Japanese USC-PC units successfully operate with steam temperatures of 610°C (1130°F). IHI is developing the next generation of USC-PC boilers, targeting 620°C (1150°F) for improved efficiency. Investigations are underway for even higher 700°C (1290°F) steam temperatures. IHI collaborates with turbine manufacturers to create reliable and efficient boiler-turbine packages for both new and existing power plants.

For VM12-SHC 11-12 wt. % Cr steel, there have been no systematic investigations to define the regions or characterise the microstructures within the heat-affected zone (HAZ) of weldments. In similar steels, these regions relate to the Ac 1 and Ac 3 transformation temperatures and can affect weldment performance. In this study, controlled thermal cycles were applied to VM12-SHC parent metal using a dilatometer and the Ac 1 and Ac 3 temperatures were measured for various heating rates. The Ae 1 and Ae 3 temperatures were also calculated by thermodynamic equilibrium modeling. Through dilatometry, thermal cycles were then applied to simulate the microstructures of the classically defined HAZ regions. The microstructural properties of each simulated material were investigated using advanced electron microscopy techniques and micro-hardness testing. It was found that the simulated HAZ regions could be classified as; (1) the completely transformed (CT) region, with complete dissolution of pre-existing precipitates and complete reaustenitisation; (2) the partially transformed (PT) region, exhibiting co-existing original martensite with nucleating austenite microstructures with partial dissolution of precipitates; and (3) the over tempered (OT) region, with no phase transformation but precipitate coarsening and decreased hardness.

The present study presents a detailed investigation on the evolution of the microstructure during welding on virgin and long-term service exposed (creep aged 1 = 535°C; 16.1 MPa; 156 kh and creep aged 2 = 555°C; 17.0 MPa; 130 kh) 12% Cr (X20CrMoV11-1) martensitic steel. This study was carried out in order to understand the impact of welding on prior creep exposed Tempered martensite ferritic (TMF) steel and to explain the preferential failure of weldments in the fine grained heat affected zone (FGHAZ) of the creep aged material side instead of the new material side. Gleeble simulation (Tp = 980°C; heating rate = 200 °C/s; holding time = 4 seconds) of the FGHAZ was performed on the materials to create homogeneous microstructures for the investigation. Quantitative microstructural investigations were conducted on the parent plate and simulated FGHAZ materials using advanced electron microscopy to quantify: a) voids, b) dislocation density, c) sub-grains, and d) precipitates (M 23 C 6 , MX, Laves, Z-phase) in the materials. Semi-automated image analysis was performed using the image analysis software MIPARTM. The pre-existing creep voids in the creep aged parent material and the large M 23 C 6 carbides (Ø > 300 nm) in the FGHAZ after welding are proposed as the main microstructural contributions that could accelerate Type IV failure on the creep aged side of TMF steel weldments.

This study demonstrates the Electro-Thermal Mechanical Testing (ETMT) system's capability to analyze the thermo-mechanical behavior of Inconel 718 (IN718) at a heating rate of 5 °C/s, achieving temperatures up to 950 °C. The temperature profile peaks at the sample's center and is approximately 25 °C at the extremes. Upon reaching 950 °C, the sample was aged for 30 hours before being rapidly quenched. This process froze the microstructure, preserving the phase transformations that occurred at various temperatures across the temperature parabolic gradient, which resulted in a complex gradient microstructure, providing a comprehensive map of phase transformations in IN718. The integration of thermal measurement, COMSOL modeling, scanning electron microscopy enabled a thorough characterization of the microstructural evolution in IN718, linking observed phases to the specific temperatures which provided a rapid screening of the effect of using different heating treatment routes.

Main steam control valves are crucial components in power plants, as they are the final elements in the steam piping system before the steam enters the turbine. If any parts of these valves become damaged, they can severely harm the steam turbines. Recently, power plants have been required to operate under cyclical loading, which increases the risk of cracks in the control valve seats. This is due to the different rates of expansion between the Stellite surface and the underlying Grade 91 steel surface when exposed to high temperatures. To ensure a reliable power supply, power plants cannot afford long downtimes, making on-site service essential. This paper presents an on-site technique for post-weld heat treatment (PWHT) of Stellite seats. By using a heating pad arrangement and an induction heater, the required PWHT temperature of 740°C, as specified in the welding specification procedure (WPS), can be achieved. This method allows for on-site valve seat repair and can be applied to other power plants as well.

