Abstract
The microstructures of an advanced Ta-added 9Cr-3Co-2W-Mo steel with increased boron content that has been homogenized at different temperatures were investigated. The chains of coarse W-rich particles were observed in the steel after homogenization at 1150°C for 24 h. These particles remained in the microstructure after normalization and tempering. Such additional dispersion hardening in the initial state of the studied steel decreased the creep rate in transient region. However, the duration of steady state creep and overall creep time was increased in the samples homogenized at 1200°C. Despite of the presence of coarse W-rich particles, the impact toughness of the low-temperature- homogenized steel in the tempered condition was significantly higher than that of the steel homogenized at 1200°C