Abstract
Nitridation is a high-temperature material degradation issue that can occur in air and in environments containing nitrogen, ammonia, etc., and in a variety of industrial processes. The nitridation behavior of several commercial nickel- and cobalt-based alloys is reviewed in this paper. The alloys include Haynes 230, Haynes 188, Haynes 625, Haynes 617, Haynes 214, Hastelloy X, and Haynes 233. The environments discussed are high-purity nitrogen gas between 871°C and 1250°C, 100% ammonia gas at 982°C and 1092°C, and a simulated combustion atmosphere at 982°C. The results showed that nitridation occurred in all the environments containing nitrogen. The nitridation attack was strongly influenced by the alloy compositions and the type of oxide formed (i.e., chromia or alumina), as some degree of oxidation was expected in the environments in which residual oxygen was present. Thermal cycling is briefly discussed because the integrity of protective oxides is also an important factor in resisting high-temperature oxidation and nitridation attack.