Creep strength enhanced ferritic steels like T/P 91 and T/P 92 are widely used for the fabrication of pressure vessel components in the petro-chemical and thermal power industry. Today, a new generation of 9-12% Cr CSEF steels like MARBN, Save12AD, G115 and Super VM12 are entering into the market. All CSEF steels require an accurate post-weld heat treatment after welding. This paper discusses the impact of chemical composition on Ac1 as well as the transformation behavior during post-weld heat treatment in a temperature range below and above Ac1. The Ac1 temperature of weld metals with variations in chemical composition has been determined and thermodynamic calculations has been carried out. Simulations of heat treatment cycles with variations in temperature have been carried out in a quenching dilatometer. The dilatation curves have been analyzed in order to detect any phase transformation during heating or holding at post weld heat treatment. Creep rupture tests have been carried out on P91 and Super VM12 type weld metals in order to investigate the effect of sub- and intercritical post weld heat treatment on creep rupture strength.

Since the 1990s, the power plant market has shifted towards more flexible and efficient Steam Power Plants (SPPs) with fewer service inspections and lifetimes of ≥200,000 hours, including combined-cycle applications. This shift has driven efforts to enhance both design and materials. One approach is the installation of super-critical SPPs with live steam temperatures of T ≥580°C and optimized steam cycles. Siemens Power Generation is leveraging its experience with Ultra Super Critical SPPs from the 1950s, which operated at up to 650°C/320bar, to develop modern turbo-set solutions using new technology from the past decade. Proven design features, such as material combinations (welded or bolted rotors and casings) and advanced cooling techniques, are being adapted for current use. Past limitations with austenitic materials have been reassessed, leading to the conclusion that improved materials are necessary for today's USC SPPs. Global material development programs, such as COST in Europe, are focusing on new 10%Cr martensitic steels, which offer cost-effectiveness and operational flexibility. Additionally, joint R&D projects are underway to evaluate the long-term creep properties and service behavior of new 10%CrMoV steels for 600/620°C applications. These projects aim to ensure the materials can withstand relevant loading conditions and multiaxial stresses.

In advanced ultra-supercritical (A-USC) power plants, which operate at steam temperatures of 700 °C or higher, there is a need to replace 9 to 12Cr martensitic steels with high-strength nickel-base superalloys or austenitic steels for components exposed to the highest temperatures. However, due to the high cost of nickel-base superalloys, it is desirable to use 9 to 12% Cr martensitic steels for components exposed to slightly lower temperatures, ideally expanding their use up to 650 °C. Key challenges in developing ferritic steels for 650 °C USC boilers include enhancing oxidation resistance and long-term creep rupture strength, particularly in welded joints where resistance to Type IV cracking is critical for constructing thick-section boiler components. The current research aims to investigate the creep deformation behavior and microstructure evolution during creep for base metals and heat-affected-zone (HAZ) simulated specimens of tempered martensitic 9Cr steels, including 9Cr-boron steel and conventional steels like grade 91 and 92. The study discusses the creep strengthening mechanisms and factors influencing creep life. It proposes an alloy design strategy that combines boron strengthening and MX nitride strengthening, avoiding the formation of boron nitrides during normalizing heat treatment, to improve the creep strength of both base metal and welded joints.

Refractory metal, such as molybdenum and tungsten, are used in increasingly severe environments. Therefore, these materials are required to have superior mechanical properties, long life and excellent reliability. In this study, we developed newly Mo alloy dispersed Mo-base intermetallic compound for material forming such as hot extrusion die. This newly Mo alloy “MSB” exhibited superior mechanical properties compared with convention Mo alloy at temperatures below 1000℃. In addition, by adding a titanium alloy to the MSB, we have developed another alloy “T-MSB” that has high mechanical properties at higher temperatures. In the hot extrusion of brass, die made of these Mo alloys had 2.5 times longer tool life than the conventional Mo alloy die.

For the safe operation of high temperature equipment, it is necessary to ensure creep rupture ductility of the components from the viewpoint of notch weakening. In this study, the effect of heat treatment conditions on creep rupture ductility was evaluated and its underlying metallurgical mechanism was investigated with using a forged Ni-based superalloy Udimet520. In order to improve the creep rupture ductility without lowering the creep rupture strength, it is important to increase both intragranular strength and intergranular strength in a balanced manner. For this purpose, it was clarified that 1) secondary γ' phase within grains should be kept fine and dense, 2) grain boundaries should be sufficiently covered by M 23 C 6 carbide by increasing its phase fraction, and 3) tertiary γ' phase within grains should be redissolved before the start of creep. To obtain such a precipitate state, it is essential to appropriately select the cooling rate after solution treatment, stabilizing treatment and aging treatment conditions.

