Search Results for heat exchangers

This paper outlines a comprehensive UK-based research project (2007-2010) focused on developing fireside corrosion models for heat exchangers in ultra-supercritical plants. The study evaluates both conventional materials like T22 and advanced materials such as Super 304H, examining their behavior under various test environments with metal skin temperatures ranging from 425°C to 680°C. The research aims to generate high-quality data on corrosion behavior for materials used in both furnace and convection sections, ultimately producing reliable corrosion prediction models for boiler tube materials operating under demanding conditions. The project addresses some limitations of existing models for these new service conditions and provides a brief review of the fuels and test environments used in the program. Although modeling is still limited, preliminary results have been presented, focusing on predicting fireside corrosion rates for furnace walls, superheaters, and reheaters under various service environments. These environments include those created by oxyfuel operation, coal-biomass co-firing, and more traditional coal firing.

In fossil-fired boilers, combustion-generated thermal energy transfers to the working fluid via exchanger tubes, where an internal oxide layer forms over time, reducing thermal conductivity and raising metal temperatures. This self-activating process accelerates creep damage, significantly shortening component lifespan. Boiler design codes set Maximum Allowable Stresses based on mechanical properties, primarily creep resistance, but oxidation effects are only indirectly considered through “design temperature” selection—an approach inadequate for next-generation high-performance boilers with increasingly severe steam conditions. This paper highlights the need to integrate oxidation behavior into the design of advanced heat-exchanging components by examining the impact of steam oxidation on tube lifespan, including oxide layer growth, metal loss, temperature rise, and reduced creep rupture time, with thermal flux effects illustrated through examples. It also compares the behavior of two 9-12Cr% steels: Grade 92, known for strong creep resistance, and VM12, which offers superior oxidation resistance. Additionally, it proposes a revised “design temperature” expression incorporating oxidation resistance performance indices and exchanger thermal characteristics. The study concludes by emphasizing the need for further research into oxidation kinetics, thermal properties, and oxide layer exfoliation mechanisms.

Diffusion bonded compact heat exchangers have exceptionally high heat transfer efficiency and might significantly improve the performance and reduce the cost of supercritical carbon-dioxide Brayton cycle power plants using high temperature heat sources, like high temperature nuclear reactors and concentrating solar power plants. While these heat exchangers have an excellent service history for lower temperature applications, considerable uncertainty remains on the performance of diffusion bonded material operating in the creep regime. This paper describes a microstructural modeling framework to explore the plausible mechanisms that may explain the reduced creep ductility and strength of diffusion bonded material, compared to wrought material. The crystal plasticity finite element method (CPFEM) is used to study factors affecting bond strength in polycrystals mimicking diffusion bonded microstructures. Additionally, the phase field method is also employed to simulate the grain growth and recrystallization at the bond line to model the bonding process and CPFEM is used to predict the resulting material performance to connect processing parameters to the expected creep life and ductility of the material, and to study potential means to improve the structural reliability of the material and the resulting components by optimizing the material processing parameters.

To improve the economics of critical components, such as receivers and heat exchangers, for Generation 3 (Gen 3) concentrating solar power (CSP) plants, research was conducted to understand how manufacturing impacts the high-temperature performance of various tube production routes. Gen 3 CSP components are expected to require the use of heat-resistant nickel- based alloys due to the elevated operating temperatures in designs carrying molten salt or supercritical CO 2 . INCONEL alloy 740H (alloy 740H) was investigated as an alternative to UNS N06230 (alloy 230) as it possesses superior high-temperature creep strength which can lead to overall reductions in material cost. A key challenge is understanding how autogenous seam welding with and without re-drawing can be used to manufacture thin-wall tubing for CSP receivers and heat-exchangers to further reduce costs over traditional seamless production routes. Alloy 740H welded tube was successfully fabricated and re-drawn to several relevant tube sizes. Since traditional mechanical testing samples could not be removed from the thin-wall tubing, full-sized tubes were used for tensile, fatigue, and vessel testing (internally pressurized creep- rupture) which was critical to understanding the weld performance of the manufactured product forms. The generated vessel test data exhibited a creep strength reduction when compared to wrought product with no clear trend with temperature or test duration. It was found that redrawing the welded tubes improved the creep strength to approximately 82% of the wrought material performance and elevated temperature tensile and fatigue behavior exceeded 85% of the design minimums. Detailed, post-test characterization found that nano-sized carbides formed during the laser seam-welding process remained stable after multiple solution-annealing steps, which restricted grain growth, and impacted the time-dependent performance. This paper will focus on the time-dependent behavior of the examined welded and redrawn tubes, supporting metallographic evidence, and give perspective on future considerations for using alloy 740H in CSP components.

