This paper reports the results of a collaborative investigation of an ex-service grade 91 bend carried out by the UK generating companies Centrica, SSE, Engie and RWE. As part of the handover exercise for Centrica’s Langage power station in 2009 a number of routine checks were carried out on the main steam and hot reheat grade 91 steam pipework. In some cases low hardness readings were found with subsequent metallurgical replication showing the presence of an aberrant non martensitic microstructure. This led to a more extensive inspection programme on the steam lines and the discovery of other areas of suspect material. A review of the operating capability of the plant, including detailed pipework stress analysis and a pipework peaking assessment, along with the assumption that lower strength grade 91 material was present, led to the steam lines being down rated and returning to service under these revised conditions. At the first C inspection in December 2012, after the HRSG and associated pipework had operated for 18720 hours, a bend with a soft weld, along with a section of the straight pipe on either side, was removed from service. An investigation was undertaken to establish how long this component would have survived, had it been left in service, and to consider the implications for the future operation of the plant.

This paper reports the results of a collaborative small scale creep testing exercise carried out by the UK generating companies Centrica, SSE, Engie and RWE as part of an investigation of an ex-service grade 91 bend.

The impression creep test method using a rectangular indenter has been well established and the applicability of the technique has been supported by the test data for a number of metallic materials at different temperatures and stresses. The technique has proved to be particularly useful in providing material data for on-site creep strength assessments of power plant components operating in the creep regime. Due to these reasons, “standard” assessment procedures using the impression testing method are needed in order for the technique to be more widely used. This paper will first address some key issues related to the use of the impression creep test method, involving the data conversion method, typical test types and validity of the test technique etc. Then some recommendations on a number of practical aspects, such as the basic requirements of test rigs, “standard” specimen geometry, indenter dimensions, sampling procedures for scoop samples, specimen preparation, temperature and loading control, and displacement measurement, are briefly addressed. Finally, applications of the test data to assist with the risk management and life assessment programme of power plant components, particularly those with service-exposed materials, using data obtained from scoop samples, are described. Proposals for future exploitation and for improvement of the technique are addressed.

Grade 91 steel has been widely utilized in power plants over the last 20 years. Its specification worldwide has dramatically increased since the acceptance of Code Case 1943 for this material in 1983. Recent evaluation of a combination of ex-service Grade 91 steel components and virgin material has provided a unique opportunity to independently assess the performance of a combination of base metal and weldments. This approach has been grounded in the fundamental objective of linking metallurgical risk factors in Grade 91 steel to the cross-weld creep performance. Establishing critical risk factors in 9Cr steels is regarded as a key consideration in the integration of a meaningful life management strategy for these complex steels. The potential metallurgical risk factors in Grade 91 steel have been fundamentally divided into factors which affect strength, ductility or both. In this study, two heats of ex-service Grade 91 steel which exhibit dramatic differences in strength and ductility have been evaluated in the ex-service condition and re-heat treated to establish a relevant set of strength:ductility variables. This set of variables includes [strength:ductility]: low:low, medium:low, low:high and medium:high. The influence of these strength:ductility variables were investigated for feature type cross-weld creep tests to better evaluate the influence of the initial base material condition on cross-weld creep performance.

This study is concerned with the creep damage evaluation for the welded joint of modified 9Cr-1Mo steels. A finite element prediction method based on ductility exhaustion approach has been proposed. Degradation of creep ductility under multi-axial stress state has been formulated from the experimental results of notched bar specimens for the base metal and the fine-grained heat affected zone, and has been taken into the damage model. Creep test of welded joint specimen of modified 9Cr-1Mo steel has been conducted to confirm the accuracy of the damage evaluation method. It has been concluded that the predicted trend of creep damage has good agreement with the experimental results, but the predicted rupture time become longer than the experimental results of rupture time.

The application of cold weld repair techniques in the power industry has been well documented. This type of repair is only considered when a conventional repair (involving post-weld heat treatment) is impracticable or the penalties of time and cost for conventional repair are sufficiently high. A typical cold weld repair in the UK has involved low alloy ferritic steel (½Cr½Mo¼V, 2¼Cr1Mo) components welded with nickel based SMAW consumables or ferritic FCAW consumables. Modified 9Cr steel components have been used in UK power plant since the late 1980’s for a number of applications, such as superheater outlet headers, reheat drums and main steam pipework. The problems associated with this material have also been well documented, particularly premature type IV cracking of welds on creep weakened modified 9Cr steel. RWE Generation UK have developed modified 9Cr cold weld repairs on headers, pipework and tubes. These repairs have been underwritten with extensive testing. This paper will describe the work performed on developing T91 cold weld repairs and where they have been applied on power plant.

Martensitic 9Cr steels have been developed which are strengthened by boron in order to stabilize the microstructure and improve their long-term creep strength. Boron plays a key role in these steels by stabilising the martensitic laths by decreasing the coarsening rate of M 23 C 6 carbides, which act as pinning points in the microstructure. In this work two modified FB2 steel forgings are compared. Both forgings have similar compositions but one underwent an additional remelting process during manufacture. Creep tests showed that this additional processing step resulted in a significant increase in time to failure. In order to investigate the effect of the processing route on microstructural evolution during aging and creep, a range of advanced electron microscopy techniques have been used including ion beam induced secondary electron imaging and High Angle Annular Dark Field (HAADF) imaging in the Scanning Transmission Electron Microscope. These techniques have enabled the particle population characteristics of all the second phase particles (M 23 C 6 , Laves phase, BN and MX) to be quantified for materials from both forging processes. These quantitative data have enabled a better understanding of how the processing route affects the microstructural evolution of FB2 steels.

