This paper presents the creep and creep-fatigue crack growth behaviors of 30Cr1Mo1V turbine rotor steel which had been in service for 16 years. Two typical sections of the rotor, i.e. high and low temperature sections, are examined at 538°C, with crack initiation and propagation monitored by D.C. potential drop method in a compact tension (CT) specimen. The material of the high temperature section has the lower resistance to creep and creep-fatigue crack growths than the low temperature section. The creep crack initiation (CCI) time decreases with the increase of initial stress intensity factor. The creep-fatigue crack growth (CFCG) is dominated by the cycle-dependent fatigue process when the hold time at the maximum load is shorter, but it becomes dominated by the time-dependent creep process when the hold time becomes longer. The high temperature section shows a larger influence of time-dependent creep behavior on CFCG than the low temperature section.

Creep-fatigue crack formation (endurance) and crack growth rate data are necessary inputs for assessing the structural integrity and for estimating the design life of high temperature components in power generation and aircraft engine industries. Ensuring consistency in the reported test data, as well as an understanding of the inherent scatter and its source in the data, are both necessary for assuring quality and limitations of the analyses that rely on the data. In 2008, the American Society for Testing and Materials (ASTM) under the umbrella of its subcommittees E08.05 on Cyclic Deformation and Crack Formation and E08.06 on Crack Growth, and the sponsorship of Electric Power Research Institute (EPRI) through its international experts’ working group on creep-fatigue embarked on the task of developing separate standard test methods for creep-fatigue crack formation and creep-fatigue crack growth. The first standard entitled, “E-2714-09: Standard Test Method for Creep-fatigue Testing” was developed in 2009 and was followed up with a round-robin consisting of 13 laboratories around the world for testing the newly developed standard. This paper discusses the results of this round-robin concluded in 2012 using the widely used P91 steel that led to the formulation of the Precision and Bias statement contained in the version of the ASTM standard E2714 that was successfully balloted in the year 2013.

In today’s market place power generation plants throughout the world have been trying to reduce their operating costs by extending the service life of their critical machines such as steam turbines and gas turbines beyond the design life criteria. The key ingredient in plant life extension is remaining life assessment technology. This paper will outline remaining life procedures which will incorporate the defect tolerant design concepts applied to the various damage mechanisms such as creep, fatigue, creep-fatigue and stress corrosion cracking. Also other embrittlement mechanisms will also be discussed and how they will influence the life or operation of the component. Application of weld repairs to critical components such as rotors and steam chest casings will be highlighted and how defect tolerant design concept is applied for the repair procedure and the acceptance standard of the nondestructive testing applied. Also highlighted will be various destructive tests such as stress relaxation tests (SRT) which measures creep strength and constant displacement rate test (CDRT) which evaluates fracture resistance or notch ductility. Also shown will be actual life extension examples applied to steam turbine components and weld repairs. Utilization of computer software to calculate fatigue and creep fatigue crack growth will also be presented

High temperature components with notches, defects and flaws may be subject to crack initiation and crack propagation under long-term service conditions. To study these problems and to support an advanced remnant life evaluation, fracture mechanics procedures are required. Since a more flexible service mode of power plants causes more start up and shut down events as well as variable loading conditions, creep-fatigue crack behavior becomes more and more decisive for life assessment and integrity of such components. For steam power plant forged and cast components, the crack initiation time and crack growth rate of heat resistant steels were determined in long-term regime up to 600 °C. Component-like double edge notched tension specimens have been examined. The results are compared to those obtained using the standard compact tension specimen. Crack initiation time and crack growth rate have been correlated using the fracture mechanics parameter C*. The applicability of the stress intensity factor K I to describe the creep crack behavior is also being assessed. A modified Two-Criteria-Diagram was applied and adapted in order to recalculate crack initiation times under creep-fatigue conditions. Recommendations are given to support the use of different fracture mechanics parameters in order to describe the long-term crack behavior under creep and/or creep-fatigue conditions.