Unpredictable failures near the phase boundary in Grade 91 dissimilar metal welds (DMW) with nickel based filler metals represent a significant problem for the power generation industry. In order to determine the root cause for these failures, it is necessary to understand the formation of the microstructure in the weld regions around the site of failure. Thermal histories were therefore measured inside the Grade 91 steel heat affected zone (HAZ) of an autogenous weld and of a DMW in the form of bead on plate with Alloy 625 to study the effect of the weld thermal cycle on microstructural formation. It was found that the HAZ in the DMW experienced longer dwell time at high temperatures because of the latent heat of fusion released during Alloy 625 solidification (1350 - 1125 °C). This allowed longer time for carbide dissolution and phase transformations in the DMW than in the autogenous weld. Additionally, the 625 filler metal created a large chemical potential gradient for carbon, which when combined with longer dwell times, yielded carbon depletion in the heat affected zone. Retention of δ ferrite in the coarse grained HAZ (CGHAZ) of DMWs was found to be an indicator for these mechanisms.

Metallurgical factors affecting the fusion boundary failure and damage mechanism of DMWs (Dissimilar Metal Welds) between the CSEF (Creep Strength Enhanced Ferritic) steels and austenitic steels were experimentally and theoretically investigated and discussed. Long-term exservice DMWs up to 123,000 hours were investigated; the precipitates near the fusion boundary were identified and quantitatively evaluated. Comparing with the other generic Ni-based weld material, MHPS original filler metal HIG370 (Ni bal.-16Cr-8Fe-2Nb-1Mo) showed superior suppression effect on fusion boundary damage of DMWs, which was verified by both of the microstructure observation and thermodynamic calculation. Based on the microstructure observation of crept specimen and ex-service samples of DMWs, temperature, time and stress dependence of fusion boundary damage of DMWs were clarified. Furthermore, fusion boundary damage morphology and mechanism due to precipitation and local constituent depletion was discussed and proposed from metallurgical viewpoints.

In the late 1980s, the domestic utility industry experienced failures in dissimilar metal welds (DMWs) between low-alloy ferritic tubing and austenitic tubing in superheaters and reheaters. Extensive research by EPRI found that nickel-based filler metals provided significant service life improvements over 309 stainless steel filler metals. Improved joint geometries and additional weld metal reinforcement were determined to extend service life further. A new nickel-based filler metal was also developed, exhibiting thermal expansion properties similar to the low-alloy base metal and a low chromium content that would result in a smaller carbon-depleted zone than currently available fillers. However, this new filler metal was never commercialized due to a tendency for microfissuring, resulting in less than desired service life. This paper discusses further investigation into the filler metal microfissuring issue and examines long-term testing to determine the filler's suitability for high-temperature applications.

In this paper, the dissimilar metal welds (DMWs) between 617B nickel-based alloy and 10%Cr martensitic heat-resistant steel filled by 617 filler metal was studied, focused on the high temperature creep rupture properties. The high temperature creep rupture properties of welded joints with different welding processes were tested, and the microstructure of welded joints before and after the creep rupture test was observed by OM and SEM. The results showed that, there were three failure modes: base metal failure, type W failure and interface failure, among which interface failure caused the most serious life reduction. The welded joints using ER NiCr-3 filler metal reduced the strain concentration at the interface, so the fracture location shifted from the interface to HAZ of 10%Cr martensitic heat-resistant steel under high temperature and low stress conditions, and creep rupture life was improved. Similarly, weld cap shifted the creep crack propagation path by changing the groove form, so as to altered the stress state of joint and prolong the creep rupture life.

Carbon migration in narrow-gap welding joints of dissimilar steels has been studied using bead-on-plate specimens to determine the factors that influence the formation of a soft ferrite structure in the carbon-depleted zone. Carbon migration was found to occur during tempering, with a ferrite structure formed at the intersection of multiple layers due to severe carbon migration. This was attributed to a steep gradient in Cr content caused by the low fusion penetration at the intersection. Experimental results and the relationship between fusion penetration and weld bead alignment confirmed that low fusion penetration is the main cause of ferrite-structured carbon depleted zones.

