The Advanced Materials and Manufacturing Technologies (AMMT) program is aiming at the accelerated incorporation of new materials and manufacturing technologies into nuclear-related systems. Complex Ni-based components fabricated by laser powder bed fusion (LPBF) could enable operating temperatures at T > 700°C in aggressive environments such as molten salts or liquid metals. However, available mechanical properties data relevant to material qualification remains limited, in particular for Ni-based alloys routinely fabricated by LPBF such as IN718 (Ni- 19Cr-18Fe-5Nb-3Mo) and Haynes 282 (Ni-20Cr-10Co-8.5Mo-2.1Ti-1.5Al). Creep testing was conducted on LPBF 718 at 600°C and 650°C and on LPBF 282 at 750°C. finding that the creep strength of the two alloys was close to that of wrought counterparts. with lower ductility at rupture. Heat treatments were tailored to the LPBF-specific microstructure to achieve grain recrystallization and form strengthening γ' precipitates for LPBF 282 and γ' and γ" precipitates for LPBF 718. In-situ data generated during printing and ex-situ X-ray computed tomography (XCT) scans were used to correlate the creep properties of LPBF 282 to the material flaw distribution. In- situ data revealed that spatter particles are the potential causes for flaws formation in LPBF 282. with significant variation between rods based on their location on the build plate. XCT scans revealed the formation of a larger number of creep flaws after testing in the specimens with a higher initial flaw density. which led to a lower ductility for the specimen.

This study investigates the steam oxidation behavior of Alloy 699 XA, a material containing 30 wt.% chromium and 2 wt.% aluminum that forms protective oxide scales in low-oxygen conditions. The research compares four variants of the alloy: conventional bulk material, a laser powder bed fusion (LPBF) additively manufactured version, and two modified compositions. The modified versions include MAC-UN-699-G, optimized for gamma-prime precipitation, and MAC-ISIN-699, which underwent in-situ internal nitridation during powder atomization. All variants were subjected to steam oxidation testing at 750°C and 950°C for up to 5000 hours, with interim analyses conducted at 2000 hours. The post-exposure analysis employed X-ray diffraction (XRD) to identify phase development and scanning electron microscopy with energy dispersive spectroscopy (SEM/EDS) to examine surface morphology, cross-sectional microstructure, and chemical composition. This study addresses a significant knowledge gap regarding the steam oxidation behavior of 699 XA alloy, particularly in its additively manufactured state.

To improve the economics of critical components, such as receivers and heat exchangers, for Generation 3 (Gen 3) concentrating solar power (CSP) plants, research was conducted to understand how manufacturing impacts the high-temperature performance of various tube production routes. Gen 3 CSP components are expected to require the use of heat-resistant nickel- based alloys due to the elevated operating temperatures in designs carrying molten salt or supercritical CO 2 . INCONEL alloy 740H (alloy 740H) was investigated as an alternative to UNS N06230 (alloy 230) as it possesses superior high-temperature creep strength which can lead to overall reductions in material cost. A key challenge is understanding how autogenous seam welding with and without re-drawing can be used to manufacture thin-wall tubing for CSP receivers and heat-exchangers to further reduce costs over traditional seamless production routes. Alloy 740H welded tube was successfully fabricated and re-drawn to several relevant tube sizes. Since traditional mechanical testing samples could not be removed from the thin-wall tubing, full-sized tubes were used for tensile, fatigue, and vessel testing (internally pressurized creep- rupture) which was critical to understanding the weld performance of the manufactured product forms. The generated vessel test data exhibited a creep strength reduction when compared to wrought product with no clear trend with temperature or test duration. It was found that redrawing the welded tubes improved the creep strength to approximately 82% of the wrought material performance and elevated temperature tensile and fatigue behavior exceeded 85% of the design minimums. Detailed, post-test characterization found that nano-sized carbides formed during the laser seam-welding process remained stable after multiple solution-annealing steps, which restricted grain growth, and impacted the time-dependent performance. This paper will focus on the time-dependent behavior of the examined welded and redrawn tubes, supporting metallographic evidence, and give perspective on future considerations for using alloy 740H in CSP components.