To solve crack problems at the tube elbow induced by high depth-to-width ratio longitudinal defects on the inner wall of boiler tube, a number of testing experiments and testing methods have been applied to analysis on the sensitivity and correspondence of such defects, and it has been found that the flattening test has an outstanding advantage to detect such defects. However, according to relevant standards, the judgment is controversy. It can be noted from the research that if a steel tube with a ratio of wall thickness to outer diameter larger than 0.1 is turned prior to the flattening test, to reduce such ratio to be less than or equal to 0.1, the shortcomings in detection and evaluation of such defects specified in the current relevant standards of many countries can be effectively overcome. The method has been proposed and adopted preliminarily in the relevant Chinese standard.

The piping stress and thermal displacement corresponding to different types of riser rigid support and hanger devices in different installation directions have been calculated by means of finite element analysis, to further analyze the impact on cracking of adjacent steam tee welds exerted by the constraint effect of riser rigid hangers on angular displacement. It can be seen from the analysis that a riser rigid hanger has a constraint effect on angular displacement, and such a constraint effect, however, is weak and limited on the piping stress and thermal displacement, so the piping stress and supports and hangers are not the main reasons for the cracking of tee welds. In addition, the calculation results alert that for an axial limiting hanger of riser with a dynamic axial pipe clamp and rigid struts, its constraint effect on angular displacement has a significant impact on the piping stress and thermal displacement.

Through inner wall oxidation scale thickness measurement, sampling tests and installation of wall temperature measuring device in the boiler, the equivalent wall temperature and its distribution of secondary high temperature reheater tube were estimated and verified, and the temperature field distribution of tube platen which is of single peak distribution in the direction vertical to tube platen and an apparent lower temperature distribution covered by the smoke shield at the side of boiler wall were both obtained. For the middlemost 10CrMo910, the wall temperature of individual tube was getting close to 600°C. Afterwards material state and residual creep life of tube platen were estimated and calculated. The results of estimate and calculation show that the tube platen in the middle is not suitable for further service due to its degraded material states and lower antioxidant ability. Thus with consideration of distribution characteristics of temperature field, parts of tube platens in the middle are proposed to be replaced with T91 tubes. Furthermore, to avoid onsite heat treatment, 10CrMo910 tube covered by the smoke shield in the boiler was reserved, and a small piece of 10CrMo910 tube was welded at the inlet and outlet ends respectively in the manufactory.

The fatigue crack propagation thresholds of SAW weld metal of 25Cr2Ni2MoV simulating product of fossil and nuclear power low pressure turbine rotor at different stress ratios are tested. There is a big dispersity of the test results, even at the same stress ratio. The double logarithm curves of the fatigue crack growth rate and stress intensity factor range are researched. The difference of critical points between stable propagation region and near-threshold region in different specimens is found to be an important cause to the dispersity. Their locations in the specimens can be determined by the method of backward inference. After the observation of the microstructures around the critical points, a good correspondence between the size of prior austenite grain and the maximum size of monotonic plastic zone on the crack tip is confirmed. The difference of the critical points at the same stress ratio is caused by the inhomogeneous microstructures. So the inhomogeneous microstructures in the multi-pass and multi-layer weld metal contribute to the dispersity of the experimental threshold values.

Remaining-life assessment of high temperature components using the small punch (SP) creep testing technique necessitates the evaluation of SP load (F)/uniaxial stress (σ) conversion factor, F/σ, obtained by comparing the SP and uniaxial creep test results. In the present study, the SP creep tests were carried out at 850°C on various Ni-base alloys having different reduction of area in the range of 0.05-0.67 to investigate the influence of creep ductility on the value of F/σ. The F/σ value was determined for each alloy by correlating SP creep rupture data with corresponding uniaxial creep ones. The experimental results revealed that the F/σ value was not well correlated with Vickers hardness, but it increased almost linearly with increasing reduction of area up to around 0.4. This result indicated that the SP creep rupture data could be converted to the uniaxial data if the creep ductility on a given material was available.

High temperature regions in the upper sections of the advanced ultrasupercritical (AUSC) boilers are exposed to temperatures higher than traditional supercritical (SC) boilers and require high strength materials. Use of modified 9-12% Cr materials such as T91 and T92, while meeting the strength requirements, are still under research stage for large-scale fabrication of the membrane walls for several reasons, such as required post weld heat treatment PWHT (ASME Code) or hardness limits on as-welded structures (European codes). The main objective of this paper is to explore alternate tubing materials that do not require a PWHT in the high temperature sections of the AUSC boiler membrane walls. Composite bimetallic tubing with high strength cladding, applied by weld overlay or co-extrusion that may meet the requirement of high operating temperature and high overall strength, is addressed through an alternate design criterion. Bimetallic tubes can replace the single metal tubes made from 9-12% Cr materials. The bimetallic tube is assumed to be fabricated from Grade 23 steel (base tubes) with Alloy 617 overlaid. The alternate design method is based on an iterative analytical solution for the through-wall heat transfer and stresses in a composite tube with temperatures and strength variations of both the materials considered in detail. A number of different analyses were performed using the proposed analytical approach, methodology verified through benchmark solutions and then applied to the membrane wall configurations.