To improve the economics of critical components, such as receivers and heat exchangers, for Generation 3 (Gen 3) concentrating solar power (CSP) plants, research was conducted to understand how manufacturing impacts the high-temperature performance of various tube production routes. Gen 3 CSP components are expected to require the use of heat-resistant nickel- based alloys due to the elevated operating temperatures in designs carrying molten salt or supercritical CO 2 . INCONEL alloy 740H (alloy 740H) was investigated as an alternative to UNS N06230 (alloy 230) as it possesses superior high-temperature creep strength which can lead to overall reductions in material cost. A key challenge is understanding how autogenous seam welding with and without re-drawing can be used to manufacture thin-wall tubing for CSP receivers and heat-exchangers to further reduce costs over traditional seamless production routes. Alloy 740H welded tube was successfully fabricated and re-drawn to several relevant tube sizes. Since traditional mechanical testing samples could not be removed from the thin-wall tubing, full-sized tubes were used for tensile, fatigue, and vessel testing (internally pressurized creep- rupture) which was critical to understanding the weld performance of the manufactured product forms. The generated vessel test data exhibited a creep strength reduction when compared to wrought product with no clear trend with temperature or test duration. It was found that redrawing the welded tubes improved the creep strength to approximately 82% of the wrought material performance and elevated temperature tensile and fatigue behavior exceeded 85% of the design minimums. Detailed, post-test characterization found that nano-sized carbides formed during the laser seam-welding process remained stable after multiple solution-annealing steps, which restricted grain growth, and impacted the time-dependent performance. This paper will focus on the time-dependent behavior of the examined welded and redrawn tubes, supporting metallographic evidence, and give perspective on future considerations for using alloy 740H in CSP components.

Simple and effective material examination methods are desired for the diffusion bonding process, so that bonding produced components, such as compact heat exchangers, can be used in nuclear applications. Optical microscopy of diffusion bond process samples is a quick way to examine diffusion bond-line microstructure and to evaluate material quality. The stacked nature of a diffusion bonded-block results in distinct regions of grain growth both at and away from the bond interface. Strong diffusion bond materials exhibit grain growth across the original bond interface plane, weak materials have little-to-no growth across. A series of 316H diffusion bonded specimens of differing quality and strength were examined using optical microscopy. The microstructure both at and away from the bond interface was examined over 15mm long sections of the bond-line. A metric for evaluating bond growth is proposed. This is defined as the Bond Line Growth Threshold (BLGT) and is evaluated as the percentage of the bond line with grains meeting the threshold. Here a fraction of the diffusion bond is considered bonded when its grains exceed a threshold of growth past the bond interface. The BLGT is determined through automated image processing methods.

The steam generation systems (SGS) of concentrated solar power (CSP) plants employ multiple heat exchangers arranged in series to convert thermal energy collected from the sun via a heat transfer fluid (HTF) to produce superheated steam in the Rankine cycle. Common CSP plant designs are based either on parabolic trough or central tower technology. The major Rankine cycle components consist of preheaters, evaporators, steam drums, superheaters, steam turbines, and water/air-cooled condensers, all connected through steel piping. For CSP plants capable of reheating the steam for improved efficiency, reheaters are also included in the Rankine cycle. In central tower design with directly heated water as the HTF, the receiver can also be considered part of the Rankine cycle. Operating experiences of CSP plants indicate that plant reliability is significantly impacted by failures in various components of the Rankine cycle. Many damage mechanisms have been identified, which include corrosion, thermal fatigue, creep, and stress corrosion cracking, among others. Much of the damage can be attributed to poor water/steam chemistry and inadequate temperature control. While damage in the Rankine cycle components is common, there is generally lack of comprehensive guidelines created specifically for the operation of these CSP components. Therefore, to improve CSP plant reliability and profitability, it is necessary to better understand the various damage mechanisms experienced by linking them to specific operating conditions, followed by developing a “theory and practice” guideline document for the CSP operators, so that failures in the Rankine cycle components can be minimized. In a major research project sponsored by the U.S. Department of Energy (DOE), effort is being undertaken by EPRI to develop such a guideline document exclusively for the CSP industry. This paper provides an overview of the ongoing DOE project along with a few examples of component failures experienced in the Rankine cycle.