This research compares creep crack growth behavior of two heats of creep strength enhanced ferritic (CSEF) steel, grade 91. These heats represent extremes of creep damage susceptibility, one heat exhibiting low creep ductility and the other high creep ductility. Creep crack growth tests were performed with compact tension specimens and were monitored with direct current potential drop and optical surface measurements. Load line displacement was measured throughout the duration of the tests. Specimens were sectioned, mounted, and analyzed using optical and scanning electron microscopy to assess the presence of oxidation, micro-cracking, creep damage, and void density. Tests were performed over a range of initial stress intensities on the low ductility material to investigate the impact of creep ductility. Metallurgical evidence and test data for each crack growth test was assessed to evaluate crack growth behavior linked to creep crack growth parameter (C*) and stress/creep damage distribution in the vicinity of the crack.

As the demand for worldwide electricity generation grows, pulverized coal steam generator technology is expected to be a key element in meeting the needs of the utility power generation market. The reduction of greenhouse gas emissions, especially CO 2 emissions, is vital to the continued success of coal-fired power generation in a marketplace that is expected to demand near-zero emissions in the near future. Oxycombustion is a technology option that uses pure oxygen, and recycled flue gas, to fire the coal. As a result, this system eliminates the introduction of nitrogen, which enters the combustion process in the air, and produces a highly-concentrated stream of CO 2 that can readily be captured and sequestered at a lower cost than competing post-combustion capture technologies. Oxycombustion can be applied to a variety of coal-fired technologies, including supercritical and ultra-supercritical pulverized coal boilers. The incorporation of oxycombustion technology in these systems raises some new technical challenges, especially in the area of advanced boiler materials. Local microclimates generated near and at the metal interface will influence and ultimately govern corrosion. In addition, the fireside corrosion rates of the boiler tube materials may be increased under high concentration oxygen firing, due to hotter burning coal particles and higher concentrations of SO 2 , H 2 S, HCl and ash alkali, etc. There is also potential to experience new fouling characteristics in the superheater and heat recovery sections of the steam generator. The continuous recirculation of the flue gases in the boiler, may lead to increasing concentrations of deleterious elements such as sulfur, chlorine, and moisture. This paper identifies the materials considerations of oxycombustion supercritical and ultrasupercritical pulverized coal plants that must be addressed for an oxycombustion power plant design.

A methodology is developed for evaluating its creep rupture life from analysis of an on-going creep curve with the aid of an Ω creep curve equation. The method is applied to on-going creep curves of grade 91 steel for evaluating their rupture lives. Quick decrease in creep rupture strength has been reported recently in long-term creep of grade 91 steel. The quick decrease of the steel is discussed by using the rupture lives evaluated. The quick decrease is confirmed in the present study in the time range longer than 3 x 10 4 h at 600°C.

The effect of grain size after solution treatment on the mechanical properties of FENIX-700, including its cooling rate, was investigated. In addition, the dependance of precipitation observed at grain boundaries on the heat treatment conditions was also discussed on the basis of the results of microstructure observations. It was confirmed that the tensile ductility, the creep rupture ductility, and the absorbed energy decreased as the grain size increased. The creep rupture strength, in contrast, increased remarkably as the grain size increased. The tensile strength increased as the cooling rate increased. Experimental results showed that satisfactory mechanical properties would be obtained for a grain size of ASTM G.S.No. 1.0-3.0.

Grade 91 steel has been found to be susceptible to Type IV cracking in the base metal heat affected zone (HAZ). In order to better understand this type of failure, a study on the metallurgical reactions occuring within the HAZ was conducted, particularly within the fine grained (FG) and intercritical (IC) regions where Type IV cracking is most commonly found to occur. The course grained (CG), FG and IC regions of the HAZ in Grade 91 steel were simulated using a Gleeble 3800 Thermo-Mechanical Simulator. A dilatometer was used to determine the phase transformations occuring during simulation of weld thermal histories. For the first time, it was shown that ferrite can form in the IC HAZ of Grade 91 steel welds. The magnitude of the ferrite transformation was observed to decrease with faster cooling rates. The presence of ferrite in the simulated IC HAZ microstructure was shown to decrease the high temperature tensile strength and increase the high temperature elongation compared to HAZ regions that did not undergo ferrite transformation. Welding parameters such as heat input, preheat and interpass temperature can be selected to ensure faster cooling rates and reduce or potentially avoid formation of ferrite in the IC HAZ.

