steels bearing tungsten, such as P92 and P122 showing higher creep rupture strength than the conventional steel P91, have been developed for thick section components in ultra-supercritical (USC) boilers. However, their creep strength is not sufficient for applying at the steam condition of 650°C/35MPa or above, which is a recent target condition in order to increase plant efficiency. The research and development project in NIMS on advanced high-Cr steels which can be applied at the steam condition of 650°C/35MPa as boiler components with large diameter and thick section has been carried out since 1997. In this project, it has been revealed that the addition of boron more than 0.01 mass% to the 0.08C-9Cr- 3W-3Co-V,Nb-<0.00ЗN steel remarkably improves creep strength. The boron enriched in M 23 C 6 carbides near prior-austenite grain boundaries suppresses coarsening of these carbides during creep deformation, leading to excellent microstructural stability and creep strength. Further improvement of creep strength is achieved by the addition of appropriate amount of nitrogen which enhances precipitation of fine MX. Excess addition of nitrogen to the high-B containing steel reduces creep rupture lives and ductility. The highest creep strength is obtained in the 0.08C-9Cr-3W-3Co-0.2V-0.05Nb-0.0139B-0.0079N (mass%) steel, resulting in excellent creep strength in comparison with that of P92 and P122. This steel shows good creep ductility even in the long term. It is, therefore, concluded that this high-B bearing 9Cr-3W-3Co-V,Nb steel with the addition of nitrogen in the order of 0.008 mass% is the promising candidate which shows superior creep strength without impairing creep ductility for thick section components in the 650°C-USC plant.

Critical sections of steam plants and heat-recovery steam generators require materials with enhanced properties such as 9Cr-1Mo steel. Ensuring compliance with specifications for heat treatment, chemical composition, contamination limits, and joint design is crucial to prevent premature failures. This study describes the development of a user-friendly, multi-property nondestructive sensor arrangement to qualify heat-treated 9Cr-1Mo steel. Experimental results demonstrate that correlations between thermal heat treatment and electronic, magnetic, and elastic measurements can determine if T91 steel achieves the necessary microstructure and properties for service. Additionally, rejected parts can be assessed for microstructural issues causing unacceptable properties. The techniques utilize a common electronic setup with different sensors, requiring calibration for specific NDE systems and sensor setups, high-speed data acquisition, and frequency analysis (FFT). Further development on crept and welded samples is recommended to enhance NDE practices for in-service T91 steel conditions.

Advanced UltraSupercritical (A-USC) Steam fossil power plants will operate at steam temperatures up to 760°C, which will require the use of Ni-based superalloys for steam boiler/superheater and turbine systems. In 2008, the Oak Ridge National Laboratory (ORNL) and the National Engineering Technology Laboratory/Albany (NETL/Albany) collaborated to make and test castings of Ni-based superalloys, which were previously only commercially available in wrought form. These cast Ni-based based alloys are envisioned for the steam turbine casing, but they may also be applicable to other large components that connect the steam supply to the steam turbine. ORNL and NETL/Albany have produced small vacuum castings of HR 282, Nimonic 105, Inconel 740, and alloy 263, which are precipitation-hardened Ni-based superalloys, as well as solid-solution superalloys such as alloys 625, 617 and 230. The initial alloy screening included tensile and creep-testing at 800°C to determine which alloys are best suited for the steam turbine casing application at 760°C. HR 282 has the best combination of high-temperature strength and ductility, making it a good candidate for the cast-casing application. Cast and wrought versions of HR 282 have similar creep-rupture strength, based on the limited data available to-date. Detailed comparisons to the other alloys and microstructures are included in this paper.

Advanced Ultra-supercritical (A-USC) steam power-plant technology is being developed for better efficiency and lower emissions at 700°C and above, but is based mainly on Ni-based alloys. The ability to include lower-cost alloys with appropriate high-temperature performance should have substantial technological and economic benefits. CF8C-Plus is a cast austenitic stainless steel recently developed for other applications at 600-900°C, which has creep-strength comparable to many solid-solution Ni-based alloys. EPRI and Carpenter Technology produced a 400 lb heat of CF8C-Plus steel and hot-forged it at 5:1 and 12:1 reductions, to assess feasibility of the alloy as a wrought advanced stainless steel for potential use as steam headers and piping for A-USC power plant applications. The hot-forged alloy has a recrystallized grain structure 6-9 times finer than the as-cast dendritic structure, resulting in better strength and impact resistance at room-temperature, and about 20% higher yield-strength (YS) at 760°C, and similar or better ductility compared to the as-cast material. The initial creep-rupture testing at 700-800°C for up to 2000h also indicates similar or better rupture resistance and better creep-ductility for wrought compared to cast material. The next steps needed to test performance of the wrought austenitic stainless steel for extruded headers and piping are discussed.

SUPER304H (18Cr-9Ni-3Cu-Nb-N, ASME CC2328) and TP347HFG (18Cr-12Ni-Nb, ASME SA213) are advanced fine-grained microstructure steel tubes developed for high strength and superior steam oxidation resistance. Their exceptional performance is demonstrated by the longest creep rupture tests, with SUPER304H tested at 600°C for 85,426 hours and TP347HFG at 700°C for 55,858 hours, both maintaining stable strength and microstructure with minimal σ phase formation and absence of other brittle phases compared to conventional austenitic stainless steels. HR3C (25Cr-20Ni-Nb-N, ASME CC2115) was specifically developed for high-strength, high-corrosion-resistant steel tubes used in severe corrosion environments of ultra-supercritical (USC) boilers operating at steam temperatures around 600°C. The longest creep test for HR3C, conducted at 700°C and 69 MPa for 88,362 hours, confirmed its high and stable creep strengths and microstructural integrity across the 600-800°C temperature range. These innovative steel tubes have been successfully installed in the Eddystone No. 3 USC power plant as superheater and reheater tubes since 1991, with subsequent microstructural investigations after long-term service exposure revealing their remarkable performance. The paper provides an up-to-date analysis of the long-term creep rupture properties and microstructural changes of these steels following extended creep rupture and aging processes, highlighting their successful application as standard materials for superheater and reheater tubes in newly constructed ultra-supercritical boilers worldwide.