Diffusion bonded compact heat exchangers have exceptionally high heat transfer efficiency and might significantly improve the performance and reduce the cost of supercritical carbon-dioxide Brayton cycle power plants using high temperature heat sources, like high temperature nuclear reactors and concentrating solar power plants. While these heat exchangers have an excellent service history for lower temperature applications, considerable uncertainty remains on the performance of diffusion bonded material operating in the creep regime. This paper describes a microstructural modeling framework to explore the plausible mechanisms that may explain the reduced creep ductility and strength of diffusion bonded material, compared to wrought material. The crystal plasticity finite element method (CPFEM) is used to study factors affecting bond strength in polycrystals mimicking diffusion bonded microstructures. Additionally, the phase field method is also employed to simulate the grain growth and recrystallization at the bond line to model the bonding process and CPFEM is used to predict the resulting material performance to connect processing parameters to the expected creep life and ductility of the material, and to study potential means to improve the structural reliability of the material and the resulting components by optimizing the material processing parameters.

Steels have a proven track record of safe operation in steam power plants for decades. Interest in developing supercritical CO 2 power cycles as a more efficient and sustainable alternative to steam cycles has driven a need to understand steel performance in these new environments. In particular, the potential of the high temperature CO 2 environment to influence the creep behavior of the steel must be determined. Prior research on this topic between the 1960s and 1980s found conflicting conclusions, but nevertheless raised the possibility that carburization during CO 2 exposure may strongly affect the creep behavior. This raises concerns particularly for thin-sectioned components such as compact heat exchangers, where even small rates of carburization can become problematic over long operating lifetimes. To shed light on this issue, this research investigates the creep behavior of austenitic stainless steel 347H and 309H (a higher Cr alternative) at 650°C. Specimens of 0.5, 1.0, and 2.0 mm thickness were tested to further assess the effect of steel thickness. Both steels show a reduction in creep life in CO 2 relative to air, with 309H showing slightly better performance than 374H. Analysis is ongoing to determine the reason for degraded creep properties.

Diffusion bonding is a key manufacturing process for nucleation applications including compact heat exchangers. Accurately predicting the alloy's behavior during the diffusion bonding process presents challenges, primarily due to the intricate interplay of microstructural evolution and physical processes such as compressive loading, temperature history, and component migration. The current study develops a phase-field model designed to simulate the diffusion bonding in 316H stainless steel, a material with exceptional high-temperature strength, corrosion resistance and suitability to high-pressure conditions. Our model incorporates a multi-phase, multi-component framework that aligns the experimental observations with the grain growth and heterogeneous nucleation, where arbitrary external compressive load and temperature history are considered. The simulations focus on grain nucleation, growth, and microstructure evolutions across diffusion bonding line under a variety of temperature profiles, mechanical loads, and surface roughness conditions, mirroring experimental setups. Our model predicts consistent simulation results with experiments in terms of the grain size and distribution near the bonding area, offering a better understanding of the diffusion bonding mechanism and the manufacturing process for building reliable compact heat exchangers.

Due to their excellent high temperature oxidation resistance, utilities worldwide are adopting advanced austenitic stainless steels (A-ASS) for critical plant components, such as heat exchangers, as they aim to achieve higher operating conditions. However, challenges may be encountered in developing life assessment and life management strategies for such components. This is because conventional methods used for life assessment, such as measuring steam side oxide scale thickness in ferritic and conventional austenitic material to predict tube metal temperature, may not be successfully applied to A-ASS. In such instances, tracking the formation and evolution of microstructural features during service, may offer a possible method to predict the temperature of these steels. For such metallurgy based lifing strategy to be successful, it is essential to develop a good understanding of microstructure evolution in these steels. In this work one heat of Super 304H, that has been creep tested at 600°C, 650°C and 700°C, with applied stress ranging from 110 to 340 MPa, is characterized using a combination of advanced characterization tools and image analysis methods. The amount of sigma phase formed at the gauge and grip sections of the samples is quantified and the methodology used to quantify this phase is presented. From the results, a time-temperature-transformation diagram for sigma formation is developed.