Additive manufacturing is a groundbreaking manufacturing method that enables nearly lossless processing of high-value materials and produces complex components with a level of flexibility that traditional methods cannot achieve. Wire arc additive manufacturing (WAAM), utilizing a conventional welding process such as gas metal arc welding, is one of the most efficient additive manufacturing technologies. The WAAM process is fully automated and guided by CAD/CAM systems on robotic or CNC welding platforms. This paper explores the fundamental concepts and metallurgical characteristics of WAAM. It focuses primarily on the mechanical properties of printed sample structures made from P91, X20, and alloys 625 and 718 wire feedstock. The study particularly addresses the anisotropy of mechanical properties through both short-term and long-term testing, comparing these results to materials processed using conventional methods.

This presentation compares the corrosion resistance of uncoated Haynes 230 and SS316HS substrates to the same substrates coated with a Fe-based amorphous alloy. The substrates were exposed to highly corrosive media, FLiNaK, for 120 hours at 700 °C. The findings indicate that the thermal spray amorphous alloy coating provided superior corrosion resistance within the coatings while protecting the substrates against the aggressive environment. As a result, the new amorphous metal coating improved the substrate's lifespan by providing better protection against high-temperature corrosion, paving the way for a more efficient and cost-effective future in various industrial applications.

Coke drums experience failures in through-wall cracking throughout their operating life, resulting from low cycle fatigue. Coke drums are typically fabricated from Chrome Moly (CrMo) steels. This study was performed on P4 (1.25Cr-0.5Mo) base material using ER70S-B2L and Alloy 625 (ERNiCrMo-3) filler materials. Specimens were welded with the temper-bead/controlled deposition welding technique. The weld processes used were HP-GTAW, GMAW and SMAW. The fatigue performance, HAZ hardness and toughness of the weld samples was evaluated. The HP-GTAW welds exhibited an order of magnitude improvement in fatigue performance when compared to the other weld processes using ER70S-B2L filler material. The HP-GTAW welds also exhibited improved HAZ hardness and toughness when compared to the other weld processes. This presentation will introduce the HP-GTAW process, its features, and benefits and where it is applied in Coke drum repair welding. Comparative test results of the different weld processes for fatigue performance, HAZ tempering, and toughness will also be presented.

There is a critical lack of data on the mechanical behavior of candidate structural materials for advanced nuclear reactors under molten halide salt environments. Limited legacy data from the molten salt reactor experiment (MSRE) program showed a significant reduction in creep rupture strength of a Ni-base alloy in molten fluoride salt. With ongoing efforts to commercialize different molten salt reactor concepts, the industry can considerably benefit from quantitative information on the impact of molten halide salts on the engineering properties such as creep and fatigue strength of materials of interest. The present work aims to assess the role of molten salt corrosion on the creep behavior of three alloys 316H, 617 and 282 at 650-816 °C. Creep tests were conducted in fluoride (FLiNaK) and chloride (NaCl-MgCl 2 ) salts. Initial results from the ongoing testing will be presented which suggest that the molten salt environment caused a 25-50% reduction in creep rupture lifetime compared to air exposures. Physics-based corrosion and creep models were employed to gain some insights into the potential degradation mechanisms.

Ductility dip cracking (DDC) is known to occur in highly restrained welds and structural overlays made using high chromium (Cr) nickel (Ni) based filler metals in the nuclear power generation industry, resulting in costly repairs and reworks. Previous work explored the role of mechanical energy imposed by the thermo-mechanical cycle of multipass welding on DDC formation in a highly restrained Alloy 52 filler metal weld. It was hypothesized that imposed mechanical energy (IME) in the recrystallization temperature range would induce dynamic recrystallization (DRX), which is known to mitigate DDC formation. It was not shown however that IME in the recrystallization temperature range (IMERT) induced DRX. The objective of the work is to discern if a relationship between IMERT and DRX exists and quantify the amount of DRX observed in a filler metal 52 (FM-52) groove weld. DRX was analyzed and quantified using electron beam scattered diffraction (EBSD) generated inverse poll figures (IPF), grain surface area and grain aspect ratio distribution, grain orientation spread (GOS), kernel average misorientation (KAM), and grain boundary (GB) length density. From the analysis, GOS was determined to be an unsuitable criterion for quantifying DRX in multipass Ni-Cr fusion welds. Based on the observed criteria, higher IMERT regions correlate to smaller grain surface area, larger grain boundary density, and higher grain aspect ratio, which are all symptoms of DRX. High IMERT has a strong correlation with the symptoms DRX, but due to the lack of observable DRX, creating a threshold for DRX grain size, grain aspect ratio, and GB density is not possible. Future work will aim to optimize characterization criteria based on a Ni-Cr weld with large presence of DRX.