Dissimilar metal welds between T91 ferritic steels and TP347H austenitic alloys are commonly used in fossil power plants in China. Premature failure of such dissimilar welds can occur, resulting in unplanned plant outages that can cause huge economic losses. In this article, microstructural evolution of T91/TP347H dissimilar welds after different service conditions were studied, mechanical properties before and after service were also analyzed, a full investigation into the failure cause was carried out. The results show, the dissimilar metal welds in the as-welded condition consists of a sharp chemical concentration gradient across the fusion line, failure is attributed to the steep microstructural and mechanical properties gradients, formation of interfacial carbides that promote creep cavity formation.

According to ASME Case N-888-3, Similar and Dissimilar Metal Welding Using Ambient Temperature SMAW or Machine GTAW Temper Bead Technique, a 48 hr waiting period before conducting the final nondestructive examination (NDE) is required when ferritic filler weld metal is used. The purpose of the 48 hr hold is to confirm the absence of hydrogen-induced cracking in the temper bead heat-affected zone. In previous research, the effect of post-weld heat treatment (PWHT) and temper bead welding (TBW) on the hydrogen-induced cracking (HIC) susceptibility in the coarse-grained heat-affected zone (CGHAZ) in welds of SA-508, P-No. 3 Group 3, pressure vessel steel was investigated using the Delayed Hydrogen Cracking Test (DHCT). In that previous study, the Gleeble thermomechanical simulator was used to generate six CGHAZ microstructural conditions: as-welded (AW), PWHT, and AW with single a TBW reheat at 675, 700, 725, and 735°C. Hydrogen was introduced to the specimen through cathodic charging under in situ constant tensile stress. The HIC susceptibility for these microstructures was ranked by the DHCT at a diffusible hydrogen level significantly exceeding typical GTAW and SMAW processes. The work described in this paper investigates the susceptibility to HIC of these same CGHAZ microstructures with DHCT at variable current densities, further ranking each condition. Test results were analyzed by fracture surface examination of failed tests, and cross-section microstructural analysis under a scanning electron microscope (SEM). Future steps include evaluating critical hydrogen content levels using gas chromatography for each condition. The results from this study will be used to consider potential elimination of the NDE hold time requirement in Case N-888-3 when ferritic weld metal is used.

Dissimilar metal welds (DMWs) between ferritic and austenitic materials at elevated temperatures have long posed challenges for boiler manufacturers and operators due to their potential for premature failure. As the industry moves towards higher pressures and temperatures to enhance boiler efficiencies, there is a need for superior weld metals and joint designs that optimize the economy of modern boilers and reduce reliance on austenitic materials for steam headers and piping. EPRI has developed a new filler metal, EPRI P87, to enhance the performance of DMWs. Previous work has detailed the development of EPRI P87 for shielded metal arc welding electrodes, gas-tungsten arc welding fine-wire, and its application in an ultra-supercritical steam boiler by B&W. This study examines the weldability of EPRI P87 consumables through various test methods, including Varestraint testing (both trans and spot), long-term creep testing (approximately 10,000-hour running tests), procedure qualification records for tube-to-tube weldments between traditional/advanced austenitic steels and creep-strength enhanced ferritic steels, and elevated temperature tensile testing. Macroscopic examinations from procedure qualification records using light microscopy confirmed the weldability and absence of cracking across all material combinations. The findings demonstrate that EPRI P87 is a weldable alloy with several advantages for DMW applications and highlight that specific weld joint configurations may necessitate the use of high-temperature tensile data for procedure qualifications.

