Coke drums experience failures in through-wall cracking throughout their operating life, resulting from low cycle fatigue. Coke drums are typically fabricated from Chrome Moly (CrMo) steels. This study was performed on P4 (1.25Cr-0.5Mo) base material using ER70S-B2L and Alloy 625 (ERNiCrMo-3) filler materials. Specimens were welded with the temper-bead/controlled deposition welding technique. The weld processes used were HP-GTAW, GMAW and SMAW. The fatigue performance, HAZ hardness and toughness of the weld samples was evaluated. The HP-GTAW welds exhibited an order of magnitude improvement in fatigue performance when compared to the other weld processes using ER70S-B2L filler material. The HP-GTAW welds also exhibited improved HAZ hardness and toughness when compared to the other weld processes. This presentation will introduce the HP-GTAW process, its features, and benefits and where it is applied in Coke drum repair welding. Comparative test results of the different weld processes for fatigue performance, HAZ tempering, and toughness will also be presented.

The harsh operating conditions of Advanced Ultra-Supercritical (A-USC) power plants, i.e., steam operation conditions up to 760°C (1400°F)/35 MPa (5000 psi), require the use of Ni-based alloys with high temperature performance. Currently, the U.S. Department of Energy Fossil Energy program together with Electric Power Research Institute (EPRI) and Energy Industries of Ohio (EIO) is pursuing a Component Test (Comets) project to address material- and manufacturing-related issues for A-USC applications. Oak Ridge National Laboratory (ORNL) is supporting this project in the areas of mechanical and microstructure characterization, weld evaluation, environmental effect studies, etc. In this work, we present results from these activities on two promising Ni-based alloys and their weldments for A-USC applications, i.e., Haynes 282 and Inconel 740H. Detailed results include microhardness, tensile, air and environmental creep, low cycle fatigue, creep-fatigue, environmental high cycle fatigue, and supporting microstructural characterization.

9-12%Cr martensitic steels can be applied to the next highest temperature components such as boiler tracts, steam pipelines and turbines of advanced ultra-supercritical power plants with steam temperatures of 650°C. New 10%Cr martensitic steels with high B and low N contents can be a worthy candidate for use in production because it has superior creep resistance. At the same time, resistance to cyclic and dynamic loads is very important. In this work, we studied the low cycle fatigue (LCF) properties at room and elevated (500-650°C) temperatures and Charpy impact toughness at temperatures ranging from -196…100°C of advanced 10% Cr martensitic steel with high B and low N contents. The effect of new alloying scheme and corresponding peculiarities of M 23 C 6 carbides on the low cycle fatigue resistance and impact toughness of the 10%Cr martensitic steel is analyzed. It is revealed that fine and densely distributed carbides has no effect on the fatigue resistance except for the slight improvement of fatigue life at small strain amplitudes and shift the ductile-brittle transition temperature (DBTT) to higher but satisfactory value of +10°C as compared to other high-chromium martensitic steels.

In several material qualification programs tubes and thick-walled components mainly from Alloy 617 and Alloy 263 were investigated. Results as low cycle fatigue and long term creep behavior of base materials and welds are presented. Numerical models to describe the material behavior have been developed and verified by multiaxial tests. In order to ensure the feasibility of A-USC plants two test loops have been installed in GKM Mannheim – one for tube materials and a new one for thick-walled piping and components. The latter consists of a part with static loading and a part subjected to thermal cycles and is in operation since November 2012. First results of measurements and numerical calculations for a pipe bend (static loading) as well as pipes and a header (thermal cycles) are presented.

The creep-fatigue properties of modified 9Cr-1Mo (grade 91) steel have been investigated for the purpose of design in cyclic service. In this paper test results from creep-fatigue (CF) and low cycle fatigue (LCF) on grade 91 steel are reported. The tests performed on the high precision pneumatic loading system (HIPS) are in the temperature range of 550-600ºC, total strain range of 0.7-0.9% and with hold periods in both tension and compression. Curves of cyclic softening and stress relaxation are presented. The CF test results and results obtained from literature are also analysed using methods described in the assessment and design codes of RCC-MRx, R5 and ASME NH as well as by the recently developed Φ-model. It is shown that the number of cycles to failure for CF data can be accurately predicted by the simple Φ-model. The practicality in using the life fraction rule for presenting the combined damage is discussed and recommendations for alternative approaches are made.

Procedures for assessing components subjected to cyclic loading at high temperatures require material property data that characterize creep-fatigue deformation behavior and resistance to cracking. While several standards and codes define test procedures for acquiring low cycle fatigue (LCF) and creep properties, no formal guidelines exist for determining creep-fatigue data. This paper reviews the results of a global survey conducted by EPRI to support the development of a new draft testing procedure intended for submission to ASTM and, ultimately, ISO standards committees. The survey included a review of relevant national and international standards, as well as responses to a questionnaire distributed to high-temperature testing specialists in Europe, North America, and Japan. Additionally, standards related to the calibration of load, extension, and temperature measurement devices were examined. The questionnaire responses provided insights into test specimen geometry, testing equipment, control and measurement of load, extension, and temperature, and data acquisition practices. This paper outlines the background and considerations for the proposed guidance in the new standard.

This paper reports on a study that investigated how low cycle fatigue (LCF) and fatigue crack propagation (FCG) properties of P92, P122, and P23 steels vary between 600°C and 700°C depending on the location relative to a cross weld. Microstructure analysis was also performed on fractured specimens. Due to its higher yield strength, P122 exhibited the best continuous LCF life. However, creep-fatigue interaction (CFI) in the weld heat-affected zone (HAZ) of P122 and P23 steels significantly reduced their lifespans compared to continuous LCF tests. This reduction is attributed to the effect of weld thermal cycles on fine precipitates. FCG tests revealed that the base metal consistently outperformed the HAZ in all tested steels and temperatures. P92 and P122 showed similar FCG rates except for P92's behavior at 600°C, which resembled P23. In both steels, the HAZ exhibited faster FCG rates at 600°C and 700°C compared to the base metal, particularly at lower stress intensity factor ranges (ΔK). Within the HAZ, the region 1 mm from the fusion line displayed the slowest FCG rates, followed by the base metal, while the fusion line and the region 2 mm from it showed the fastest. Fracture surfaces near the fusion line displayed cleavage-like features, while the region 1 mm away exhibited features associated with higher crack growth resistance.

This paper explores the low cycle fatigue (LCF) and creep-fatigue properties of a hot-forged, normalized, and tempered 9Cr-1Mo ferritic steel. This steel offers good performance in high-temperature applications (up to 873K) in power plants and reactors. The steel was forged into 70 mm diameter rods and then heat-treated with normalizing (1313K for 1 hour, air cooling) and tempering (1033K for 1 hour, air cooling). LCF tests were conducted at 300-873K with varying strain amplitudes and strain rates to understand the influence of both factors. Additionally, some specimens were aged at different temperatures for 10,000 hours before testing. Finally, creep-fatigue interaction tests were performed at 823K and 873K using tensile hold times ranging from 1 to 30 minutes.