Despite the significant progress achieved in power generation technologies in the past two decades, finding effective solutions to further reduce emissions of harmful gases from thermal power plant still remains the major challenge for the power generation industry as well as alloy material developers. In the European material programmes COST 522 and COST 536, based on the existing 9-12%Cr creep resisting steels, an advanced 9%Cr-Mo martensitic alloy, C(F)B2 (GX13CrMoCoVNbNB9-2-1) alloy has been developed. By modification through alloying of boron and cobalt and together with other micro-adjustment of the composition, C(F)B2 alloys has showed very encouraging properties. The current paper summaries the development and evaluation of the matching filler metals for C(F)B2 grade. The design of the filler metal composition is discussed and comparison is made with the parent materials in respect to the alloy additions and microstructure. The mechanical properties of the weld metals at ambient temperature are examined. Creep properties of both undiluted weld metals and cross-weld joints are examined through stress rupture test and the data are evaluated and compared with those of the base alloy and other existing 9%Cr-Mo creep resisting steels.

In the late 1980s, the domestic utility industry experienced failures in dissimilar metal welds (DMWs) between low-alloy ferritic tubing and austenitic tubing in superheaters and reheaters. Extensive research by EPRI identified that nickel-based filler metals significantly improved service life compared to 309 SS filler metals. Additionally, optimized joint geometries and increased weld metal reinforcement were found to further enhance durability. A new nickel-based filler metal was developed with thermal expansion properties similar to the low-alloy base metal, along with a low chromium content designed to minimize the carbon-denuded zone. However, this filler metal was never commercialized due to its tendency to microfissure, which resulted in a shorter-than-expected service life. This paper explores further investigations into the microfissuring of this filler metal and examines long-term testing to assess its suitability for high-temperature applications.

The Department of Energy and Ohio Coal Development Office jointly sponsored research to evaluate materials for advanced ultrasupercritical (A-USC) coal power plants, testing both monolithic tube materials and weld overlay combinations under real operating conditions. Testing was conducted in the highly corrosive, high-sulfur coal environment of Reliant Energy's Niles Plant Unit 1 boiler in Ohio. After 12 months of exposure, researchers evaluated six monolithic tube materials and twelve weld overlay/tube combinations for their high-temperature strength, creep resistance, and corrosion resistance in both steam-side and fire-side environments. Among the monolithic materials, Inconel 740 demonstrated superior corrosion resistance with the lowest wastage rate, while EN72 emerged as the most effective weld overlay material across various substrates, offering consistent protection against corrosion.

Solidification cracking (SC) is a defect that occurs in the weld metal at the end of the solidification. It is associated with the presence of mechanical and thermal stresses, besides a susceptible chemical composition. Materials with a high solidification temperature range (STR) are more prone to the occurrence of these defects due to the formation of eutectic liquids wetting along the grain boundaries. The liquid film collapses once the structure shrinks and stresses act during the solidification. Thus, predicting the occurrence of SC before the welding process is important to address the problem and avoid the failure of welded components. The nuclear power industry has several applications with dissimilar welding and SC-susceptible materials, such as austenitic stainless steels, and Ni-based alloys. Compositional optimization stands out as a viable approach to effectively mitigate SC in austenitic alloys. The integration of computational modeling into welding has significantly revolutionized the field of materials science, enabling the rapid and cost-effective development of innovative alloys. In this work, a SC resistance evaluation is used to sort welding materials based on a computational fluid dynamic (CFC) model and the alloy's chemical composition. An index named Flow Resistance Index (FRI) is used to compare different base materials and filler metals as a function of dilution. This calculation provides insights into the susceptibility to SC in dissimilar welding, particularly within a defined dilution range for various alloys. To assess the effectiveness of this approach, the relative susceptibility of the materials was compared to well-established experimental data carried out using weldability tests (Transvarestraint and cast pin tear test). The FRI calculation was programmed in Python language and was able to rank different materials and indicate the most susceptible alloy combination based on the dilution and chemical composition.

Super Duplex stainless steels (SDSS) are alloys based on the Fe-Cr-Ni-N system. The chemical composition is tailored to achieve a balanced microstructure of 50% ferrite and 50% austenite. Hyper Duplex Stainless Steels (HDSS) are also duplex materials distinguished by their remarkable yield strength (≥700 MPa) and corrosion resistance (PREN>48). They have been developed as an alternative to the well-established SDSS when superior mechanical and corrosion performance is required. This enhanced performance is attributed to alloying additions, primarily Cr, Mo, and N. In this study, a comparison is conducted between filler metals of SDSS and HDSS for the root welding of SDSS plates. The gas tungsten arc welding (GTAW) process was used to carry out root welding passes and Gas Metal Arc Welding (GMAW) for filling passes on SDSS substrates arranged in a V groove to simulate a repair scenario. The heat input was controlled in both processes, keeping it below 2.0 kJ/mm in the GTAW and 1.2 kJ/mm in the GMAW. GTAW with constant current was used and the parameters achieved producing full penetration welds with SDSS and HDSS. In this case, Nitrogen was used as backing gas to avoid oxidation of the root. Thus, a special GMAW-Pulsed version was applied to achieve good wettability and defect-free joints. ASTM G48 tests were performed to evaluate the corrosion resistance through Critical Pitting Testing (CPT) analysis on the root pass, microstructural analysis via optical microscopy, and impact toughness. Consequently, a comprehensive examination of the welded joints outlines manufacturing conditions, limitations, and the applications of SDSS and HDSS filler metals.