Creep-fatigue tests strain-controlled with different strain amplitudes and different hold times at 725 were done on nickel-based alloy 617 as a typical candidate material for turbine rotor of advanced ultra-supercritical power plant. Stress relaxes during the hold time when the strain remains at the tensile peak. The analysis of the stress relaxation during different strain hold times shows that the ratio of the relaxation stress and the maximum stresses has strong correlation with strain amplitude and hold time. The failure life also has a certain dependence on the relaxation stress ratio. The failure life decreases and the relaxation stress ratio increases as the strain amplitude increases. The failure life decreases and the relaxation stress ratio increases as the hold time increases. Therefore the stress relaxation ratio was used as an intermediate variable to obtain the corresponding relationship model by establishing the relationship between the relaxation stress ratio and the strain and the relationship between the relaxation stress ratio and the failure life. This model can be used to predict the creep-fatigue interaction life more simply and directly.

This study investigates the role of grain-boundary precipitates in enhancing creep rupture strength of Ni-based alloys through analysis of Ni-15Cr-15Mo and Ni-15Cr-17Mo (at.%) model alloys. The investigation focused on the “Grain-boundary Precipitation Strengthening (GBPS)” effect from the thermally stable TCP phase, a phenomenon previously observed in Fe-Cr-Ni-Nb austenitic heat-resistant steels. Through multi-step heat treatments, specimens were prepared with varying grain boundary coverage ratios (ρ) of TCP P phase (oP56) and consistent grain-interior hardness from GCP Ni2(Cr, Mo) phase (oP6). In the 15 at.% Mo alloy, specimens with a higher coverage ratio (~80%) demonstrated significantly improved creep performance, achieving nearly four times longer rupture time (3793 h vs. 1090 h) at 300 MPa and 973 K compared to specimens with lower coverage (~35%). However, the 17 at.% Mo alloy showed unexpectedly lower performance despite high coverage ratios, attributed to preferential cavity formation at bare grain boundaries. These findings confirm that GBPS via thermally stable TCP phase effectively enhances creep properties in Ni-based alloys, with grain boundary coverage ratio being more crucial than intragranular precipitation density.

The measurement of damage from high temperature solid particle erosion (HTSPE) can be a lengthy process within the laboratory with many lab-based systems requiring sequential heat and cooling of the test piece to enable mass and/or scar volume measurements to be made ex situ. Over the last few years a new lab-based system has been in development at the National Physical Laboratory which has the ability to measure the mass and volume change of eroded samples in situ without the need to cool the sample. Results have previously been shown demonstrating the in situ mass measurement, more recently the in situ volume measurement capability has been added and used to evaluate the erosion performance of additively manufactured materials. Selective laser melting (SLM) is an advanced manufacturing method which is growing in popularity and application. It offers the ability to manufacture low volume complex parts and has been used in rapid prototyping. As the technique has developed there is increasing interest to take advantage of the ability to manufacture complex parts in one piece, which in some case can be more cost and time effective than traditional manufacturing routes. For all the benefits of SLM there are some constraints on the process, these include porosity and defects in the materials such as ‘kissing bonds’, surface roughness, trapped powder and microstructural variation. These features of the processing route may have implications for component performance such as strength, fatigue resistance wear and erosion. To investigate this further SLM IN718 has been used to evaluate factors such as surface roughness, microstructure and morphology on the erosion performance as measured in situ and compared with conventional produced wrought IN718 material.

