Abstract
Flux cored wires are worldwide used in power generation industry due to their technical and economic advantages. For welding P91 and P92 flux cored wires with a rutile slag system are available for several years. Results of long-term investigations up to 30.000 h show that specimens of all weld metal meet the requirements of the base material. Following the recent demand of reduced Mn+Ni content the chemical composition of all weld metal has been modified. For P91 a matching flux cored wire with Mn+Ni<1wt% and for P92 with Mn+Ni<1.2wt% is now available. In this paper the mechanical properties of all weld metal and welded joints are being presented. Latest developments in cast materials have shown that the so-called CB2 (GX13CrMoCoVNbNB 10-1-1) enables steam temperatures up to 620°C (1148°F). Therefore a matching flux cored wire with low Ni-content has been developed. Results of welding procedure qualification and first experience of manufacturing industrial components show the successful implementation of this new material grade and welding consumable.