Abstract
Up to now, the amount of supercritical boilers in China has ranked number one in the world. Many supercritical boilers have run for more than 100,000 hours. Creep becomes one of the main reasons for supercritical boiler tubes failure. In this article, the failure of superheater tubes in a supercritical boiler was analyzed, the microstructural evolution of austenitic stainless steel tubes were studied, a full investigation into the failure cause was carried out involving in visual examination, optical microscope, SEM, TEM and XRD. The results show, sigma phase precipitates in this austenitic steel with the extension of service time, sigma precipitates form at grain boundaries by continuous chain. Sigma precipitates are hard and brittle, weaken grain boundaries and cause microscopic damage, eventually lead to boiler tubes failure.