Ultrasupercritical (USC) steam boiler and heat recovery steam generator (HRSG) technology is constantly evolving to improve efficiency and reduce emissions. Currently, temperatures are pushing beyond the capabilities of even the most advanced ferritic steels with some applications requiring nickel-based superalloys. Cost-effective design of these systems requires the application of a variety of alloys representing a range of cost/property trade-offs. CF8C-Plus is a cast austenitic stainless steel recently developed for application in high temperatures similar to those in power plants (600 - 900 °C) with creep strength comparable to several superalloys. This makes it an attractive alternative for those expensive alloys. EPRI, with assistance from PCC subsidiaries Special Metals and Wyman Gordon Pipes and Fittings, has produced and characterized two pipe extrusions nominally 5.25 inch OD x 0.5 inch wall thickness and 6 inch OD x 0.75 inch wall (13.3 x 1.3 cm and 15.2 x 1.9 cm), each about 1000 lbs, to continue to assess the feasibility of using a wrought version of the alloy in power piping and tubing applications. The mechanical properties from these extrusions show performance in the same population as earlier forging trials demonstrating capability exceeding several austenitic stainless steels common to the industry. Creep-rupture performance in these extrusions continues to be competitive with nickel-based superalloys.

High nitrogen steel was manufactured by solid state nitriding and Laminate- rolling at laboratory to study the nitride morphology and creep properties through the TEM, EPMA and creep strain test. Nitriding made the nitride dispersing steels possible. Solid state nitriding of thin plates and those laminate rolling enabled the high nitrogen containing thick plate steel. Precipitated coarse nitrides during the nitriding resolved by normalizing and re-precipitated by tempering finely. Needle type VN was detected in V containing high nitrogen steels. Its coherency seems to affect the creep strength significantly. V precipitated steels indicated the higher creep strength than the steels without VN precipitation. Thermodynamically stable precipitates like VN increases the creep rupture strength. Ti and Zr containing high nitrogen steels also will be evaluated and discussed by the presentation.

Constricted steam oxidation resistance and finite microstructural stability limits the use of 9 - 12 wt.-% chromium ferritic-martensitic steels to steam temperatures of about 620 °C. Newly developed 12 wt.-% Cr steels are prone to Z-phase precipitation, which occurs at the expense of the strengthening precipitates, and therefore suffer an accelerated decline in strength during longterm operation. While the concept of ferritic-martensitic chromium steels thus seems to hit technological limitations, further improvement in steam power plant efficiency necessitates a further increase of steam pressure and temperature. Furthermore increasing integration of intermitting renewable energy technologies in electrical power generation poses a great challenge for supply security, which has to be ensured on the basis of conventional power plant processes. Besides improved efficiency for resource preservation, load flexibility, thermal cycling capability and downtime corrosion resistance will play key roles in the design of tailored materials for future energy technology. Under these preconditions a paradigm shift in alloy development towards improvement of cyclic steam oxidation and downtime corrosion resistance in combination with adequate creep and thermomechanical fatigue strength seems to be mandatory. The steam oxidation, mechanical and thermomechanical properties of fully ferritic 18 - 24 wt.-% chromium model alloys, strengthened by the precipitation of intermetallic (Fe,Cr,Si)2(Nb,W) Laves phase particles, indicate the potential of this type of alloys as candidate materials for application in highly efficient and highly flexible future supercritical steam power plants.

The recently developed 12%Cr steel VM12-SHC is characterized by very good creep properties at temperatures up to 620°C. This new material development exhibits an excellent oxidation resistance in steam atmospheres at the typical application temperature but also at temperatures up to 650°C. In comparison to the existing 9% Cr grades T/P91 and T/P92, VM12-SHC steel opens due to its excellent oxidation behavior, new possibilities for its application as a heat exchanger boiler component. It was found that outside its application temperature range VM12-SHC also shows, as all 9-12%Cr steels, the appearance of the so called Z-phase. This effect was investigated to understand its influence on creep properties of this class of ferritic/martensitic steels aiming at controlling the microstructure stabilities for future grade developments. Creep testing has been carried out in the temperature range between 525°C and 700°C. Selected crept specimens have been investigated using light optical microscopy, SEM with EDX and TEM. In this study, the oxidation behavior of a number of typical martensitic 9-12%Cr steels was compared with the newly developed 12% Cr steel VM12-SHC. The compositions and morphologies of oxide scales formed after 5000 h exposure steels in simulated steam environments as function of temperature were characterized by light optical metallography and scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDX).

Precipitation of Z-phase, Cr(V,Nb)N, is known to negatively affect creep properties of 9-12%Cr steels for power plant applications as it dissolves finely distributed MX particles, (V,Nb)N, especially in high Cr steels. As the Z-phase precipitates slowly as large particles, this causes a net drop in precipitation strengthening. Two model alloys containing 9 and 12%Cr, but otherwise having similar composition, were produced in order to quantify the difference in Z-phase precipitation speed at different Cr levels. The nitride precipitation behavior was followed at different temperatures using TEM and XRD, allowing for a quantification of the Z-phase precipitation. The Z-phase was found to precipitate 20-50 times faster in the 12%Cr steel compared to 9%Cr steel in the temperature range 600- 650°C. The transformation of MX into Z-phase was followed in a Ta containing alloy without V or Nb. In this alloy the Z-phase precipitates very quickly, and thus appears as finely distributed particles which have the same strengthening effect as MX particles. Investigations using atomic resolution microscopy showed how Cr diffuses from the matrix into the TaN MX particles and gradually transforms them both chemically and crystallographically into Z-phase CrTaN particles.

Two Z-phase strengthened test steels with similar chemical composition were studied. The main difference in composition is the addition of 1 wt% Cu into one of the steels (referred to as “ZCu”). Mechanical testing was performed. The impact strength is very different: 3 J vs. 46.3 J, for the original and the Z-Cu steel, respectively. In the original steel that contains no Cu, much more Laves-phase (Fe 2 (W,Mo)) precipitates had formed along the prior austenite grain boundaries than in the steel with Cu addition. This is believed to be the reason for the difference in impact strength. Furthermore, the Cu addition also influenced the morphology of Laves-phase precipitates; fine rod-shaped instead of coarse equiaxed Laves-phase particles were observed in Z-Cu steel in comparison to the original steel. No partitioning of Cu into the Laves-phase particles was detected by using atom probe tomography (APT). The main function of Cu seems to be the formation of Cu precipitates that act as nucleation site for Laves-phase.

The addition of boron without the formation of any boron nitrides during normalizing heat treatment at high temperature minimizes the degradation in creep strength of both base metal and welded joints of 9Cr steel at 650 °C and long times. The enrichment of soluble boron near prior austenite grain boundaries (PAGBs) by the segregation is essential for the reduction of coarsening rate of M 23 C 6 carbides in the vicinity of PAGBs, enhancing boundary and subboundary hardening, and also for the production of same microstructure between the base metal and heat-affected-zone (HAZ) in welded joints, indicating no Type IV fracture in HAZ. Excess addition of boron and nitrogen promotes the formation of boron nitrides during normalizing, which reduces the soluble boron concentration and accelerates the degradation in creep rupture ductility at long times. 9Cr- 3W-3Co-VNb steel with 120 - 150 ppm boron and 60 - 90 ppm nitrogen (MARBN) exhibits not only much higher creep strength of base metal than Gr.92 but also substantially no degradation in creep strength due to Type IV fracture at 650 °C. The pre-oxidation treatment in Ar gas promotes the formation of protective Cr 2 O 3 scale on the surface of 9Cr steel, which significantly improves the oxidation resistance in steam at 650 °C.