This study addresses the welding challenges encountered when joining Haynes 282, a heat-resistant superalloy, to 3.5NiCrMoV high-strength low alloy steel (HSLA) for advanced power plant applications, particularly in thick-section components like rotors. The project demonstrated successful thick-section dissimilar metal welding up to 76 mm (3 in.) using two techniques: keyhole tungsten inert gas welding and conventional gas tungsten arc welding with Haynes 282 filler metal. Various groove weld geometries were evaluated, supported by computational weld modeling to predict and minimize weld distortion. The results validate these welding approaches for critical power plant components requiring both high-temperature performance and cost-effectiveness.

An innovative additively manufactured gradient composite transition joint (AM-GCTJ) has been designed to join dissimilar metals, to address the pressing issue of premature failure observed in conventional dissimilar metal welds (DMWs) when subjected to increased cyclic operating conditions of fossil fuel power plants. The transition design, guided by computational modeling, developed a gradient composite material distribution, facilitating a smooth transition in material volume fraction and physical properties between different alloys. This innovative design seeks to alleviate structural challenges arising from distinct material properties, including high thermal stress and potential cracking issues resulting from the thermal expansion mismatch typically observed in conventional DMWs. In this study, we investigated the creep properties of transition joints comprising Grade 91 steel and 304 stainless steel through a combination of simulations and creep testing experiments. The implementation of a gradient composite design in the plate transition joint resulted in a significant enhancement of creep resistance when compared to the baseline conventional DMW. For instance, the creep rupture life of the transition joint was improved by > 400% in a wide range of temperature and stress testing conditions. Meanwhile, the failure location shifted to the base material of Grade 91 steel. Such enhancement can be primarily attributed to the strong mechanical constraint facilitated by the gradient composite design, which effectively reduced the stresses on the less creep-resistant alloy in the transition zone. Beyond examining plate joints, it is crucial to assess the deformation response of tubular transition joints under pressure loading and transient temperature conditions to substantiate and demonstrate the effectiveness of the design. The simulation results affirm that the tubular transition joint demonstrates superior resistance compared to its counterpart DMW when subjected to multiaxial stresses in tubular structures. In addition, optimization of the transition joint’s geometry dimensions has been conducted to diminish the accumulated deformation and enhance the service life. Lastly, the scalability and potential of the innovative transition joints for large-diameter pipe applications are addressed.

In order to improve thermal efficiency of fossil-fired power plants through increasing steam temperature and pressure high strength martensitic 9-12%Cr steels have extensively been used, and some power plants have experienced creep failure in high temperature welds after several years operations. The creep failure and degradation in welds of longitudinally seam-welded Cr- Mo steel pipes and Cr-Mo steel tubes of dissimilar metal welded joint after long-term service are also well known. The creep degradation in welds initiates as creep cavity formation under the multi-axial stress conditions. For the safety use of high temperature welds in power plant components, the complete understanding of the creep degradation and establishment of creep life assessment for the welds is essential. In this paper creep degradation and initiation mechanism in welds of Cr-Mo steels and high strength martensitic 9-12%Cr steels are reviewed and compared. And also since the non-destructive creep life assessment techniques for the Type IV creep degradation and failure in high strength martensitic 9-12%Cr steel welds are not yet practically established and applied, a candidate way based on the hardness creep life model developed by the authors would be demonstrated as well as the investigation results on the creep cavity formation behavior in the welds. Additionally from the aspect of safety issues on welds design an experimental approach to consider the weld joint influence factors (WJIF) would also be presented based on the creep rupture data of the large size cross-weld specimens and component welds.

Components in ultrasupercritical steam (USC) boilers will operate under significantly more severe conditions than current subcritical and supercritical steam boilers. Existing construction rules for power boilers lack design guidance or criteria to assess the adequacy of designs for USC conditions. A Department of Energy (DOE) project addresses this by evaluating advanced materials under conditions similar to potential USC service environments. The project focuses on six tubing alloys and four thick-section alloys. Testing is underway for pressurized tube bends, notched thick-section bars, fatigue, and thermal shock on thick-section tubing made of materials like CCA617, Alloy 230, and Alloy 740. Further testing is planned for pressurized tubes, dissimilar metal welds, and thick-section weldments. This paper summarizes the status of this initial testing program aimed at enabling USC boiler material qualification.

