Abstract
Welding processes and fabrication techniques have been studied in the development of Advanced USC boilers. Advanced 9Cr steels, Fe-Ni alloy (HR6W) and Nickel base alloys (HR35, Alloy 617, Alloy 263, Alloy 740 and Alloy 740H) have been selected as candidate materials for the boiler. The weld joints of these alloys were prepared from plates, small diameter tubes and large pipes, and welding procedure tests were performed. In this study, TIG and SMAW were applied. Both welding process produced good weld joints, and they showed good results in bending tests, tensile tests and the Charpy impact test. To select the annealing conditions for stress relief, stress relaxation tests and hardness tests were conducted on the weld joints after various heat treatments. The microstructure was also evaluated by SEM and TEM. Creep rupture tests are being performed for the weld joints with and without heat treatment. The maximum creep rupture tests are expected to take over 100,000 hours. In the study of fabrication techniques, hot bending tests by high frequency induction heating for large pipes and cold/hot bending tests for small diameter tubes were established. After the bending tests, mechanical property tests such as tensile tests, impact tests and creep rupture tests were conducted. The effect of pre-strain on creep strength was studied to take the creep test results after bending into consideration. The creep rupture test will be continued for specimens from weld joints and bending pipes to show their long term reliability.