Search Results for creep test specimens

Two materials with different purity of 2.25Cr-1Mo steel thick weld joint were prepared and creep rupture behavior was investigated by large sized specimens. For high purity material, two types of challenging heat treatment was tried to modify the original microstructural conditions. Weld joints were made and large sized creep test specimens were machined. Creep tests were performed at 903K, 40MPa. Specimen made from low purity material fractured at fine grained heat affected zone (FGHAZ) and showed so-called Type IV cracking. On the other hand, specimen made from high purity material showed maximum creep damage at weld metal. In the case of specimens applied challenging heat treatment, remarkably high ductility were observed at fracture. Regarding 2.25Cr-1Mo steel, it was confirmed that the suppression of Type IV cracking had been basically achieved by past improvement on purity level. At the same time, improvement of heat treatment condition was found to have further effect. Because of improved creep properties of high purity material, properties of weld metal had rose up to be the next issue to be examined. At least, taking care on layout design of weld beads to avoid creating wide spread fine grained portion is desired.

Creep properties of 9Cr heat resistant steels can be improved by the addition of boron and nitrogen to produce martensitic boron-nitrogen strengthened steels (MarBN). The joining of this material is a crucial consideration in the material design since welds can introduce relatively weak points in the structural material. In the present study, creep tests of a number of MarBN weld filler metals have been carried out to determine the effect of chemistry on the creep life of weld metal. The creep life of the weld metals was analysed, and the evolution of creep damage was investigated. Significant differences in the rupture life during creep have been observed as a function of boron, nitrogen and molybdenum concentrations in the weld consumable composition. Although the creep lives differed, the particle size and number in the failed creep tested specimens were similar, which indicates that there is a possible critical point for MarBN weld filler metal creep failure.

Long-term creep tested specimens of the advanced austenitic stainless steel Super 304H were subjected to detailed metallographic analysis with an emphasis on the relationship between creep induced cavities (voids) and microstructural features. The creep specimens were tested between 873 and 973 K (600 and 700°C) at stresses between 110 and 340 MPa, with rupture times up to ~1.8 x 10 8 s (50,000 hours). To characterize damage, the distributions of creep cavities along the length of the gage section were determined and microstructural features associated with the cavities were investigated using optical microscopy and scanning electron microscopy.

The creep behavior of a γ-TiAl based alloy at 1073 K was investigated, examining three different microstructures: equiaxed γ (Eγ), γ/γ fully lamellar (FLγ), and equiaxed γ with α 2 phase on grain boundaries (Eγα 2 ). The aim was to understand the influence of lamellar interfaces and grain boundary α 2 phase on creep behavior. Initially, creep rates were consistent across all specimens upon loading. However, Eγ exhibited a gradual decrease in creep rate compared to Eγα 2 and FLγ. Notably, the minimum creep rate of Eγ was one order of magnitude lower than that of Eγα 2 and FLγ. Conversely, Eγα 2 and FLγ displayed a slight acceleration and the longest rupture strain, albeit with the shortest rupture time compared to Eγ. Upon microstructural analysis of of the creep-test specimens, it was observed that numerous dynamic recrystallized grains (DXGs) and sub-grains formed along grain boundaries and interiors in Eγ, whereas they were limited to the region along grain boundaries in FLγ. In contrast, very few DXGs were formed in Eγα 2 . These findings indicate that γ/γ interfaces inhibit the extension of DXGs into grain interiors, suggesting that the grain boundary α 2 phase effectively suppresses the formation of DXGs.

This study conducted creep tests, microstructural, and hardness analyses on SA213T23-TP347H dissimilar weld joints of long-term serviced coal-fired boiler final superheater tube. The welded joint (SA213 T23-TP347H) of the superheater tube, after approximately 105,000 hours of service, was sampled for creep life assessment and maintenance planning. Creep tests were conducted at 600°C under three stress conditions: 100, 140, and 160MPa. Most cracks were observed in the heat-affected zone of T23, and compared to unused tubes, the creep life consumption rate was approximately 90%. All dissimilar weld joints used welding rods similar in chemical composition to T23, and significant hardness reduction occurred in the flame-affected zone.