Effects of alloying additions of Ti or Mo to a simplified chemical composition of the γ′′-Ni 3 Nb strengthened type Ni-based alloy 718 on the precipitation mode of δ-Ni 3 Nb phase were investigated to aim at designing grain boundaries using the δ phase for raising temperature capability of the γ′′ strengthened Ni-based wrought alloys. In the base alloy of Ni-22Cr-16Fe-3.5Nb, the δ phase precipitated at the grain boundaries of the matrix phase in a platelet form by continuous precipitation mode at temperatures above 1273K (1000°C) but in a lamellar morphology by discontinuous precipitation mode below that temperature. The boundary temperature where the continuous/discontinuous precipitation mode changes was raised by addition of 1 % Ti and lowered by addition of 5% Mo. The increase in the boundary temperature by Ti addition can be considered to have occurred by an increase in the solvus temperature of γ′′ phase. The decrease in the boundary temperature by Mo addition can be interpreted by the reduction of the strain energy caused by the coherent γ′′ precipitates and/or the volume change by the formation of δ phase from the γ/γ′′ phases, which may promote the continuous precipitation with respect to the discontinuous precipitation.

Ni-38Cr-3.8Al has high hardness and high corrosion resistance with good hot workability, and therefore, it has been applied on various applications. However, in order to expand further application, it is important to understand the high temperature properties. Then, this study focused on the high temperature properties such as thermal phase stability, hardness, tensile property, creep property and hot corrosion resistance. As the result of studies, we found that the thermal phase stability of (γ/α-Cr) lamellar structure and the high temperature properties were strongly influenced by the temperature. Although the high temperature properties, except for creep property, of Ni-38Cr-3.8Al were superior to those of conventional Ni-based superalloys, the properties were dramatically degraded beyond 973 K. This is because the lamellar structure begins to collapse around 973 K due to the thermal stability of the lamellar structure. The hot corrosion resistance of Ni-38Cr-3.8Al was superior to that of conventional Ni-based superalloys, however, the advantage disappeared around 1073 K. These results indicate that Ni-38Cr-3.8Al is capable as a heat resistant material which is required the hot corrosion resistance rather than a heat resistant material with high strength at high temperature.

The relationship between the hot workability and the precipitation morphology of γ′ phase in the Alloy U520 was examined with a focus on the presence of γ′-nodule. To change the morphology of γ’ phase, forged bars of the Alloy U520 were solution treated followed by cooling process with the cooling rates of 5~100 K/h. After the heat treatment, both γ’ phases of intragranular particle and nodule along grain boundaries were observed, and the both sizes increased by slowing down the cooling rate. That is, the area fraction of γ’-nodule increased from about 0.1 % in the sample cooled at 100 K/h to about 70 % at 5 K/h. In Gleeble tension test, the slow-cooled samples basically exhibited higher ductility than water-quenched samples below the γ′-solvus temperature. However, the ductility was maximized in the sample cooled at 20 K/h, and excessive decrease of cooling rate resulted in a drop in ductility. EBSD analysis revealed that dynamic recrystallization (DRX) was often occurred in grain interior but suppressed at γ′-nodule area, indicating that presence of γ′-nodule had a negative influence on hot workability at subsolvus temperature.

Development of the advanced USC (A-USC) boiler technology has been promoted in recent years, which targets 700°C steam condition. HR6W (Ni-23Cr-7W-Ti-Nb-25Fe) and HR35 (Ni-30Cr-6W-Ti-15Fe) have been developed for A-USC boiler tubes and pipes. The former alloy is mainly strengthened by Fe 2 W type Laves phase. The latter one employs precipitation strengthening of α-Cr phase in addition to Laves phase. Characteristic alloy design of both alloys, which does not use precipitation strengthening of γ′ phase (Ni 3 Al), leads to superior ductility and resistance to stress-relaxation cracking. Stability of creep strength and microstructure has been confirmed by long-term creep rupture tests. The 100,000h average creep rupture strength of HR6W is 85MPa at 700C. That of HR35 is 126MPa at 700°C which is comparable with conventional Alloy617. Tubes of both alloys have been evaluated by the component test in Japanese national A-USC project with γ′ hardened Alloy617 and Alloy263. Detailed creep strength, deformation behavior and microstructural evolution of these alloys are described from the viewpoint of the difference in strengthening mechanisms. Capability of these alloys for A-USC boiler materials has been demonstrated by the component test in the commercial coal fired boiler as the part of the A-USC project.