Components such as tubes, pipes and headers used in power generation plants are operated in a creep regime and have a finite life. During partial replacement, creep exhausted materials are often welded to virgin materials with superior properties. The aim of this study was to identify a suitable weld filler material to join creep aged X20CrMoV12-1 to a virgin P91 (X10CrMoVNbV9-1) steel. Two dissimilar joints were welded using the gas tungsten arc welding (GTAW) process for the root passes, and manual metal arc (MMA) welding for filling and capping. The X20 and the P91 fillers were selected for joining the pipes. The samples were further heat treated at 755°C to stress relief the samples. Microstructural evolution and mechanical properties of the weld metals were evaluated. The average hardness of X20 weld metal (264 HV10) was higher than the hardness measurement of P91 weld metal (206 HV10). The difference in hardness was attributed to the high carbon content in X20 material. The characterisation results revealed that the use of either X20 or P91 weld filler for a butt weld of creep aged X20 and virgin P91 pipes material does not have a distinct effect on the creep life and creep crack propagation mechanism. Both weld fillers (X20 and P91) are deemed to be suitable because limited interdiffusion (<10 μm) of chromium and carbon at the dissimilar weld interface was observed across the fusion line. The presence of a carbon ‘denuded’ zone was limited to <10 μm in width, based on the results from local measurements of the precipitate phase fractions using image analysis and from elemental analysis using EDS. However the nanoindentation hardness measurements across the fusion line could not detect any ‘soft’ zone at the dissimilar weld interface. The effect of the minute denuded zone was also not evident when the samples were subjected to nanoindentation hardness testing, tensile mechanical testing, Small Punch Creep Test (SPCT) and cross weld uniaxial creep testing.

Enhancement of the steam conditions is one of the most effective measures to achieve the goal of higher thermal efficiency. 700°C class A-USC (Advanced Ultra Super Critical Steam Conditions) power plant is one of the remarkable technologies to achieve the goal and reduce CO 2 emissions from fossil fuel power plants. Toshiba has been working on the A-USC development project with subsidy from METI (Ministry of Economy, Trade and Industry) and NEDO (New Energy and Industrial Technology Development Organization). In this project, A-USC power plants with steam parameters of 35MPa 700/720/720°C were considered. To date, various materials have been developed and tested to verify their characteristics for use in A-USC power plants. And some of these materials are being investigated as to their suitability for use in long term. Together with members of the project, we carried out the boiler component test using a commercially-operating boiler. We manufactured a small-scale turbine casing made of nickel-based alloy, and supplied it for the test. In addition, we manufactured a turbine rotor for turbine rotation tests, and carried out the test at 700°C and rotating speed of 3,600rpm conditions. In this paper, we show the results of the A-USC steam turbine development obtained by the project.

Qualifying welding procedures for repair of components in high temperature service requires careful consideration of factors including identification of the materials involved, existing mechanical properties and service operating parameters such as temperature, pressure and environment. Selection of weld metals to match, under match or overmatch base material as well as direct and indirect consequences on the heat-affected zone also require evaluation. Application of post weld heat treatment and ramifications where dissimilar base materials are involved are discussed plus the necessity of conducting tests at the operating temperatures and conditions where information is not available from the literature. Each of these factors is discussed and examples provided.

This study conducted creep tests, microstructural, and hardness analyses on SA213T23-TP347H dissimilar weld joints of long-term serviced coal-fired boiler final superheater tube. The welded joint (SA213 T23-TP347H) of the superheater tube, after approximately 105,000 hours of service, was sampled for creep life assessment and maintenance planning. Creep tests were conducted at 600°C under three stress conditions: 100, 140, and 160MPa. Most cracks were observed in the heat-affected zone of T23, and compared to unused tubes, the creep life consumption rate was approximately 90%. All dissimilar weld joints used welding rods similar in chemical composition to T23, and significant hardness reduction occurred in the flame-affected zone.

