Driven by the need to reduce CO 2 emissions through increased steam temperature and pressure in new power plants, research in Europe led to the development of enhanced high-chromium steels with improved creep resistance and service temperature stability. After years of development, Rotor E, a steel composition created during the COST programs (501, 522, and 536), has become a commercially available product. While traditionally forged and remelted using electroslag remelting (ESR), this paper demonstrates the successful production of large rotor components using a conventional process without ESR, achieved through tailored process control. This paper details Società delle Fucine's (SdF) current production of Rotor E using a conventional route based on ladle furnace and vacuum degassing, as well as the mechanical and creep behaviors of the resulting forged products. Additionally, SdF produced a prototype FB2 rotor using a conventional process. FB2, a 10% Cr steel containing cobalt and boron but lacking tungsten, emerged from the COST 522 program as the best candidate for scaling up from a laboratory experiment to a full-sized industrial component. Notably, the addition of boron effectively improved the microstructure's stability and consequently enhanced the creep resistance of these new, advanced martensitic steels. Finally, the paper will present updates on the long-term characterization program for the FB2 steel trial rotor.

The development of new ferritic-martensitic steels for rotor applications was a primary focus of the joint research projects COST 501 and COST 522. During COST 501, multiple trial compositions of 9-10% chromium steels underwent comprehensive testing, with the COST 522 project ultimately selecting the most promising candidate, FB2, a 10% Cr steel containing cobalt and boron additions, notably without tungsten. Società delle Fucine (SdF) successfully produced an FB2 prototype rotor using a conventional manufacturing process involving ladle furnace and vacuum degassing techniques. A comprehensive creep test program was initiated to characterize the full-size component's properties, with results demonstrating consistency with laboratory material performance in both creep resistance and ductility. The extensive testing, which exceeded 30,000 hours, aimed to achieve a 15-20 MPa improvement over Grade 92, targeting 100,000 creep hours at 600°C. Complementing the mechanical testing, a parallel microstructural investigation program was launched to evaluate structural evolution and gain deeper insights into boron's role as a creep-strengthening element in advanced ferritic-martensitic steels.