Abstract
Due to a high degree of mixing between substrate and weld deposit, fusion welding of dissimilar metal joints functionally produce new, uncharacterized alloys. In the power generation industry, such mixing during the application of cobalt-based hardfacing has led to a disconcerting number of failures characterized by the hard overlay welds disbonding. Investigations into this failure mechanism point to the unknown alloy beneath the surface of the hardfacing layer transforming, hardening, and becoming brittle during service. This research describes a methodology for exploring a chemical space to identify alloy combinations that are expected to be safe from deleterious phase formation. Using thermodynamic modeling software and a stepped approach to potential chemistries, the entire phase stability space over the full extent of possible mixing between substrate and weld material can be studied. In this way diffusion effects – long term stability – can also be accounted for even in the case where mixing during application is controlled to a low level. Validation of predictions specific to the hardfacing system in the form of aged weld coupons is also included in this paper. Though the application of this methodology to the hardfacing problem is the focus of this paper, the method could be used in other weld- or diffusion- combinations that are expected to operate in a high temperature regime.