Abstract
Remaining-life assessment of high temperature components using the small punch (SP) creep testing technique necessitates the evaluation of SP load (F)/uniaxial stress (σ) conversion factor, F/σ, obtained by comparing the SP and uniaxial creep test results. In the present study, the SP creep tests were carried out at 850°C on various Ni-base alloys having different reduction of area in the range of 0.05-0.67 to investigate the influence of creep ductility on the value of F/σ. The F/σ value was determined for each alloy by correlating SP creep rupture data with corresponding uniaxial creep ones. The experimental results revealed that the F/σ value was not well correlated with Vickers hardness, but it increased almost linearly with increasing reduction of area up to around 0.4. This result indicated that the SP creep rupture data could be converted to the uniaxial data if the creep ductility on a given material was available.