Grade 91 steel has been widely utilized in power plants over the last 20 years. Its specification worldwide has dramatically increased since the acceptance of Code Case 1943 for this material in 1983. Recent evaluation of a combination of ex-service Grade 91 steel components and virgin material has provided a unique opportunity to independently assess the performance of a combination of base metal and weldments. This approach has been grounded in the fundamental objective of linking metallurgical risk factors in Grade 91 steel to the cross-weld creep performance. Establishing critical risk factors in 9Cr steels is regarded as a key consideration in the integration of a meaningful life management strategy for these complex steels. The potential metallurgical risk factors in Grade 91 steel have been fundamentally divided into factors which affect strength, ductility or both. In this study, two heats of ex-service Grade 91 steel which exhibit dramatic differences in strength and ductility have been evaluated in the ex-service condition and re-heat treated to establish a relevant set of strength:ductility variables. This set of variables includes [strength:ductility]: low:low, medium:low, low:high and medium:high. The influence of these strength:ductility variables were investigated for feature type cross-weld creep tests to better evaluate the influence of the initial base material condition on cross-weld creep performance.

Achieving high temperature creep strength while maintaining rupture ductility in weld metal for austenitic stainless steel weldments has always been challenging. In the late 1940's and early 1950's, independent work in both Europe and the USA resulting in what is known today as the 16-8-2 (nominally16% chromium -8% nickel -2% molybdenum) stainless steel weld metal. Philo 6 and shortly thereafter at Eddystone used the alloy to construct the first supercritical boilers and piping in the USA. Concurrent with domestic boiler and piping fabrication, the US Navy was also using this material for similar supercritical applications. Over the decades, enhanced performance has evolved with variations of the basic composition and by adding specific residual elements. Controlled additions of P, B, V, Nb and Ti have been found to greatly enhance elevated temperature as well as cryogenic behavior. The history of these developments, example compositions and areas of use as well as mechanical property results are presented.

The INCONEL filler metals 72 and 72M have been utilized significantly for weld overlay protection of superheaters and reheaters, offering enhanced corrosion and erosion resistance in this service. Laboratory data conducted under simulated low-NOx combustion conditions, field exposure experience, and laboratory analysis (microstructure, chemical composition, overlay thickness measurements, micro-hardness) of field-exposed samples indicate that these overlay materials are also attractive options as protective overlays for water wall tubes in low-NOx boilers. Data and field observations will be compared for INCONEL filler metals 72, 72M, 625 and 622.

Developed 9Cr-3W-3Co-Nd-B heat-resistant steel SAVE12AD (Recently designated as ASME Grade 93) pipes and tubes have higher creep strength in both base metal and welded joints than conventional high Cr ferritic steels such as ASME Grades 91, 92 and 122. The welded joints of SAVE12AD tubes with commercial filler wire for W62-10CMWV-Co (Gr. 92) or Ni base filler wire ERNiCr-3 (Alloy82) also have much better creep rupture strength than those of conventional steels because of suppression of refining in the Heat-Affected-Zone (HAZ). However, the creep rupture strength of weld metal of W62-10CMWV-Co was marginal. Additionally, the hot cracking susceptibility of weld metal using Ni base filler wire ERNiCr-3 was occasionally below the required level. Similar welding consumable for SAVE12AD has been developed to solve these problems. Optimization of nickel, neodymium and boron contents on similar welding consumable enables to obtain both the good long-term creep rupture strength and low enough hot cracking susceptibility of weld metal. Consequently, SAVE12AD welded joint is expected to be applied of piping and tubing above 600°C in USC power plants because of its good properties with similar welding consumable.

Thick-walled valves, steam chests, and casings suffer service damage from thermal stresses due to the significant through-thickness temperature gradients that occur during operating transients. Fatigue is the primary damage mechanism, but recent examination of turbine casings has revealed extensive sub-surface creep cavitation. The low primary stress levels for these components are unlikely to cause creep damage, so detailed inelastic analysis was performed to understand the complex stress state that evolves in these components. This illustrates that fatigue cycles can cause elevated stresses during steady operation that cause creep damage. This paper will explore a case study for a 1CrMoV turbine casing where the stress-strain history during operating transients will be related to damage in samples from the turbine casing. This will also highlight how service affects the mechanical properties of 1CrMoV, highlighting the need for service- exposed property data to perform mechanical integrity assessments. Finally, the consequences for repair of damage will be discussed, illustrating how analysis can guide volume of material for excavation and selection of weld filler metal to maximize the life of the repair. This, in turn, will identify opportunities for future weld repair research and material property data development.

