Abstract
This paper presents the creep and creep-fatigue crack growth behaviors of 30Cr1Mo1V turbine rotor steel which had been in service for 16 years. Two typical sections of the rotor, i.e. high and low temperature sections, are examined at 538°C, with crack initiation and propagation monitored by D.C. potential drop method in a compact tension (CT) specimen. The material of the high temperature section has the lower resistance to creep and creep-fatigue crack growths than the low temperature section. The creep crack initiation (CCI) time decreases with the increase of initial stress intensity factor. The creep-fatigue crack growth (CFCG) is dominated by the cycle-dependent fatigue process when the hold time at the maximum load is shorter, but it becomes dominated by the time-dependent creep process when the hold time becomes longer. The high temperature section shows a larger influence of time-dependent creep behavior on CFCG than the low temperature section.