Effect of Stress State on Microstructural Change during Creep in Grade 92 Steel Welded Joint

In order to clarify the effect of stress state on microstructural changes during creep, the microstructure was observed in the central part of the cross section of the fine-grained heat-affected zone (FGHAZ) and in the surface region of the FGHAZ in Gr.92 steel welded joint. Creep tests were performed under constant load in air at 650°C, using cross-weld specimens. The creep strength of welded joint was lower than that of base metal. Type IV fracture occurred in the long-term. Creep voids were detected in the FGHAZ after the fracture. Number of creep voids was higher in the central part of the cross section of the FGHAZ than in the surface region of the FGHAZ. It was checked the multiaxiality of stress during creep was higher in the central part of the cross section of the FGHAZ than in the surface region of the FGHAZ. The recovery of dislocation structure occurred after creep in the base metal and the FGHAZ. Mean subgrain size increased with increasing time to rupture. However, there was no difference of change of subgrain size during creep in the central part of the cross section of the FGHAZ and in the surface region of the FGHAZ. The growth of M₂₃C₆ carbide and MX carbonitrides was observed during creep in the base metal and the FGHAZ. Laves phase precipitation occurred during creep. There was no difference of the change of mean diameter of MX carbonitrides in the central part of the cross section of the FGHAZ and in the surface region of the FGHAZ after creep. However, the growth rate of M₂₃C₆ carbide in the FGHAZ was much higher in the central part of the cross section than in the surface region.