Diffusion bonding is a key manufacturing process for nucleation applications including compact heat exchangers. Accurately predicting the alloy's behavior during the diffusion bonding process presents challenges, primarily due to the intricate interplay of microstructural evolution and physical processes such as compressive loading, temperature history, and component migration. The current study develops a phase-field model designed to simulate the diffusion bonding in 316H stainless steel, a material with exceptional high-temperature strength, corrosion resistance and suitability to high-pressure conditions. Our model incorporates a multi-phase, multi-component framework that aligns the experimental observations with the grain growth and heterogeneous nucleation, where arbitrary external compressive load and temperature history are considered. The simulations focus on grain nucleation, growth, and microstructure evolutions across diffusion bonding line under a variety of temperature profiles, mechanical loads, and surface roughness conditions, mirroring experimental setups. Our model predicts consistent simulation results with experiments in terms of the grain size and distribution near the bonding area, offering a better understanding of the diffusion bonding mechanism and the manufacturing process for building reliable compact heat exchangers.

To stay competitive in today’s dynamic energy market, traditional thermal power plants must enhance efficiency, operate flexibly, and reduce greenhouse gas emissions. This creates challenges for material industries to provide solutions for harsh operating conditions and fluctuating loads. Higher efficiency demands steels with excellent steam oxidation resistance, favoring ferritic steels for cycling operation due to their limited thermal expansion. This paper presents a study modeling a combined cycle power plant using GE 9HA0.2 GT technology. The analysis compares different maximum live steam temperatures (585°C, 605°C, 620°C) and four alloys (grades 91 and 92, stainless S304H, and Thor 115) for heat exchangers exposed to steam oxidation. Results indicate that Thor 115, a creep strength enhanced ferritic (CSEF) steel, is a viable alternative to stainless steel for live steam temperatures above 600°C, offering improved oxidation resistance with minimal weight increase. Modern CSEF steels outperform stainless steel in power plants with lower capacity factors, reducing thermal fatigue during load changes. Increasing the live steam temperature boosts plant efficiency, leading to significant CO 2 savings for the same power output.

The steam generation systems (SGS) of concentrated solar power (CSP) plants employ multiple heat exchangers arranged in series to convert thermal energy collected from the sun via a heat transfer fluid (HTF) to produce superheated steam in the Rankine cycle. Common CSP plant designs are based either on parabolic trough or central tower technology. The major Rankine cycle components consist of preheaters, evaporators, steam drums, superheaters, steam turbines, and water/air-cooled condensers, all connected through steel piping. For CSP plants capable of reheating the steam for improved efficiency, reheaters are also included in the Rankine cycle. In central tower design with directly heated water as the HTF, the receiver can also be considered part of the Rankine cycle. Operating experiences of CSP plants indicate that plant reliability is significantly impacted by failures in various components of the Rankine cycle. Many damage mechanisms have been identified, which include corrosion, thermal fatigue, creep, and stress corrosion cracking, among others. Much of the damage can be attributed to poor water/steam chemistry and inadequate temperature control. While damage in the Rankine cycle components is common, there is generally lack of comprehensive guidelines created specifically for the operation of these CSP components. Therefore, to improve CSP plant reliability and profitability, it is necessary to better understand the various damage mechanisms experienced by linking them to specific operating conditions, followed by developing a “theory and practice” guideline document for the CSP operators, so that failures in the Rankine cycle components can be minimized. In a major research project sponsored by the U.S. Department of Energy (DOE), effort is being undertaken by EPRI to develop such a guideline document exclusively for the CSP industry. This paper provides an overview of the ongoing DOE project along with a few examples of component failures experienced in the Rankine cycle.