Metallurgical factors affecting the fusion boundary failure and damage mechanism of DMWs (Dissimilar Metal Welds) between the CSEF (Creep Strength Enhanced Ferritic) steels and austenitic steels were experimentally and theoretically investigated and discussed. Long-term exservice DMWs up to 123,000 hours were investigated; the precipitates near the fusion boundary were identified and quantitatively evaluated. Comparing with the other generic Ni-based weld material, MHPS original filler metal HIG370 (Ni bal.-16Cr-8Fe-2Nb-1Mo) showed superior suppression effect on fusion boundary damage of DMWs, which was verified by both of the microstructure observation and thermodynamic calculation. Based on the microstructure observation of crept specimen and ex-service samples of DMWs, temperature, time and stress dependence of fusion boundary damage of DMWs were clarified. Furthermore, fusion boundary damage morphology and mechanism due to precipitation and local constituent depletion was discussed and proposed from metallurgical viewpoints.

Qualifying welding procedures for repair of components in high temperature service requires careful consideration of factors including identification of the materials involved, existing mechanical properties and service operating parameters such as temperature, pressure and environment. Selection of weld metals to match, under match or overmatch base material as well as direct and indirect consequences on the heat-affected zone also require evaluation. Application of post weld heat treatment and ramifications where dissimilar base materials are involved are discussed plus the necessity of conducting tests at the operating temperatures and conditions where information is not available from the literature. Each of these factors is discussed and examples provided.

This paper discusses the development of matching filler metals for new creep-resistant steels (P911 and P92) that enable higher operating temperatures (600-625 °C) in fossil fuel power plants, improving efficiency. The filler metals were evaluated with long-term testing (up to 30,000 hours) confirming their suitability for welded components in power stations. This development benefits not only power plant operators by reducing maintenance costs and downtime, but also builders, suppliers, and inspection bodies by providing a reliable solution for high-temperature applications. Additionally, matching filler metals developed for VM12 (12% Cr) martensitic steel are discussed.

In conventionally fired power plants, appropriate materials are required which correspond to the different temperature and oxidizing conditions in the boiler and in the superheater sections. Pipe steels with 2 1/4 Cr (P22; T23; T24) must be welded to 9 - 12 % Cr steels (P91; E911; P92; VM12). In this area, the choice of the appropriate welding filler material is vital for the quality of the weldment. This report highlights the possibilities for achieving optimal properties in differing dissimilar metal welds under conditions of reduced carbon diffusion.

Inconel alloy 740 is a precipitation-hardenable nickel-chromium-cobalt alloy with niobium, derived from Nimonic 263, and is considered a prime candidate for the demanding conditions of advanced ultrasupercritical boilers. It offers an exceptional combination of stress rupture strength and corrosion resistance under steam conditions of 760°C (1400°F) and 34.5 MPa (5000 psi), surpassing other candidate alloys. Initially, Inconel alloy 740 was prone to liquation cracking in sections thicker than 12.7 mm (0.50 in), but this issue has been resolved through modifications in the chemical composition of both the base and weld metals. Current concerns focus on the weld strength reduction factor for direct-age weldments. This has led to further development in welding Inconel alloy 740 using Haynes 282, which has higher creep strength and may mitigate the weld strength reduction factor. This study details successful efforts to eliminate liquation cracking and compares the properties of Inconel alloy 740 and Haynes 282 filler materials using the gas tungsten arc welding process.

Development of steels used in the power generation industry for the production of boilers characterized by supercritical parameters poses new challenges. The introduction of new combinations of alloying agents aimed at obtaining the best possible mechanical properties, including creep resistance, affects the weldability of new steels. Each of the latter has to undergo many tests, particularly as regards bending and welding, in order to enable the development of technologies ensuring failure-free production and assembly of boiler systems. Martensitic steels containing 9% Cr, used in the manufacturing of steam superheaters, are characterized by excellent creep resistance and, at the same time, low oxidation resistance at a temperature in excess of 600°C. In turn, steels with a 12% Cr content, i.e., VM12-SHC or X20CrMoV12-1 are characterized by significantly higher oxidation resistance but accompanied by lower strength at higher temperatures, which translates to their limited application in the production of boilers operating at the most top parameters.X20CrMoV12-1 was withdrawn from most of the power plants, and VM12-SHC was supposed to replace it, but unfortunately, it failed in regards to creep properties. To fulfill the gap a new creep strength-enhanced ferritic steel for service in supercritical and ultra-supercritical boiler applications was developed by Tenaris and it is designated as Thor115 (Tenaris High Oxidation Resistance). This paper covers the experience gained during the first steps of fabrication, which includes cold bending and welding of homogenous joints.