This paper presents comprehensive test results of thick-walled VM12 steel pipes containing 12% chromium, vanadium, and tungsten, with cobalt addition. The primary objective was to verify welding technologies for boiler superheater thick-walled components and characterize the strength, technological properties, and microstructure of welded joints produced at RAFAKO S.A. The extensive research program encompassed a broad range of tests on both parent material and welded joints, including mechanical property assessments at room temperature, creep resistance evaluations, low-cycle fatigue testing at room temperature and 600°C (1120°F), and detailed macro- and microstructural examinations. Furthermore, the investigation included a comprehensive microstructural stability assessment using light microscopy (LM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM), conducted after fatigue resistance testing at room and elevated temperatures, following additional annealing at 700°C (1,920°F), and after 1,000 hours of exposure for both parent material and welded joints. These investigations were conducted as part of the COST 536 Action, representing a collaborative effort to understand and characterize high-temperature creep-resistant steels like VM12 for advanced power generation applications.

Ni-based superalloy Haynes 282 is a prime candidate for advanced power generation systems due to its superior fabricability, weldability, and high-temperature performance. Additive manufacturing offers potential cost and time savings for gas turbine components. Wire-arc direct energy deposition can create large components but often requires post-processing treatments, such as hot isostatic pressing (HIP), to address porosity. This study explores a low heat-input, high deposition rate GMAW process to achieve fully dense Haynes 282 without HIP. Twenty-one blocks were deposited, varying travel and wire feed speeds. Initial analysis (visual inspection, microstructural examination, and CT) revealed the impact of build parameters on internal porosity and defects. Scanning electron microscopy provided insights into structural heterogeneity and microstructural properties.

The Advanced Materials and Manufacturing Technologies (AMMT) program is aiming at the accelerated incorporation of new materials and manufacturing technologies into nuclear-related systems. Complex Ni-based components fabricated by laser powder bed fusion (LPBF) could enable operating temperatures at T > 700°C in aggressive environments such as molten salts or liquid metals. However, available mechanical properties data relevant to material qualification remains limited, in particular for Ni-based alloys routinely fabricated by LPBF such as IN718 (Ni- 19Cr-18Fe-5Nb-3Mo) and Haynes 282 (Ni-20Cr-10Co-8.5Mo-2.1Ti-1.5Al). Creep testing was conducted on LPBF 718 at 600°C and 650°C and on LPBF 282 at 750°C. finding that the creep strength of the two alloys was close to that of wrought counterparts. with lower ductility at rupture. Heat treatments were tailored to the LPBF-specific microstructure to achieve grain recrystallization and form strengthening γ' precipitates for LPBF 282 and γ' and γ" precipitates for LPBF 718. In-situ data generated during printing and ex-situ X-ray computed tomography (XCT) scans were used to correlate the creep properties of LPBF 282 to the material flaw distribution. In- situ data revealed that spatter particles are the potential causes for flaws formation in LPBF 282. with significant variation between rods based on their location on the build plate. XCT scans revealed the formation of a larger number of creep flaws after testing in the specimens with a higher initial flaw density. which led to a lower ductility for the specimen.

Inconel 718 is a nickel-based superalloy known for its excellent combination of high-temperature strength, corrosion resistance, and weldability. Additive Manufacturing (AM) has revolutionized traditional manufacturing processes by enabling the creation of complex and customized components. In this work, three prominent AM techniques: Laser-Based Powder Bed Fusion (PBF), Wire Direct Energy Deposition (DED), and Binder Jet (BJ) processes were explored. A thorough metallographic analysis and comparison of samples was conducted after short-term creep testing originating from each of the three aforementioned techniques in addition to wrought material. Detailed electron microscopy unveiled equiaxed grains in both BJ and wrought samples while PBF samples displayed elongated finer grain structures in the build direction, characteristic of PBF. The DED samples revealed a more bimodal grain distribution with a combination of smaller equiaxed grains accompanied by larger more elongated grains. When assessing the three processes, the average grain size was found to be larger in the BJ samples, while the PBF samples exhibited the most significant variation in grain and sub-grain size. Number density, size, and shape of porosity varied between all three techniques. Post-creep test observations in PBF samples revealed the occurrence of wedge cracking at the failure point, accompanied by a preference for grain boundary creep void formation while BJ samples exhibited grain boundary creep void coalescence and cracking at the failure location. In the DED samples, void formation was minimal however, it seemed to be more prevalent in areas with precipitates. In contrast, the wrought sample showed void formation at the failure site with a preference for areas with primary carbide formation. Despite BJ samples demonstrating similar or even superior rupture life compared to other AM techniques, a noteworthy reduction in rupture ductility was observed. While a coarse, uniform grain size is generally linked to enhanced creep resistance and rupture life, the combination of pre-existing voids along grain boundaries and the formation of new voids is hypothesized to accelerate rapid fracture, resulting in diminished ductility. This research shows careful consideration is needed when selecting an AM technology for high- temperature applications as creep behavior is sensitive to the large microstructural variations AM can introduce.