18Cr-9Ni-3Cu-Nb-N steel is widely used for heat exchanger tubes such as super-heaters and reheaters of ultra-super critical power generation boilers. In this study, long-term creep rupture tests were carried out on 18Cr-9Ni-3Cu-Nb-N seamless steel tubes of 7 heat materials, and the specimens of 2 heat materials with different creep rupture strengths were observed by ultra-low voltage scanning electron microscope after creep rupture tests. The results of the investigation of the creep rupture specimens and the coverage ratios of M 23 C 6 on grain boundary were different. The cause of this was estimated to be the difference in B content between the 2 heat materials. Creep rupture tests with different final ST temperatures were also carried out using the same heat material, and it was revealed that the higher final ST temperature, the higher the creep rupture strength. As the final ST temperature is higher, the amount of Nb(C, N) solid solution in the matrix increases, and the amount of precipitation of NbCrN and M 23 C 6 increases during creep, therefore it is assumed that the creep rupture strength increases.

Due to their excellent high temperature oxidation resistance, utilities worldwide are adopting advanced austenitic stainless steels (A-ASS) for critical plant components, such as heat exchangers, as they aim to achieve higher operating conditions. However, challenges may be encountered in developing life assessment and life management strategies for such components. This is because conventional methods used for life assessment, such as measuring steam side oxide scale thickness in ferritic and conventional austenitic material to predict tube metal temperature, may not be successfully applied to A-ASS. In such instances, tracking the formation and evolution of microstructural features during service, may offer a possible method to predict the temperature of these steels. For such metallurgy based lifing strategy to be successful, it is essential to develop a good understanding of microstructure evolution in these steels. In this work one heat of Super 304H, that has been creep tested at 600°C, 650°C and 700°C, with applied stress ranging from 110 to 340 MPa, is characterized using a combination of advanced characterization tools and image analysis methods. The amount of sigma phase formed at the gauge and grip sections of the samples is quantified and the methodology used to quantify this phase is presented. From the results, a time-temperature-transformation diagram for sigma formation is developed.

INCONEL alloy 740H has been specified for tube and pipe for the boiler and heat exchanger sections of AUSC and sCO 2 pilot plants currently designed or under construction. These systems also require fittings and complex formed components such as flanges, saddles, elbows, tees, wyes, reducers, valve parts, return bends, thin-wall cylinders and tube sheets. The initial evaluation of alloy 740H properties, leading to ASME Code Case 2702, was done on relatively small cross-section tube and plate. The production of fittings involves the use of a wide variety of hot or cold forming operations. These components may have complex geometric shapes and varying wall thickness. The utility industry supply chain for fittings is largely unfamiliar with the processing of age-hardened nickel-base alloys. Special Metals has begun to address this capability gap by conducting a series of trials in collaboration with selected fittings manufacturers. This paper describes recent experiences in first article manufacture of several components. The resulting microstructure and properties are compared to the published data for tubular products. It is concluded that it will be possible to manufacture most fittings with properties meeting ASME Code minima using commercial manufacturing equipment and methods providing process procedures appropriate for this class of alloy are followed. INCONEL and 740H are registered trademarks of Special Metals Corporation.

High efficiency in power generation is not only desirable because of economical reasons but also for enhanced environmental performance meaning reduced quantity of forming ash and emissions. In modern medium to large size plants, improvements require supercritical steam values. Furthermore, in future there will be an increasing share of renewables, such as wind and solar power, which will enhance the fluctuation of supply with the consequence that other power sources will have to compensate by operating in a more demanding cyclic or ramping mode. The next generation plant will need to operate at higher temperatures and pressure cycles coupled with demanding hot corrosion and oxidation environments. Such an operation will significantly influence the performance of materials used for boilers and heat exchanger components by accelerating oxidation rates and lowering mechanical properties like creep resistance. The paper discusses the oxidation behaviour of San25, 800H and alloy 263 in supercritical water at temperatures 650 and 700 °C at 250 bar, and compares the changes of mechanical properties of materials at these temperatures.