As flux cored wires for gas metal arc welding offer several technical and economic advantages they are becoming more and more popular. Matching flux cored wires for welding P92 have already been available for several years. A matching flux cored wire for welding the Co-alloyed cast steel CB2, which is used for turbine and valve casings operating at steam temperatures of up to 620°C, was developed recently. To connect casings with P92 pipes, dissimilar welding of CB2 to P92 is necessary. This can be done with filler metal that matches either CB2 or P92. Pre-tests have confirmed that flux cored arc welding (FCAW) can generally be used for dissimilar joint welding of CB2 to P92. To evaluate creep rupture strength dissimilar welds were performed with filler metal matching CB2 and P92, respectively. TIG welding was used for the root and the second pass and FCAW for the intermediate and final passes. Cross-weld tensile tests, side bend tests and impact tests of weld metals and heat-affected zones were carried out at ambient temperatures after two post-weld heat treatments (PWHT), each at 730°C for 12 hours. Creep rupture tests of cross-weld samples were performed at 625°C. This study compares the results of the mechanical tests at ambient temperature and the creep rupture tests, and discusses why P92 filler metals are preferred for such welds.

This paper addresses the limitations of P92 steel used in ultra-supercritical power plants, particularly ferrite formation in thick components and its impact on short- and long-term properties. A guideline for determining ferritic content in P92 steel is presented. Furthermore, a novel 12% Cr boiler steel grade, VM12-SHC, is introduced. This new material offers good creep properties and oxidation resistance, overcoming the limitations of P92 steel. Finally, the development of matching filler metals for welding P92 and VM12-SHC steels is presented, ensuring optimal weld compatibility and performance in power plant applications.

Components such as tubes, pipes and headers used in power generation plants are operated in a creep regime and have a finite life. During partial replacement, creep exhausted materials are often welded to virgin materials with superior properties. The aim of this study was to identify a suitable weld filler material to join creep aged X20CrMoV12-1 to a virgin P91 (X10CrMoVNbV9-1) steel. Two dissimilar joints were welded using the gas tungsten arc welding (GTAW) process for the root passes, and manual metal arc (MMA) welding for filling and capping. The X20 and the P91 fillers were selected for joining the pipes. The samples were further heat treated at 755°C to stress relief the samples. Microstructural evolution and mechanical properties of the weld metals were evaluated. The average hardness of X20 weld metal (264 HV10) was higher than the hardness measurement of P91 weld metal (206 HV10). The difference in hardness was attributed to the high carbon content in X20 material. The characterisation results revealed that the use of either X20 or P91 weld filler for a butt weld of creep aged X20 and virgin P91 pipes material does not have a distinct effect on the creep life and creep crack propagation mechanism. Both weld fillers (X20 and P91) are deemed to be suitable because limited interdiffusion (<10 μm) of chromium and carbon at the dissimilar weld interface was observed across the fusion line. The presence of a carbon ‘denuded’ zone was limited to <10 μm in width, based on the results from local measurements of the precipitate phase fractions using image analysis and from elemental analysis using EDS. However the nanoindentation hardness measurements across the fusion line could not detect any ‘soft’ zone at the dissimilar weld interface. The effect of the minute denuded zone was also not evident when the samples were subjected to nanoindentation hardness testing, tensile mechanical testing, Small Punch Creep Test (SPCT) and cross weld uniaxial creep testing.

Dynamic development of steels used in power engineering industry for the production of boilers characterised by supercritical parameters poses new welding challenges. The introduction of new combinations of alloying agents aimed at obtaining the best possible mechanical properties, including creep resistance, affects the weldability of new steels. Each of the latter have to undergo many tests, particularly as regards bending and welding, in order to enable the development of technologies ensuring failure-free production and assembly of boiler systems. Martensitic steels containing 9% Cr, used in the manufacturing of steam superheaters, are characterised by good creep resistance and, at the same time, low oxidation resistance at a temperature in excess of 600°C. In turn, steels with a 12% Cr content are characterised by significantly higher oxidation resistance, but accompanied by lower strength at higher temperatures, which translates to their limited application in the production of boilers operating at the highest parameters. The niche between the aforesaid steels is perfectly filled by austenitic steels, the creep resistance and oxidation resistance of which are unquestionable. This article presents experience gained while welding dissimilar joints of advanced steels TEMPALOY AA-1 and T92, with the use of EPRI P87, Inconel 82 and Inconel 617 filler metals. The tests involving the said steel grades belong to the very few carried out in the world.