Traditional laboratory steam experiments are conducted at ambient pressure with water of variable chemistry. In order to better understand the effect of steam pressure and water chemistry, a new recirculating, controlled chemistry water loop with a 650°C autoclave was constructed. The initial experiments included two different water chemistries at 550° and 650°C. Two 500-h cycles were performed using oxygenated (OT, pH ~9 and ~100 ppb O 2 ) or all-volatile treated (AVT, pH ~9 and <10 ppb O 2 ) water conditions at each temperature. Coupons exposed included Fe-(9-11)%Cr and conventional and advanced austenitic steels as well as shot peened type 304H stainless steel. Compared to ambient steam exposures, the oxides formed after 1,000 h were similar in thickness for each of the alloy classes but appeared to have a different microstructure, particularly for the outer Fe-rich layer. An initial attempt was made to quantify the scale adhesion in the two environments.

Because of the problems experienced with steam-side oxidation in commercial power plants, there has been continuing interest in better understanding the steam oxidation behavior of creep strength enhanced ferritic steels such as grades 23, 24 and 91 as well as 300-series stainless steels such as 347H and 304H. Analysis of field-exposed tubes has provided information on the oxidation reaction products but relatively few specimens are available and there is limited information about the kinetics. Specimens have included tube sections with a shot peened surface, a treatment that is now widely used for austenitic boiler tubes. To complement this information, additional laboratory studies have been conducted in 1bar steam at 600°-650°C on coupons cut from conventional and shot-peened tubing. Exposures of 1-15 kh provide some information on the steam oxidation kinetics for the various alloys classes. While shot-peened type 304H retained its beneficial effect on oxidation resistance past 10,000 h at 600° and 625°C, the benefit appeared to decline after similar exposures at 650°C.

Steam-side oxidation and the resultant exfoliation of iron-based scales cause unplanned shutdowns at coal-fired power generation plants. Exfoliate removal is currently limited to frequent unit cycling to minimize the volume of exfoliated scale, upgrading a plant with a “blow down” system, or installing a higher alloy. This paper discusses the rate of steam-side oxidation on Type 304H stainless steel (304H) tube after shot peening the internal surface with commercially available techniques. Shot peening the ID of Type 304H austenitic stainless steel superheater tubes has been shown to improve the overall oxidation resistance in steam. Decreasing the oxidation rate directly impacts the volume of exfoliated scale. The adherent spinel scales are thinner and more robust than non-shot peened tubes of the same alloy. Most of the improved oxidation resistance can be attributed to the presence of a spinel oxide layer combined with a continuous chromia layer formed near the steam-touched surfaces. The presence of a continuous chromia layer vastly reduces the outward diffusion of iron and minimizes the formation of iron-based scales that exfoliate. This work showed that a uniform cold-worker layer along the tube ID has a profound effect on oxidation resistance. Incomplete coverage allows oxidation to proceed in the non-hardened regions at a rate comparable to the oxidation rate on unpeened Type 304H.

As part of the Boiler Materials for Ultrasupercritical Coal Power Plants program, sponsored by the United States (U.S.) Department of Energy (DOE) and the Ohio Coal Development Office (OCDO), the steamside oxidation and oxide exfoliation behavior of candidate alloys have been thoroughly evaluated in steam at temperatures between 620°C and 800°C (1148°F and 1472°F) for times up to 10,000 hours. The results from this test program indicate that the oxidation rates and oxide morphologies associated with steamside oxidation are a strong function of the crystallographic lattice structure and the chromium content of the material. Oxide exfoliation correlates to oxide thickness. The time required to reach the critical oxide thickness for exfoliation can be estimated based on oxidation kinetic relationships. For austenitic stainless steels, shot peening is effective in reducing steamside oxidation/exfoliation, but the efficacy of this technique is limited by the operating temperature. Nickel-based alloys exhibit very low oxidation/exfoliation rates, but have a propensity to form aluminum/titanium oxides along near surface grain boundaries.

