Abstract
Electron beam melting (EBM) is one of the candidate manufacturing processes for TiAl alloys which have been considered as next generation high-temperature structural materials. The microstructure and mechanical properties of Ti-48Al-2Cr-2Nb (48-2-2) alloy bars fabricated using EBM were investigated, with a particular focus on the effect of processing parameters such as input energy density and building direction. We observed that the microstructure of the alloy bars fabricated using EBM depends strongly on the processing parameters used during the fabrication process of alloy. In particular, the alloy bars fabricated under appropriate processing parameters have a unique layered microstructure composed of duplex regions and equiaxed γ-grain regions (γ bands). Because of their fine microstructure and deformable soft γ bands, the alloy bars with the unique layered microstructure exhibit higher strength and higher ductility at room temperature (RT) than that of cast alloys. In addition, the alloy bars fabricated at an angle between the building direction and the loading axis of 45° show good fatigue properties at RT even without hot isostatic pressing treatment.