Early supercritical units such as American Electric Power (AEP) Philo U6, the world’s first supercritical power plant, and Eddystone U1 successfully operated at ultrasupercritical (USC) levels. However due to the unavailability of metals that could tolerate these extreme temperatures, operation at these levels could not be sustained and units were operated for many years at reduced steam (supercritical) conditions. Today, recently developed creep strength enhanced ferritic (CSEF) steels, advanced austenitic stainless steels, and nickel based alloys are used in the components of the steam generator, turbine and piping systems that are exposed to high temperature steam. These materials can perform under these prolonged high temperature operating conditions, rendering USC no longer a goal, but a practical design basis. This paper identifies the engineering challenges associated with designing, constructing and operating the first USC unit in the United States, AEP’s John W. Turk, Jr. Power Plant (AEP Turk), including fabrication and installation requirements of CSEF alloys, fabrication and operating requirements for stainless steels, and life management of high temperature components

In this study, creep rupture behaviors and rupture mechanisms of dissimilar welded joint between Inconel 617B and COST E martensitic steel were investigated. Creep tests were conducted at 600 ℃ in the stress range 140-240 MPa. Scanning electron microscopy (SEM) and micro-hardness were used to examine the creep rupture behaviors and microstructure characteristics of the joint. The results indicated that the rupture positions of crept joints shifted as stress changed. At higher stress level, the rupture position was located in the base metal (BM) of COST E martensitic steel with much plastic deformation and necking. At relatively lower stress level, the rupture positions were located in the fine-grained heat affected zone (FGHAZ) of COST E or at the interface between COST E and WM both identified to be brittle fracture. Rupture in the FGHAZ was caused by type Ⅳ crack due to matrix softening and lack of sufficient precipitates pinning at the grain boundaries (GBs). Rupture at the interface was related to oxide notch forming at the interface.

Due to a high degree of mixing between substrate and weld deposit, fusion welding of dissimilar metal joints functionally produce new, uncharacterized alloys. In the power generation industry, such mixing during the application of cobalt-based hardfacing has led to a disconcerting number of failures characterized by the hard overlay welds disbonding. Investigations into this failure mechanism point to the unknown alloy beneath the surface of the hardfacing layer transforming, hardening, and becoming brittle during service. This research describes a methodology for exploring a chemical space to identify alloy combinations that are expected to be safe from deleterious phase formation. Using thermodynamic modeling software and a stepped approach to potential chemistries, the entire phase stability space over the full extent of possible mixing between substrate and weld material can be studied. In this way diffusion effects – long term stability – can also be accounted for even in the case where mixing during application is controlled to a low level. Validation of predictions specific to the hardfacing system in the form of aged weld coupons is also included in this paper. Though the application of this methodology to the hardfacing problem is the focus of this paper, the method could be used in other weld- or diffusion- combinations that are expected to operate in a high temperature regime.

As flux cored wires for gas metal arc welding offer several technical and economic advantages they are becoming more and more popular. Matching flux cored wires for welding P92 have already been available for several years. A matching flux cored wire for welding the Co-alloyed cast steel CB2, which is used for turbine and valve casings operating at steam temperatures of up to 620°C, was developed recently. To connect casings with P92 pipes, dissimilar welding of CB2 to P92 is necessary. This can be done with filler metal that matches either CB2 or P92. Pre-tests have confirmed that flux cored arc welding (FCAW) can generally be used for dissimilar joint welding of CB2 to P92. To evaluate creep rupture strength dissimilar welds were performed with filler metal matching CB2 and P92, respectively. TIG welding was used for the root and the second pass and FCAW for the intermediate and final passes. Cross-weld tensile tests, side bend tests and impact tests of weld metals and heat-affected zones were carried out at ambient temperatures after two post-weld heat treatments (PWHT), each at 730°C for 12 hours. Creep rupture tests of cross-weld samples were performed at 625°C. This study compares the results of the mechanical tests at ambient temperature and the creep rupture tests, and discusses why P92 filler metals are preferred for such welds.