Because of the problems experienced with steam-side oxide scale exfoliation in commercial power plants, there has been increased interest in understanding the steam oxidation resistance of 300- series stainless steels such as 347H and 304H. Model alloys were used in an attempt to understand the effect of varying Ni (9-12%) and Cr (16-20%) on steam oxidation resistance at 650°C. However, the model alloys generally showed superior oxidation resistance than commercial alloys of similar composition. Several surface engineering solutions also were investigated. The commercially favored solution is shot peening. Laboratory steam testing at 650°C found that annealing temperatures of ≥850°C eliminated the benefit of shot peening and a correlation was observed with starting hardness in the peened region. This effect of annealing has implications for the fabrication of shot peened tubing. Another route to improving oxidation resistance is the use of oxidation resistant diffusion coatings, which can be deposited inexpensively by a vapor slurry process. Uniform coatings were deposited on short tube sections and annealed at 1065°C to retain good 650°C creep properties. The coating was thicker than has been investigated in laboratory processes resulting in increased brittleness when the coating was assessed using 4-point bending.

Steam oxidation of a novel austenitic steel, of which composition is Fe-20Cr-30Ni-2Nb (at.%), has been conducted at 973 K to evaluate steam oxidation resistance based on detail analyses of scale morphology and scale growth. Two types of scale morphologies were observed in the solution treated sample, depending on the grain of the steel. Although thin duplex scale with the Cr-rich layer was formed in the early stage, most of the surface was covered with thick duplex scale which consists of magnetite as the outer scale and the mixture of Fe-Cr spinel and metallic Ni as the inner scale. On the other hand, surface morphology of the oxide scale was independent of grain of the steel and thick duplex scale as seen on the solution treated sample was formed on the pre-aged sample. Steam oxidation resistance of the steel is almost the same as that of commercial austenitic steels and it can be improved by the surface treatment such as shot peening. Based on the results, this steel has both enough creep rupture strength and good steam oxidation resistance for A-USC power plants.

The growth behavior of oxide scale in a laboratory steam environment has been conducted for the shot-peened 18Cr-8Ni stainless steels differing in grain size. Both steels (fine grained and coarse grained) have demonstrated almost the same steam oxidation behavior reacted at 700°C for up to 2000h, which had excellent oxidation resistance due to formation of a protective Cr 2 O 3 scale. After the exposure of 4000h, however, nodule-like oxide occurred on the coarse grained steel, while the fine grained steel still remained the uniform Cr 2 O 3 scale. These behaviors well explained in terms of changes of the outward Cr flux due to recovery and recrystallization of the deformed structure. This result has proven that the shot-peened tube composed of fine grain structure is capable of combat against the steam oxidation at high temperatures.

This paper investigates the combined effect of shot peening and pre-oxidation treatment in air on the subsequent steam oxidation resistance of Modified 9Cr-1Mo steel with different sulfur contents. Cast steel balls (50-180 μm diameter) and pure Cr (50-230 μm diameter) were used for shot peening durations of 5-50 seconds. After shot peening, pre-oxidation was performed in air at 973K for 3.6ks. Then, oxidation testing was conducted in steam at 923K for up to 3.6Ms. Only the combination of Cr shot peening and pre-oxidation treatment facilitated the formation of a protective Cr-rich oxide scale on the specimen surface during pre-oxidation. This Cr-rich oxide scale remained stable during subsequent steam oxidation, resulting in excellent oxidation resistance of the steel.

This paper describes the steam oxidation behavior of two 18Cr-8Ni austenitic fine-grained stainless steels, TP347HFG and SUPER304H, which have been developed for ultra-supercritical (USC) boilers. A field exposure test was conducted by installing these tubes, along with comparative materials, in the tertiary superheater of a utility power boiler. After periodic service, the fine-grained tubes were removed to examine their steam oxidation behavior. Examination of the steam oxidation scale on the inner surface of the tubes indicated an extremely low scale growth rate for the fine-grained steels, even after 10 years of service. The oxidation structure is discussed and compared with conventional materials, TP321H and TP347H. Accelerated steam oxidation tests were conducted using an oxidation test with saturated dissolved oxygen concentration. The combination of fine-grained steel and a shot-peening layer exhibits high steam oxidation resistance at 700°C or higher temperatures.