Development of steels used in the power generation industry for the production of boilers characterized by supercritical parameters poses new challenges. The introduction of new combinations of alloying agents aimed at obtaining the best possible mechanical properties, including creep resistance, affects the weldability of new steels. Each of the latter has to undergo many tests, particularly as regards bending and welding, in order to enable the development of technologies ensuring failure-free production and assembly of boiler systems. Martensitic steels containing 9% Cr, used in the manufacturing of steam superheaters, are characterized by excellent creep resistance and, at the same time, low oxidation resistance at a temperature in excess of 600°C. In turn, steels with a 12% Cr content, i.e., VM12-SHC or X20CrMoV12-1 are characterized by significantly higher oxidation resistance but accompanied by lower strength at higher temperatures, which translates to their limited application in the production of boilers operating at the most top parameters.X20CrMoV12-1 was withdrawn from most of the power plants, and VM12-SHC was supposed to replace it, but unfortunately, it failed in regards to creep properties. To fulfill the gap a new creep strength-enhanced ferritic steel for service in supercritical and ultra-supercritical boiler applications was developed by Tenaris and it is designated as Thor115 (Tenaris High Oxidation Resistance). This paper covers the experience gained during the first steps of fabrication, which includes cold bending and welding of homogenous joints.

In order to establish a induction bending technique for Ni-based alloy HR6W large pipe, induction bending test was conducted on HR6W, which is a piping candidate material of 700°C class Advanced Ultra-Super Critical. In this study, a tensile bending test in which tensile strain was applied and a compression bending test in which compression strain was applied to the extrados side of the pipe bending part. As the results of these two types of induction bending tests, it was confirmed that a predetermined design shape could be satisfied in both bending tests. In addition, the wall thickness of the pipe was equal to or greater than that of the straight pipe section in compression bending. Therefore, if compression bending is used, it is considered unnecessary to consider the thinning amount of the bent portion in the design. Next, penetrant test(PT) on the outer surface of the bending pipes were also confirmed to be acceptable. Subsequently, metallographic samples were taken from the outer surface of the extrados side, neutral side and intrados side of the pipe bending portion. Metallographic observation confirmed that the microstructures were normal at all the three selected positions. After induction bending, the pipe was subjected to solution treatment. Thereafter, tensile tests and creep rupture tests were carried out on samples that were cut from the extrados side, neutral side and intrados side of the pipe bending portion. Tensile strength satisfied the minimum tensile strength indicated in the regulatory study for advanced thermal power plants report of Japan. Each creep rupture strength was the almost same regardless of the solution treatment conditions. From the above, it was possible to establish a induction bending technique for HR 6W large piping.

Cold working and bending during boiler manufacturing can induce strain hardening in austenitic stainless steel, potentially compromising creep ductility and leading to premature failures during operation. While design codes like ASME I, PG 19 provide guidelines for maximum strain levels before solution treating is required, industry concerns suggest these limits may be too high, prompting some boiler manufacturers to implement more conservative thresholds. This study examined the creep ductility of four austenitic stainless steels (TP310HCbN, XA704, TX304HB, and Sanicro 25) at prior strain levels of 12% and 15%, with Sanicro 25 demonstrating the highest ductility, followed by TX304HB, XA704, and TP310HCbN. Solution annealing successfully restored creep ductility to exceed 10% elongation in all materials, though this treatment may be necessary at strains of 12% and 15% for all materials except Sanicro 25 to ensure adequate creep ductility. The findings suggest that ASME I PG 19 guidelines for austenitic stainless steels containing Cb, V, and N should be reviewed, as lower strain limits could help reduce strain-induced precipitation hardening failures.

With the desire for higher operating temperatures and pressures to improve the thermal efficiency of new power generating plant there have been significant changes in the materials used. For operation up to 620°C, a new range of ferritic steels with 9-13%Cr has been developed. With proper control of composition and heat treatment these materials, including Grades 91 and 92,exhibit predominantly martensitic microstructures and a good balance between strength and ductility. However, fabrication processes such as welding and bending, normally combined with extreme operating conditions have resulted in in-service damage. Examples of factors leading to accelerated creep, creep fatigue and oxidation damage are described.

A new 12%Cr steel, VM12, has been developed with the combined strength and oxidation resistance characteristics desired for high-temperature applications. The steel increases chromium content by around 0.2% to improve oxidation properties while alloying with other elements such as cobalt, tungsten, and boron to meet a range of requirements, including extending fatigue life. The steel is designed to have the same creep strength as T/P92 but with better oxidation resistance due to the higher chromium content. It has about a 0.2% increase in mechanical properties compared to T/P92 steel. Results are presented for tubes and pipes cast with a variety of surface conditions. In addition, detailed results are provided on the effects of alloying elements on creep and oxidation resistance.