To stay competitive in today’s dynamic energy market, traditional thermal power plants must enhance efficiency, operate flexibly, and reduce greenhouse gas emissions. This creates challenges for material industries to provide solutions for harsh operating conditions and fluctuating loads. Higher efficiency demands steels with excellent steam oxidation resistance, favoring ferritic steels for cycling operation due to their limited thermal expansion. This paper presents a study modeling a combined cycle power plant using GE 9HA0.2 GT technology. The analysis compares different maximum live steam temperatures (585°C, 605°C, 620°C) and four alloys (grades 91 and 92, stainless S304H, and Thor 115) for heat exchangers exposed to steam oxidation. Results indicate that Thor 115, a creep strength enhanced ferritic (CSEF) steel, is a viable alternative to stainless steel for live steam temperatures above 600°C, offering improved oxidation resistance with minimal weight increase. Modern CSEF steels outperform stainless steel in power plants with lower capacity factors, reducing thermal fatigue during load changes. Increasing the live steam temperature boosts plant efficiency, leading to significant CO 2 savings for the same power output.

INCONEL alloy 740H has been specified for tube and pipe for the boiler and heat exchanger sections of AUSC and sCO 2 pilot plants currently designed or under construction. These systems also require fittings and complex formed components such as flanges, saddles, elbows, tees, wyes, reducers, valve parts, return bends, thin-wall cylinders and tube sheets. The initial evaluation of alloy 740H properties, leading to ASME Code Case 2702, was done on relatively small cross-section tube and plate. The production of fittings involves the use of a wide variety of hot or cold forming operations. These components may have complex geometric shapes and varying wall thickness. The utility industry supply chain for fittings is largely unfamiliar with the processing of age-hardened nickel-base alloys. Special Metals has begun to address this capability gap by conducting a series of trials in collaboration with selected fittings manufacturers. This paper describes recent experiences in first article manufacture of several components. The resulting microstructure and properties are compared to the published data for tubular products. It is concluded that it will be possible to manufacture most fittings with properties meeting ASME Code minima using commercial manufacturing equipment and methods providing process procedures appropriate for this class of alloy are followed. INCONEL and 740H are registered trademarks of Special Metals Corporation.

High efficiency in power generation is not only desirable because of economical reasons but also for enhanced environmental performance meaning reduced quantity of forming ash and emissions. In modern medium to large size plants, improvements require supercritical steam values. Furthermore, in future there will be an increasing share of renewables, such as wind and solar power, which will enhance the fluctuation of supply with the consequence that other power sources will have to compensate by operating in a more demanding cyclic or ramping mode. The next generation plant will need to operate at higher temperatures and pressure cycles coupled with demanding hot corrosion and oxidation environments. Such an operation will significantly influence the performance of materials used for boilers and heat exchanger components by accelerating oxidation rates and lowering mechanical properties like creep resistance. The paper discusses the oxidation behaviour of San25, 800H and alloy 263 in supercritical water at temperatures 650 and 700 °C at 250 bar, and compares the changes of mechanical properties of materials at these temperatures.

This paper outlines a comprehensive UK-based research project (2007-2010) focused on developing fireside corrosion models for heat exchangers in ultra-supercritical plants. The study evaluates both conventional materials like T22 and advanced materials such as Super 304H, examining their behavior under various test environments with metal skin temperatures ranging from 425°C to 680°C. The research aims to generate high-quality data on corrosion behavior for materials used in both furnace and convection sections, ultimately producing reliable corrosion prediction models for boiler tube materials operating under demanding conditions. The project addresses some limitations of existing models for these new service conditions and provides a brief review of the fuels and test environments used in the program. Although modeling is still limited, preliminary results have been presented, focusing on predicting fireside corrosion rates for furnace walls, superheaters, and reheaters under various service environments. These environments include those created by oxyfuel operation, coal-biomass co-firing, and more traditional coal firing.