The creep strength of the base metals and welded joints of ASME Grade 91 type steel under actual service conditions was investigated using long-term used materials in this study. Creep tests were conducted on the materials used for hot reheat or main steam piping at power plants. The remaining creep life of each material under actual service conditions was evaluated using the Larson-Miller parameter for the test result. Then, the creep life of each material under the service condition was estimated as a summation of the service time at the plants and the remaining creep life. The estimation results were useful for examining the validity of the life evaluation formula in the long-term region because it is extremely difficult to obtain creep rupture data under such conditions owing to the long test duration. The estimated creep lives were compared with creep life evaluation curves, which were regulated for Grade 91 type steel in Japan. Regarding the base metals, the estimation results suggest that Grade 91 pipe-type steel tends to exhibit a shorter life than the 99% confidence lower limit of the evaluation curve of the material. This finding indicated that the life evaluation formula for the Grade 91 type steel base metals should be reviewed. On the other hand, the estimation results suggest that the welded joints of Grade 91 type steel generally exhibit a longer life than the 99% confidence lower limit of the evaluation curve of the material, indicating that there is no need to review the life evaluation formula for the Grade 91 type steel welded joints.

Alloy 718 is an important class of Nb-bearing Ni-based superalloys for high-temperature applications, such as compressor disks/blades and turbine disks in gas turbine systems. The service temperature of this alloy is, however, limited below 650 °C probably due to the degradation of its strengthening phase γ"-Ni3Nb. Aiming at understanding and improving creep properties of 718-type alloys, we investigated creep behaviors of alloy 718 and alloy Ta-718 where different types of γ" phases, Ni3Nb and Ni3Ta, were precipitated, respectively. Creep tests were conducted at 700 °C under stress conditions of 400 and 500 MPa for the two alloys in aged conditions. It was found that while the minimum creep rates were comparable in the two alloys, the creep rate acceleration was lower in alloy Ta-718 than in alloy 718 under the creep conditions studied. Microstructural observations on the specimens before and after the creep tests suggested that the γ" precipitates were distinguishably finer in alloy Ta-718 than in alloy 718 throughout the creep tests. The formation of planar defects and shearing of γ" precipitates occurred frequently in the alloy 718 specimen. The observed creep deformations were discussed in terms of the critical resolved shear stress due to shearing of γ" particles by strongly paired dislocations.

In order to establish a creep damage assessment method for 47Ni-23Cr-23Fe-7W (HR6W), which is a candidate material of A-USC, microstructure observation of creep interrupted specimens and ruptured specimen was conducted, and the creep damage process was examined. Creep tests were conducted under conditions of 800°C, 70 MPa, 700°C, and 100 MPa. For creep damage assessment, an optical microscope was used for replicas sampled from the outer surface of specimens, and crack ratio at grain boundaries was assessed. The results indicated that creep voids and cracks were initiated at grain boundaries from about 0.35 of creep life ratio, and crack ratio increased drastically after creep life ratio of 0.65. This crack ratio was almost the same regardless of the specimen shape Therefore, the method to assess crack ratio using replicas is considered to be an effective method for creep damage assessment of HR6W. An increase in the crack ratio due to an increase in creep life ratio showed the same trend as the change in elongation of creep interrupted specimens. Microstructure observations were conducted with interrupted specimens using SEM-ECCI (Electron Channeling Contrast Imaging) in order to clarify the cause of acceleration creep. The results showed that sub-boundary developed significantly near grain boundaries, which indicates that sub-boundary development may cause acceleration.

The creep strength and ductility of Grade P22 steel (2¼ Cr) was measured at 600°C under standard uniaxial tensile conditions at 150MPa. Test specimens were prepared by solution heat treatment at austenitization temperatures ranging from 900°C - 1200°C followed by normalization at 900°C before continuous air cooling to room temperature. In addition to specimens tested in the solution treated state, creep tests were also performed after tempering. The variable austenitization temperatures gave rise to different prior austenite grain (PAG) sizes, which in turn influenced the crystallographic packet and block boundary misorientation angle distribution. The latter parameters were measured using electron backscattered diffraction which also allowed partial reconstruction of the PAG boundaries. The time to creep failure at 600°C increased as function of PAG size up to approximately 70µm, but significantly decreased when the average prior austenite grain size measured approximately 108 µm. However, the minimum creep rate decreased even up to the largest PAG size with corresponding decrease in creep ductility. The stability of the crystallographic packet and block boundaries influences the high strength-low ductility for the large PAGs in comparison to the dominant effect of PAG boundaries at the smallest grain size where extensive recovery and recrystallization reduces creep strength.

