The morphological evolution of secondary γ′ precipitates under the coarsening process was investigated for commercial wrought Ni-based superalloys, which can be classified into two processes, i.e. “localization process” and “aggregation process”. The localization process was defined as a phenomenon in which cuboidal γ′ precipitates were arranged in the <100> direction for superalloys. In contrast, the aggregation process was defined as a phenomenon in which neighboring spherical γ′ precipitates coarsen while overlapping their interfaces for superalloys. All the wrought Ni-based superalloys could be classified into the above two processes based on their volume fraction and lattice misfit. The coarsening of γ′ precipitates follow the aggregation process when the misfit is smaller than 0.05%, and it follows the localization process otherwise.

In this work, the effects of phosphorus addition on the creep properties and microstructural changes of wrought γ’-strengthened Ni-based superalloys (Haynes 282) were investigated, focusing on the effects of carbides precipitation. In an alloy with a phosphorus content of 8 ppm, precipitation of M 23 C 6 carbides was observed in both grain boundaries and the grain interior prior to the creep tests. Grain boundary coverage by carbide increased with phosphorus content up to approximately 30 ppm. On the other hand, the amount of M 23 C 6 in the grain interior decreased with phosphorus content. The results of the creep tests revealed the relationship between the time to rupture and the grain boundary coverage by carbides. The microstructure of the crept specimens showed the existence of misorientation at the vicinity of grain boundaries without carbides, as demonstrated via electron backscattered diffraction (EBSD) analysis. These results suggest that the observed improvement in the time to rupture is due to a grain-boundary precipitation strengthening mechanism caused by grain boundary carbides and that phosphorus content affects the precipitation behavior of M 23 C 6 carbides in the grain interior and grain boundaries. These behaviors were different between alloys with the single addition of phosphorus and alloys with the multiple addition of phosphorus and niobium.

In wrought nickel-base alloys used at elevated temperatures for extended periods of time, it is commonly observed that unwanted phases may nucleate and grow. One such phase is the eta phase, based on Ni 3 Ti, which is a plate-shaped precipitate that nucleates at the grain boundaries and grows at the expense of the strengthening gamma prime phase. In order to study the effects of eta phase on creep performance, Alloy 263 was modified to contain 3 different microstructures: standard (contains gamma prime); aged (contains gamma prime and eta); and modified (contains only eta and no gamma prime). These microstructures were then creep tested in the range of 973-1123 K (700-850°C). An extensive test matrix revealed that the eta-only modified alloy had creep rupture strengths within 10% of the standard alloy even though this alloy had no strengthening gamma prime precipitates. It also exhibited superior creep ductility. A preliminary test matrix on the aged material containing eta and gamma prime prior to the creep tests revealed that the performance of this microstructure was generally between that of the standard alloy (best) and the eta-only alloy (worst). The aged material exhibited far superior creep ductility. These results suggest that the presence of the eta phase may not be deleterious to creep ductility, and in fact, may enhance it.

Advanced 700C class steam turbines require austenitic alloys instead of conventional ferritic heat-resistant steels which have poor creep strength and oxidation resistance above 650C. Austenitic alloys, however, possess a higher thermal expansion coefficient than ferritic 12Cr steels. Therefore, Ni-based superalloys were tailored to reduce their coefficients to the level of 12Cr steels. Regression analysis of commercial superalloys proves that Ti, Mo and Al decrease the coefficient quantitatively in this order, while Cr, used to secure oxidation resistance, increases it so significantly that Cr should be limited to 12wt%. The newly designed Ni-18Mo-12Cr-l.lTi-0.9Al alloy is strengthened by gamma-prime [Ni 3 (Al,Ti)] and also Laves [Ni 2 (Mo,Cr)] phase precipitates. It bears an RT/700C mean thermal expansion coefficient equivalent to that of 12Cr steels and far lower than that of low-alloyed heat resistant steels. Its creep rupture life at 700C and steam oxidation resistance are equivalent to those of a current turbine alloy, Refractaloy 26, and its tensile strength at RT to 700C surpasses that of Refractaloy 26. The new alloy was trial produced using the VIM-ESR melting process and one ton ingots were successfully forged into round bars for bolts without any defects. The bolts were tested in an actual steam turbine for one year. Dye penetrant tests detected no damage. The developed alloy will be suitable for 700C class USC power plants.