Microstructural Evolution in Cast Haynes 282 for Application in Advanced Power Plants

A global movement is pushing for improved efficiency in power plants to reduce fossil fuel consumption and CO₂ emissions. While raising operating temperatures and pressures can enhance thermal efficiency, it necessitates materials with exceptional high-temperature performance. Currently, steels used in power plants operating up to 600°C achieve efficiencies of 38-40%. Advanced Ultra Supercritical (A-USC) designs aim for a significant leap, targeting steam temperatures of 700°C and pressures of 35 MPa with a lifespan exceeding 100,000 hours. Ni-based superalloys are leading candidates for these extreme conditions due to their superior strength and creep resistance. Haynes 282, a gamma prime (γ′) precipitation-strengthened alloy, is a promising candidate for A-USC turbine engines, exhibiting excellent creep properties and thermal stability. This research investigates the microstructural evolution in large, sand-cast components of Haynes 282. Microstructure, referring to the arrangement of grains and phases within the material, significantly impacts its properties. The research examines the alloy in its as-cast condition and after various pre-service heat treatments, aiming to fully identify and quantify the microstructural changes. These findings are then compared with predictions from thermodynamic equilibrium calculations using a dedicated Ni alloy database. The research reveals that variations in heat treatment conditions can significantly affect the microstructure development in Haynes 282, potentially impacting its mechanical properties.