Cast nickel-based superalloys used as structural materials for gas turbine parts need to withstand high temperatures and dynamic mechanical loads. When in contact with ambient air, the formation of protective oxide scales causes a depletion of γ’-precipitates in the surface-near region and leaves a weakened microstructure. This environmentally based degradation of the material might be accelerated under cyclic thermal exposure. In this paper, the cyclic oxidation behavior of two cast nickel-based superalloys and one single crystalline variant are investigated: C1023, CM-247 LC and M-247 SX. Exposure tests were carried out under both isothermal and cyclic conditions in air at 850 °C, 950 °C and 1050 °C for times up to 120 h to investigate the impact of thermal cycling. The differences in oxidation mechanisms are analyzed phenomenologically via light and electron microscopy and brought in correlation with the oxidation kinetics, determined based on net mass change and depletion zone growth. An assessment of the impact of precipitation loss on local mechanical strength is attempted via nano-indentation method. The found relations can be transferred onto an acceleration of crack growth under creep-fatigue and thermo-mechanical fatigue conditions.

Haynes 282 alloy is a relatively new Ni-based superalloy that is being considered for advanced ultrasupercritical (A-USC) steam turbine casings for steam temperatures up to 760°C. Weld properties are important for the turbine casing application, so block ingots of Haynes 282 alloy were cast for properties studies. Good, sound welds were produced using Haynes 282 weld-wire and a hot gas-tungsten-arc welding method, and tensile and creep-rupture properties were measured on cross-weld specimens. In the fully heat-treated condition (solution annealed + aged), the tensile properties of the welded specimens compare well with as-cast material. In the fully heat-treated condition the creep-rupture life and ductility at 750°C/250MPa and 800°C/200MPa of the cross-weld specimens are similar to the as-cast base metal, and repeat creep tests show even longer rupture life for the welds. However, without heat-treatment or with only the precipitate age-hardening heat-treatment, the welds have only about half the rupture life and much lower creep ductility than the as-cast base metal. These good properties of weldments are positive results for advancing the use of cast Haynes 282 alloy for the A-USC steam turbine casing application.

Additive manufacturing (AM) is a process where, as the name suggests, material is added during production, in contrast to techniques such as machining, where material is removed. With metals, AM processes involve localised melting of a powder or wire in specific locations to produce a part, layer by layer. AM techniques have recently been applied to the repair of gas turbine blades. These components are often produced from nickel-based superalloys, a group of materials which possess excellent mechanical properties at high temperatures. However, although the microstructural and mechanical property evolution during the high temperature exposure of conventionally produced superalloy materials is reasonably well understood, the effects of prolonged high temperature exposure on AM material are less well known. This research is concerned with the microstructures of components produced using AM techniques and an examination of the effect of subsequent high temperature exposures. In particular, the paper will focus on the differences between cast and SLM IN939 as a function of heat treatment and subsequent ageing, including differences in grain structure and precipitate size, distribution and morphology, quantified using advanced electron microscopy techniques.

A global movement is pushing for improved efficiency in power plants to reduce fossil fuel consumption and CO 2 emissions. While raising operating temperatures and pressures can enhance thermal efficiency, it necessitates materials with exceptional high-temperature performance. Currently, steels used in power plants operating up to 600°C achieve efficiencies of 38-40%. Advanced Ultra Supercritical (A-USC) designs aim for a significant leap, targeting steam temperatures of 700°C and pressures of 35 MPa with a lifespan exceeding 100,000 hours. Ni-based superalloys are leading candidates for these extreme conditions due to their superior strength and creep resistance. Haynes 282, a gamma prime (γ′) precipitation-strengthened alloy, is a promising candidate for A-USC turbine engines, exhibiting excellent creep properties and thermal stability. This research investigates the microstructural evolution in large, sand-cast components of Haynes 282. Microstructure, referring to the arrangement of grains and phases within the material, significantly impacts its properties. The research examines the alloy in its as-cast condition and after various pre-service heat treatments, aiming to fully identify and quantify the microstructural changes. These findings are then compared with predictions from thermodynamic equilibrium calculations using a dedicated Ni alloy database. The research reveals that variations in heat treatment conditions can significantly affect the microstructure development in Haynes 282, potentially impacting its mechanical properties.

As conventional coal-fired power plants seek to reduce greenhouse gas emissions by increasing efficiency, the temperature limitations of traditional ferritic/martensitic steels used in high-temperature components present a significant challenge. With Advanced Ultra Supercritical (A-USC) power plants proposing steam temperatures of 760°C, attention has turned to nickel-based superalloys as potential replacements, since ferritic/martensitic steels cannot withstand such extreme conditions. However, the current absence of cast nickel-based superalloys combining high strength, creep-resistance, and weldability has led to the development of cast analogs of wrought nickel-based superalloys, including H263, H282, and N105. This paper examines the alloy design criteria, processing experiences, as-processed and heat-treated microstructures, and selected mechanical properties of these materials while also discussing their potential for full-scale development.

Advanced UltraSupercritical (A-USC) Steam fossil power plants will operate at steam temperatures up to 760°C, which will require the use of Ni-based superalloys for steam boiler/superheater and turbine systems. In 2008, the Oak Ridge National Laboratory (ORNL) and the National Engineering Technology Laboratory/Albany (NETL/Albany) collaborated to make and test castings of Ni-based superalloys, which were previously only commercially available in wrought form. These cast Ni-based based alloys are envisioned for the steam turbine casing, but they may also be applicable to other large components that connect the steam supply to the steam turbine. ORNL and NETL/Albany have produced small vacuum castings of HR 282, Nimonic 105, Inconel 740, and alloy 263, which are precipitation-hardened Ni-based superalloys, as well as solid-solution superalloys such as alloys 625, 617 and 230. The initial alloy screening included tensile and creep-testing at 800°C to determine which alloys are best suited for the steam turbine casing application at 760°C. HR 282 has the best combination of high-temperature strength and ductility, making it a good candidate for the cast-casing application. Cast and wrought versions of HR 282 have similar creep-rupture strength, based on the limited data available to-date. Detailed comparisons to the other alloys and microstructures are included in this paper.