Abstract
A trial weld joint of COST F and COST FB2 steels was produced using the GTAW HOT-WIRE method in conditions used in industry for production of welding steam turbine rotors. Conventional long-term creep tests (CCT) to the rupture of this weldment and the base materials were carried out at temperatures ranging from 550 °C to 650 °C in the stress range from 70 to 220 MPa (the longest time to rupture was above 52,000 hours). Creep rupture strength was evaluated using Larson-Miller parameter model. Assessment of microstructure was correlated with the creep strength. Precipitation of Laves phase and structure recovery during creep exposures were the main reasons for the failure which occurred in the heat affected zone of steel COST F. The recently developed simulative accelerated creep testing (ACT) on thermal-mechanical simulator allows the microstructural transformation of creep-resisting materials in a relatively short time to a state resembling that of multiyear application under creep conditions. ACT of samples machined from various positions in the weldment was performed at 600 °C under 100 MPa. Changes in the hardness and the microstructures of the samples, which underwent both types of creep tests, were compared. Small sample creep test (SPCT), another alternative method how to obtain information about the creep properties of materials when only a limited amount of test material is at disposal, were performed. It was shown that the same stress-temperature dependence and relationships are valid in the SPCT as in the CCT. Using a simple load-based conversion factor between the SPCT test and the CCT test with the same time to rupture, the results of both test types can be unified.