In this study, creep rupture behaviors and rupture mechanisms of dissimilar welded joint between Inconel 617B and COST E martensitic steel were investigated. Creep tests were conducted at 600 ℃ in the stress range 140-240 MPa. Scanning electron microscopy (SEM) and micro-hardness were used to examine the creep rupture behaviors and microstructure characteristics of the joint. The results indicated that the rupture positions of crept joints shifted as stress changed. At higher stress level, the rupture position was located in the base metal (BM) of COST E martensitic steel with much plastic deformation and necking. At relatively lower stress level, the rupture positions were located in the fine-grained heat affected zone (FGHAZ) of COST E or at the interface between COST E and WM both identified to be brittle fracture. Rupture in the FGHAZ was caused by type Ⅳ crack due to matrix softening and lack of sufficient precipitates pinning at the grain boundaries (GBs). Rupture at the interface was related to oxide notch forming at the interface.

Long-term creep rupture tests up to 10 5 hours at 600℃ and 650℃ were carried out on mod.9Cr- 1Mo steel base metal and weldments from five different materials, consisting of various chemical compositions and heat treatments as well as welding conditions. As a result, positive correlations of creep rupture strength were clarified between the base metal and weldments from the same materials. Microstructural observations and thermokinetic calculations revealed that the strength correlations were attributed to the precipitation strengthening behavior of finely dispersed M 23 C 6 carbides and V-type MX carbonitrides, where their precipitation distribution characteristic in the fine-grained HAZ microstructures partially or almost entirely took over those in base metal. This finding implies that the long-term creep rupture strength of mod.9Cr-1Mo steel weldment might be able to be evaluated as long as the corresponding base metal strength is obtained.

Haynes 282 alloy is a relatively new Ni-based superalloy that is being considered for advanced ultrasupercritical (A-USC) steam turbine casings for steam temperatures up to 760°C. Weld properties are important for the turbine casing application, so block ingots of Haynes 282 alloy were cast for properties studies. Good, sound welds were produced using Haynes 282 weld-wire and a hot gas-tungsten-arc welding method, and tensile and creep-rupture properties were measured on cross-weld specimens. In the fully heat-treated condition (solution annealed + aged), the tensile properties of the welded specimens compare well with as-cast material. In the fully heat-treated condition the creep-rupture life and ductility at 750°C/250MPa and 800°C/200MPa of the cross-weld specimens are similar to the as-cast base metal, and repeat creep tests show even longer rupture life for the welds. However, without heat-treatment or with only the precipitate age-hardening heat-treatment, the welds have only about half the rupture life and much lower creep ductility than the as-cast base metal. These good properties of weldments are positive results for advancing the use of cast Haynes 282 alloy for the A-USC steam turbine casing application.

TAF steel is a Japanese high-boron 10.5% Cr martensitic stainless steel known for its exceptional high-temperature creep strength. Its high boron content (300-400 ppm) limited practical applications due to reduced hot workability in large turbine components. Recent research suggests that increasing boron content while adjusting nitrogen levels could enhance creep properties by promoting fine vanadium carbonitride formation while preventing boron nitride formation. This study presents microstructural investigations, particularly using transmission electron microscopy, focusing on precipitation characteristics and long-term precipitate evolution within the COST 536 framework.

Austenitic and super-austenitic stainless steels are a critical component of the spectrum of high temperature materials. With respect to power generation, alloys such as Super 304H and NF709 span a gap of capability between ferritic and martensitic high chromium steels and nickel-based alloys in boiler tube applications for both conventionally fired boilers and heat-recovery steam generators (HRSG). This research explores a wrought version of a cast austenitic stainless steel, CF8C-Plus or HG10MNN, which offers promise in creep strength at relatively low cost. Various manufacturing techniques have been employed to explore the impact of wrought processing on nano-scale microstructure and ultimately performance, especially in high temperature creep. Transmission electron microscopy has been used to quantify and characterize the creep-strengthening particles examining the relationship between traditional melting and extrusion as compared to powder metallurgy.

A longitudinal crack and window opening type failure occurred in neutral zone that is applied to least plastic deformation in the bent TP347H tube during operation. From the analysis of residual stress and plastic deformation during the tube bending, there is low creep strength and high residual stress in neutral zone as compared other regions like intrados and extrados. Therefore, failure occurred in neutral zone due to stress relaxation concentrated in grain boundary during operation.