The recently developed 12%Cr steel VM12-SHC is characterized by very good creep properties at temperatures up to 620°C. This new material development exhibits an excellent oxidation resistance in steam atmospheres at the typical application temperature but also at temperatures up to 650°C. In comparison to the existing 9% Cr grades T/P91 and T/P92, VM12-SHC steel opens due to its excellent oxidation behavior, new possibilities for its application as a heat exchanger boiler component. It was found that outside its application temperature range VM12-SHC also shows, as all 9-12%Cr steels, the appearance of the so called Z-phase. This effect was investigated to understand its influence on creep properties of this class of ferritic/martensitic steels aiming at controlling the microstructure stabilities for future grade developments. Creep testing has been carried out in the temperature range between 525°C and 700°C. Selected crept specimens have been investigated using light optical microscopy, SEM with EDX and TEM. In this study, the oxidation behavior of a number of typical martensitic 9-12%Cr steels was compared with the newly developed 12% Cr steel VM12-SHC. The compositions and morphologies of oxide scales formed after 5000 h exposure steels in simulated steam environments as function of temperature were characterized by light optical metallography and scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDX).

Simple and effective material examination methods are desired for the diffusion bonding process, so that bonding produced components, such as compact heat exchangers, can be used in nuclear applications. Optical microscopy of diffusion bond process samples is a quick way to examine diffusion bond-line microstructure and to evaluate material quality. The stacked nature of a diffusion bonded-block results in distinct regions of grain growth both at and away from the bond interface. Strong diffusion bond materials exhibit grain growth across the original bond interface plane, weak materials have little-to-no growth across. A series of 316H diffusion bonded specimens of differing quality and strength were examined using optical microscopy. The microstructure both at and away from the bond interface was examined over 15mm long sections of the bond-line. A metric for evaluating bond growth is proposed. This is defined as the Bond Line Growth Threshold (BLGT) and is evaluated as the percentage of the bond line with grains meeting the threshold. Here a fraction of the diffusion bond is considered bonded when its grains exceed a threshold of growth past the bond interface. The BLGT is determined through automated image processing methods.

Steels have a proven track record of safe operation in steam power plants for decades. Interest in developing supercritical CO 2 power cycles as a more efficient and sustainable alternative to steam cycles has driven a need to understand steel performance in these new environments. In particular, the potential of the high temperature CO 2 environment to influence the creep behavior of the steel must be determined. Prior research on this topic between the 1960s and 1980s found conflicting conclusions, but nevertheless raised the possibility that carburization during CO 2 exposure may strongly affect the creep behavior. This raises concerns particularly for thin-sectioned components such as compact heat exchangers, where even small rates of carburization can become problematic over long operating lifetimes. To shed light on this issue, this research investigates the creep behavior of austenitic stainless steel 347H and 309H (a higher Cr alternative) at 650°C. Specimens of 0.5, 1.0, and 2.0 mm thickness were tested to further assess the effect of steel thickness. Both steels show a reduction in creep life in CO 2 relative to air, with 309H showing slightly better performance than 374H. Analysis is ongoing to determine the reason for degraded creep properties.

The combustion of coal and biomass fuels in power plants generates deposits on the surfaces of superheater / reheater tubes that can lead to fireside corrosion. This type of materials degradation can limit the lives of such tubes in the long term, and better methods are needed to produce predictive models for such damage. This paper reports on four different approaches that are being investigated to tackle the challenge of modelling fireside corrosion damage on superheaters / reheaters: (a) CFD models to predict deposition onto tube surfaces; (b) generation of a database of available fireside corrosion data; (c) development of mechanistic and statistically based models of fireside corrosion from laboratory exposures and dimensional metrology; (d) statistical analysis of plant derived fireside corrosion datasets using multi-variable statistical techniques, such as Partial Least Squares Regression (PLSR). An improved understanding of the factors that influence fireside corrosion is resulting from the use of a combination of these different approaches to develop a suite of models for fireside corrosion damage.

Oxide scale formation in the inner bore of steam tubing has been identified as a key metric for determining operational parameters and life expectancy of modern boiler systems. Grade 91 tubing is commonly used for the construction of key components within boiler systems designed for power generation operating in the temperature range of 500 to 650 °C. Standard laboratory test procedures involve grinding the surface of test coupons to homogenise their surface structure and improve experimental consistency, however, data presented here shows a discrepancy between laboratory and industrial practices that has long term implications on scale growth kinetics and morphological development. Microstructural analysis of both virgin and ex-service tubing reveals the presence of a pre-existing oxide structure that is incorporated into the inwardly growing scale and is implicated in the formation of multiple laminar void networks. These void networks influence thermal diffusivity across the scale and may function as regions of spallation initiation and propagation.

