As flux cored wires for gas metal arc welding offer several technical and economic advantages they are becoming more and more popular. Matching flux cored wires for welding P92 have already been available for several years. A matching flux cored wire for welding the Co-alloyed cast steel CB2, which is used for turbine and valve casings operating at steam temperatures of up to 620°C, was developed recently. To connect casings with P92 pipes, dissimilar welding of CB2 to P92 is necessary. This can be done with filler metal that matches either CB2 or P92. Pre-tests have confirmed that flux cored arc welding (FCAW) can generally be used for dissimilar joint welding of CB2 to P92. To evaluate creep rupture strength dissimilar welds were performed with filler metal matching CB2 and P92, respectively. TIG welding was used for the root and the second pass and FCAW for the intermediate and final passes. Cross-weld tensile tests, side bend tests and impact tests of weld metals and heat-affected zones were carried out at ambient temperatures after two post-weld heat treatments (PWHT), each at 730°C for 12 hours. Creep rupture tests of cross-weld samples were performed at 625°C. This study compares the results of the mechanical tests at ambient temperature and the creep rupture tests, and discusses why P92 filler metals are preferred for such welds.

The toughness of girth welds in 9Cr-1Mo-V and 9Cr-0.5Mo-V steel seamless pipe (ASME SA-335 Grades P91 and P92, respectively) made using the flux-cored arc welding (FCAW) process was evaluated. Electrodes from two different suppliers were used for production quality welding of each steel. The welds received post-weld heat-treatment (PWHT) in accordance with the requirements of the ASME Code. The objective of the work was to determine if the fracture toughness of the FCAW welds was acceptable for high-temperature steam piping. Toughness was measured using standard sized Charpy V-notch impact specimens. The specimens were oriented transverse to the weld seam with notch located approximately in the center of the weld metal and parallel to the direction of weld seam. Full-range (lower to upper shelf) Charpy impact energy and shear area curves were developed for each weld joint. These were used to estimate the temperatures corresponding to 30 ft-lb average impact energy. The estimated temperatures were well below the service temperature but were above the typical hydrostatic test temperature.

The use of flux-cored arc welding (FCAW) is rapidly gaining acceptance in a variety of industries. Much of the gains are due to advances in manufacturing technology that result in superior wires that satisfy both technical and operability concerns. Additionally, productivity gains and the ability to use unsophisticated welding equipment have made these wires very popular. This paper concentrates on FCAW wires that have been formulated to address chromium-molybdenum, nickel base, and stainless steels for high-temperature and environmental applications. Mechanical properties, including creep rupture strength and ductility data, as well as corrosion in environmental components, are discussed.