The susceptibilities of hot cracking and reheat cracking of A-USC candidate Ni-based alloys were evaluated relatively by Trans-Varestraint testing and Slow Strain Rate Tensile (SSRT) testing. In addition, semi-quantitative evaluation of the stress relaxation cracking susceptibility of Alloy 617 was conducted, because stress relaxation cracking in the heat affected zone (HAZ) has actually been reported for repair welds in Alloy 617 steam piping in European A-USC field-testing. Solidification cracking susceptibilities of Alloy 617 were the highest; followed by HR35, Alloy 740 and Alloy 141, which were all high; and then by HR6W and Alloy 263, which were relatively low. In addition, liquation cracking was observed in the HAZ of Alloy 617. The reheat cracking susceptibilities of Alloy 617, Alloy 263, Alloy 740 and Alloy 141 were somewhat higher than those of HR6W and HR35 which have good creep ductility due to the absence of γ’ phase precipitates. A method to evaluate stress relaxation cracking susceptibility was developed by applying a three-point bending test using a specimen with a V-notch and finite element analysis (FEA), and it was shown that stress relaxation cracking of aged Alloy 617 can be experimentally replicated. It was proposed that a larger magnitude of creep strain occurs via stress relaxation during the three-point bending test due to a higher yield strength caused by γ’ phase strengthening, and that low ductility due to grain boundary carbides promoted stress relaxation cracking. The critical creep strain curve of cracking can be created by means of the relationship between the initial strain and the creep strain during the three-point bending tests, which were calculated by FEA. Therefore, the critical conditions to cause cracking could be estimated from the stress relaxation cracking boundary from of the relationship between the initial strain and the creep strain during the three-point bending test.

A constitutive equation, with parameters derived from the interpolation of primary and steady state stages of constant load creep curves, has been utilized to estimate the stress relaxation behavior of the martensitic steel X20Cr13, alloy used in many high temperature applications, including heavy duty gas turbines. Creep and stress relaxation tests have been performed at 350°C, close to the negligible creep temperature of the studied alloy for stresses of interest for engineering applications. The creep tests were carried out at stresses below and above the yield stress, whereas, for the relaxation stress tests, the imposed strain was in the range 0.2% to 1.2% with the purpose to have, at the beginning of the tests, the same initial stresses of the performed creep tests. After a stress relaxation period, lasting between 10 to 1000 hours, each specimen was generally reloaded at the initial stress and a new relaxation test, on the same specimen, was carried out. This “reloading procedure”, simulating the re-tightening of bolts, has been repeated several times. The proposed equation has shown to well predict the experimental creep and stress relaxation behavior of the steel under investigation.

Finite element (FE) modeling has been applied to a stress relaxation cracking (SRC) test in order to evaluate the effects of changing sample geometry and material type. This SRC test uses compressive pre-straining to create a tensile residual stress in modified compact-tension specimens and has been used to test 316H stainless steel. The FE model is first used to verify that sample integrity will not be compromised by modifying the geometry. The FE model is then applied to candidate Advanced Ultra Supercritical nickel-base alloys 617, 740H, and 800. It is determined that this stress relaxation test will be appropriate for these alloys.

In today’s market place power generation plants throughout the world have been trying to reduce their operating costs by extending the service life of their critical machines such as steam turbines and gas turbines beyond the design life criteria. The key ingredient in plant life extension is remaining life assessment technology. This paper will outline remaining life procedures which will incorporate the defect tolerant design concepts applied to the various damage mechanisms such as creep, fatigue, creep-fatigue and stress corrosion cracking. Also other embrittlement mechanisms will also be discussed and how they will influence the life or operation of the component. Application of weld repairs to critical components such as rotors and steam chest casings will be highlighted and how defect tolerant design concept is applied for the repair procedure and the acceptance standard of the nondestructive testing applied. Also highlighted will be various destructive tests such as stress relaxation tests (SRT) which measures creep strength and constant displacement rate test (CDRT) which evaluates fracture resistance or notch ductility. Also shown will be actual life extension examples applied to steam turbine components and weld repairs. Utilization of computer software to calculate fatigue and creep fatigue crack growth will also be presented

High precision stress relaxation tests (SRT) at temperatures between 550C and 700C were performed on serviced and reheat treated T91, 9%Cr steel. The service exposure was 116,000 hours at steam temperatures to 550C. Constant displacement rate (CDR) tests were also run at 600C on notched specimens for the two conditions. Specimens, heat treated after service, were stronger at the lower test temperatures in terms of both tensile strength and creep strength. This difference was reflected in the CDR results, which also suggested a lower fracture resistance in the heat treated condition. Thus, service exposure appears to have softened the alloy and enhanced its resistance to fracture, with no evidence of embrittling reactions. Based on the analysis of the SRT tests, projections were made of the times to 1% creep and the times to rupture as well as direct comparisons with minimum creep rate data'. When plotted on the basis of a Larson- Miller parameter (C=30), the calculated values compared well with actual long time rupture testing for exposed and re-heat treated specimens, and generally showed higher precision. The longest test time was about eighteen months for the stress rupture data compared with the use of one machine for a few weeks for the SRT data. The latter actually covered a far greater range of creep rates and projected lives. The SRT test is especially consistent at higher parameter values, i.e., higher temperatures and/or lower stresses. This method of accelerated testing is now being applied to a wide range of alloys for fossil power plants for composition and process optimization, design analysis, and life assessment.