Abstract
ASME Grade 91 steel seam-welded elbow pipe, which has been used in a USC plant (A-Plant) for about 6 × 104 h, was investigated to clarify the microstructure and remaining creep life of the material at long-term region. SEM and TEM observations were conducted on specimens cut from the welded portions of the intrados and extrados of the elbow, and the number density of creep voids in fine-grained HAZ was measured in the wall-thickness direction. Then, creep rupture tests were performed to examine the remaining life of each portion of the base metal and welded joint. On the basis of the results, it was suggested that the microstructural changes were small and that the cumulative creep damage was also small for the elbow pipe during its use at the USC plant for about 6 × 104 h. The present result was compared with the result of an investigation on Grade 91 steel elbow used in another USC plant (B-Plant) for about 5 × 104 h. The A-Plant material had a creep life about ten times longer than that of the B-Plant material for not only the base metals but also the welded joint. Through the comparison of the investigation results, it was suggested that the difference in the creep deformation property between the base metals of the elbows was the main reason for the difference in their creep lives.