In order to establish a induction bending technique for Ni-based alloy HR6W large pipe, induction bending test was conducted on HR6W, which is a piping candidate material of 700°C class Advanced Ultra-Super Critical. In this study, a tensile bending test in which tensile strain was applied and a compression bending test in which compression strain was applied to the extrados side of the pipe bending part. As the results of these two types of induction bending tests, it was confirmed that a predetermined design shape could be satisfied in both bending tests. In addition, the wall thickness of the pipe was equal to or greater than that of the straight pipe section in compression bending. Therefore, if compression bending is used, it is considered unnecessary to consider the thinning amount of the bent portion in the design. Next, penetrant test(PT) on the outer surface of the bending pipes were also confirmed to be acceptable. Subsequently, metallographic samples were taken from the outer surface of the extrados side, neutral side and intrados side of the pipe bending portion. Metallographic observation confirmed that the microstructures were normal at all the three selected positions. After induction bending, the pipe was subjected to solution treatment. Thereafter, tensile tests and creep rupture tests were carried out on samples that were cut from the extrados side, neutral side and intrados side of the pipe bending portion. Tensile strength satisfied the minimum tensile strength indicated in the regulatory study for advanced thermal power plants report of Japan. Each creep rupture strength was the almost same regardless of the solution treatment conditions. From the above, it was possible to establish a induction bending technique for HR 6W large piping.

Creep strength enhanced ferritic (CSEF) steels, particularly modified 9Cr steels Grade 91 and 92, are increasingly used in advanced coal-fired power plants for header and steam piping construction. While these materials typically enter service after receiving a standard high-temperature normalizing treatment followed by lower temperature tempering to achieve optimal microstructure, practical situations like welding operations may expose components to additional heat treatment exceeding the Ac 1 , and potentially the Ac 3 , temperature before returning to tempering temperature. This research examines the effects of simulated post weld heat treatments (PWHT) on Grade 91 and 92 materials using dilatometer-controlled heating and cooling rates, with peak temperatures below Ac 1 , between Ac 1 and Ac 3 , and above Ac 3 , followed by heat treatment at 750°C for 2 hours. Hardness measurements revealed significant reduction when exceeding the Ac 1 temperature, while advanced electron microscopy, including electron back scatter diffraction, was employed to analyze changes in martensite laths and grain structure, along with detailed carbide size distribution analysis using both scanning and transmission electron microscopy. The findings are discussed in terms of how such PWHT overshoots might affect mechanical properties during high-temperature service.

Type IV creep damage is a problem in high-temperature steam piping made of high chromium steel at thermal power plants, and a method for evaluating the remaining life is required. In this study, we considered that void’s initiation and growth can be expressed by initiation rate f, growth rate h, and initiation start time t 1 , and that stress and TF affect f, h and t 1 . We also proposed the method to estimate f, h and t 1 by measuring the change of the distribution of radius of voids during creep test. The creep test conditions are (1) test temperature of 650 C, maximum principal stress σ 1 of 79.5MPa, and TF of 2.5 ~ 3.0, and (2) test temperature of 650C, maximum principal stress of 71.5MPa, and TF of 2.5 ~ 3.0. The influence of σ 1 to f, h and t 1 was quantified by comparing the result of test (1) and that of test (2).

Delivered condition of Inconel740H specified in ASME Code Case 2702 is solution heat treated and aged condition, fabricating performances are also based on the condition, and a re-annealing and aging shall be performed if cold forming to strains is over 5%. These almost harsh requirements bring great inconvenience for its engineering practice and utilization. The comparative bending tests on 740H tubes in solution heat treated + aged condition and solution heat treated condition were performed, and the rules’ reasonability of the specification on delivered condition was discussed and analyzed from point view of deformability and weldability in the paper. The bending test results showed that tube bent was difficult because of its high strength and limited deforming capacity in solution heat treated + aged condition. Therefore, the material supplied in the solution condition may be better from fabricating points. Whether re-solution for the bent tube is performed after bending depends on its bending radius, followed by welding and post weld heat treatment of component (this treatment can also be the aging treatment for annealed sector at the same time), this treating manner can meet regulatory requirements. For solution tubes, however, there are some inconveniences to its engineering application because fewer research studies were carried out on its properties up to now, and no regulations on them were given for the material in the specification. Suggestions are: 1) deeply investigating the properties of tubes in solution condition, including mechanical and fabricating performances, 2) adding the mechanical properties, maximum allowable cold forming to stain without performing re-solution and weld strength reduction factor of solution material to the code case.

In 9~12% Cr containing martensitic stainless steels, Laves phase usually occurs after long term high temperature exposure, while in the present work, some sparse relatively large particles of (Fe,Cr)2Mo type Laves phase were observed in virgin FB2 steel. It is speculated that the large Laves phase particles formed in casting process due to dendritic segregation. Then the evolutionary behavior of Laves phase during welding thermal cycle was studied and constitutional liquation of Laves phase was found, suggesting a liquation crack tendency in FB2 steel. At last, the hot ductility tests showed that the area where constitutional liquation occurred would act as crack initiation site, and the tested specimen fractured without any obvious plastic deformation. This work provided some guidance for the practical production of welded turbine rotors made of FB2 steel.