With nearly half of the world's electricity generation fueled by coal and an increasing focus on limiting carbon dioxide emissions, several technologies are being evaluated and developed to capture and prevent such emissions while continuing to use this primary fossil energy resource. One method aimed at facilitating the capture and processing of the resulting carbon dioxide product is oxy-combustion. With appropriate adjustments to the process, the approach is applicable to both new and existing power plants. In oxy-combustion, rather than introducing ambient air to the system for burning the fuel, oxygen is separated from the nitrogen and used alone. Without the nitrogen from the air to dilute the flue gas, the flue gas volume leaving the system is significantly reduced and consists primarily of carbon dioxide and water vapor. Once the water vapor is reduced by condensation, the purification and compression processes otherwise required for carbon dioxide transport and sequestration are significantly reduced. As an introduction to and overview of this technology, the paper summarizes the basic concepts and system variations, for both new boiler and retrofit applications, and also serves as an organized review of subsystem issues identified in recent literature and publications. Topics such as the air separation units, flue gas recirculation, burners and combustion, furnace performance, emissions, air infiltration issues, and materials issues are introduced.

The capacity of PC power plants in Japan rose to 35GW in 2004. The most current plants have a 600 deg-C class steam temperature and a net thermal efficiency of approximately 42% (HHV). Older plants, which were built in the ‘70s and early ‘80s, will reach the point where they will need to be rebuilt or refurbished in the near future. The steam temperatures of the older plants are 538 deg-C or 566 deg-C. We have done a case study on the refurbishment of one of these plants with the advanced USC technology that uses a 700 deg-C class steam temperature in order to increase the thermal efficiency and to reduce CO 2 emissions. The model plant studied for refurbishing has a 24.1MPa/538 deg-C /538 deg-C steam condition. We studied three possible systems for the refurbishing. The first was a double reheat system with 35MPa/700 deg-C /720 deg-C /720 deg-C steam conditions, the second one was a single reheat 25MPa/700 deg-C/720 deg-C system, the last one was a single reheat 24.1MPa/610 deg-C/720 deg-C system. In addition to these, the most current technology system with 600 deg-C main and reheat temperatures was studied for comparison. The study showed that the advanced USC Technology is suitable for refurbishing old plants. It is economical and environmentally-friendly because it can reuse many of the parts from the old plants and the thermal efficiency is much higher than the current 600 deg-C plants. Therefore, CO 2 reduction is achieved economically through refurbishment.

Advanced power systems that operate at temperatures higher than about 650°C will require nickel-base alloys in critical areas for pressure containment. Age-hardened alloys offer an additional advantage of reduced volume of material compared with lower strength solid solution-strengthened alloys if thinner tube wall can be specified. To date, the only age-hardened alloy that has been approved for service in the time dependent temperature regime in the ASME Boiler and Pressure Vessel Code is INCONEL alloy 740H. Extensive evaluation of seamless tube, pipe, and forged fittings in welded construction, including implant test loops and pilot plants, has shown the alloy to be fit for service in the 650-800°C (1202-1472°F) temperature range. Since, nickel-base alloys are much more expensive than steel, manufacturing methods that reduce the cost of material for advanced power plants are of great interest. One process that has been extensively used for stainless steels and solution-strengthened nickel-base alloys is continuous seam welding. This process has rarely been applied to age-hardened alloys and never for use as tube in the creep-limited temperature regime. This paper presents the initial results of a study to develop alloy 740H welded tube, pipe and fittings and to generate data to support establishment of ASME code maximum stress allowables.

A new martensitic steel for power generation applications was developed: Tenaris High Oxidation Resistance (Thor) is an evolution of the popular ASME grade 91, offering improved steam oxidation resistance and better long-term microstructural stability, with equal or better creep strength. Thanks to its design philosophy, based on consolidated metallurgical knowledge of microstructural evolution mechanisms, and an extensive development performed in the last decade, Thor was engineered to overcome limitations in the use of ASME grade 91, yet allow being processed in the same fashion, permitting the re-use of consolidated best practices for boiler fabrication. In order to evaluate the possibility to produce complete pressure part systems, various tests to manufacture components have been performed on Thor pipes and tubes (i.e. finning, bending, welding) and on Thor forged material (i.e. flanges). In all cases consolidated industrial best practices used on ASME grade 91 were applied, and resulting properties met ASME requirements.