Abstract
The creep rupture properties of welded joints of advanced 9%Cr-Mo-Co-B steel used for 620°C USC steam turbine have been studied. The welded joints were prepared by means of shielded metal arc welding (SMAW). A lot of creep tests have been conducted and the results indicate that fracture usually occurs in the intercritical heat affected zone (ICHAZ) of the welded joint and is typical of Type IV cracking. The microstructure of the HAZ has been investigated by using optical microscopy, SEM and TEM. The degradation mechanism of welded joint of the 9%Cr-Mo-Co-B steel has been explored by analysing the phases of precipitates. Creep voids were observed in the vicinity of the coarse Laves phase particles, resulting in the degradation of the creep rupture properties.