In order to establish a creep damage assessment method for 47Ni-23Cr-23Fe-7W (HR6W), which is a candidate material of A-USC, microstructure observation of creep interrupted specimens and ruptured specimen was conducted, and the creep damage process was examined. Creep tests were conducted under conditions of 800°C, 70 MPa, 700°C, and 100 MPa. For creep damage assessment, an optical microscope was used for replicas sampled from the outer surface of specimens, and crack ratio at grain boundaries was assessed. The results indicated that creep voids and cracks were initiated at grain boundaries from about 0.35 of creep life ratio, and crack ratio increased drastically after creep life ratio of 0.65. This crack ratio was almost the same regardless of the specimen shape Therefore, the method to assess crack ratio using replicas is considered to be an effective method for creep damage assessment of HR6W. An increase in the crack ratio due to an increase in creep life ratio showed the same trend as the change in elongation of creep interrupted specimens. Microstructure observations were conducted with interrupted specimens using SEM-ECCI (Electron Channeling Contrast Imaging) in order to clarify the cause of acceleration creep. The results showed that sub-boundary developed significantly near grain boundaries, which indicates that sub-boundary development may cause acceleration.

Long-term performance of high temperature alloys is critically linked to the oxidation behavior in power generation applications in wet air and steam. As power generation systems move towards higher efficiency operation, nextgeneration fossil, nuclear and concentrating solar power plants are considering supercritical CO 2 cycle above 700°C. Wrought solid solution strengthened and precipitations strengthened alloys are leading candidates for both steam and Supercritical CO 2 power cycles. This study evaluates the cyclic oxidation behavior of HAYNES 230, 282, and 625 alloys in wet air, flowing laboratory air, steam and in 1 and 300 bar Supercritical CO 2 at ~750°C for duration of 1000 -10,000h. Test samples were thermally cycled for various times at temperature followed by cooling to room temperature. Alloy performances were assessed by analyzing the weight change behavior and extent of attack. The results clearly demonstrated the effects of alloy composition and environment on the long-term cyclic oxidation resistance. The extents of attack varied from alloy to alloy but none of the alloys underwent catastrophic corrosion and no significant internal carburization was observed in supercritical CO 2 . The performance of these alloys indicates that these materials are compatible not only in oxidizing environments, but also in Supercritical CO 2 environments for extended service operation.

The current work presented a study of isothermal-oxidation behavior of the additive manufactured (AM) Alloy718 in air at 800°C. The oxidation behavior of Alloy718 specimens produced by selective laser melting (SLM) and electron beam melting (EBM) process were comparatively examined. No significant differences were observed in oxidation kinetics while different microstructures of the oxide scale were found. Coarse and columnar chromia grains developed on SLM specimens, whereas the chromia scale of EBM specimens consisted of extremely fine grains. Glow Discharge Optical Emission Spectrometry (GD-OES) analysis revealed that SLM specimens contain a higher content of Ti in chromia compared with EBM specimens. Process-induced supersaturation in SLM specimens might lead to a relatively high concentration of Ti in the chromia, which may affect the grain morphology of oxide scale in the SLM specimen.

The effect of gas impurities on corrosion behavior of candidate Fe- and Ni-base alloys (SS 316LN, Alloy 800HT, Alloy 600) in high temperature CO 2 environment was investigated in consideration of actual S-CO 2 cycle applications. Preliminary testing in research and industrial grade S-CO 2 at 600 °C (20 MPa) for 1000 h showed that oxidation rates were significantly reduced in industrial-grade S-CO 2 environment. Meanwhile, controlled tests with individual impurity additions such as CH 4 , CO, and O 2 in research-grade CO 2 were performed. The results indicated that CH 4 and CO additions did not seem to significantly affect oxidation rates. On the other hand, O 2 addition resulted in lower weight gains for all alloys, suggesting that O 2 may be primarily affecting corrosion behavior.

Model alloys of Fe-20Cr and Ni-20Cr (all compositions in weight %) and variants containing small amounts of Si or Mn were exposed to Ar-20CO 2 and Ar-20CO 2 -H 2 O (volume %) at 650 or 700°C. Protective Cr 2 O 3 scale was more readily formed on Fe-20Cr than Ni-20Cr, as a result of the different alloy diffusion coefficients. Silicon additions slowed chromia scale growth, promoting passivation of both alloy types. Water vapour accelerated chromia scaling, but slowed NiO growth.