Based on the research and development of Ni-based alloy of 700°C steam turbine bolts and blades worldwide, the process, microstructure, properties characteristics and strengthening mechanism of typical 700°C steam turbine bolts and blades materials Waspaloy are discussed in this study. The result shows that Waspaloy has higher elevated temperature yield strength, creep rupture strength, anti-stress relaxation property and good microstructure stability. The Waspaloy alloy could meet the design requirements of 700°C steam turbine bolts and blades.

In this study, the creep strength of welded joints of Grade 91 Type 1 and Type 2 steels was evaluated. It was determined that impurity elements in the Type 1 steel reduced its creep strength. This reduction was attributed to an increase in the amount of residual carbides in the fine-grain heat-affected zone during welding.

Type IV damage was found at several ultra-supercritical (USC) plants that used creep-strength-enhanced ferritic (CSEF) steels in Japan, and the assessment of the remaining life of the CSEF steels is important for electric power companies. However, there has been little research on the remaining life of material that has actually served at a plant. In this study, the damage and remaining life of a Gr.91 welded elbow pipe that served for 54,000 h at a USC plant were investigated. First, microscopic observation and hardness testing were conducted on specimen cut from the welded joint; the results indicated that the damage to the elbow was more severe in the fine-grain heat-affected zone near the inner surface. Furthermore, creep rupture tests were performed using specimens cut from the welded joint of the elbow, and from these results, the remaining life was evaluated using the time fraction rule as almost 110,000 h. Finite-element analysis was also conducted to assess the damage and remaining life, and the results were compared with the experimental results.

Increasing demand on efficiency and power output of steam generators leads to new designs of welded rotors. The reason for rotor welding is the large size of rotors, which are difficult to produce in a single piece. Secondly, as there are varying operation conditions along the rotor length. In a heterogeneous rotor, several materials appropriate for local service conditions can be used. At the rotor service temperatures, creep properties are crucial for successful design. The weakest point of every welded component is the heat affected zone. Therefore, the creep properties of a heterogeneous weld are subject of the investigation herein the current study, a heterogeneous weld of COST F and COST FB2 materials is investigated. The welding was performed by multi pass technique with overlaying welding beads that applied several heating cycles to heat affected zone. Metallographic investigation of the weld was performed and the weakest microstructure spots were detected. With the use of FEM simulation, appropriate heating/cooling cycles were obtained for the detected weak points. The temperature cycles obtained were subsequently applied to both base materials under laboratory conditions by induction heating. Creep properties of these materials were investigated. The influence of the initial base material’s grain size was also considered in the investigation. Two heating/cooling schedules were applied to both base materials with two grain sizes. Altogether, 8 different microstructures were examined in short term creep tests and the results were summarized.

The Haynes 282 Ni-based superalloy (57Ni-20Cr-10Co-8.5Mo-2.1Ti-1.5Al) is a very promising candidate for the fabrication by additive manufacturing of gas turbine components of complex geometries. Alloy 282 was fabricated by electron beam melting (EBM) and exposed to two different heat treatments, (a) solution anneal (SA) at 1135°C followed by the standard 2-step aging treatment (2h at 1010°C plus 8h at 788°C) and (b) SA followed by 4h 800°C. Large elongated grains were observed for the as-fabricated and annealed EBM 282 materials, with a γ′ (Ni 3 (Al,Ti)) average size of ~100 nm and 20 nm, respectively. The as-fabricated EBM 282 alloy exhibited good ductility at 20-900°C and tensile strength slightly lower than the tensile strength of wrought 282. Annealing the alloy resulted in a moderate increase of the alloy strength at 800 and 900°C but a decrease of the alloy ductility. The creep lifetime at 800°C, 200MPa of the as-fabricated and annealed EBM 282 specimens machined along the build direction was 2 times and 1.5 times superior to the expected lifetime for wrought 282, respectively. For creep specimens machined perpendicular to the build direction, the lifetimes were ~25% lower compared to the wrought alloy. These creep results are directly related to the strong grain texture of the EBM 282 alloy and the limited impact of the initial γ′ (Ni 3 (Al,Ti)) size on alloy 282 creep properties.