Creep-resistant austenitic stainless steels are known to be the potential candidate materials for use as super- and re-heater tubes in ultra-super critical (USC) power plants. Among them, ASTM A213/A213M S30432, a novel 18-8 stainless steel (18Cr- 9Ni-3Cu-Nb-N), has attracted considerable attention from electric industry due to its combined lower cost and more excellent performance in contrast to traditional TP347H steel. More than 10 years of service in Japan laid a solid foundation for the steel being selectable USC boiler materials. Steels of S30432 have been recently developed in China during the past few years. This paper presents the evaluation results of S30432 tubes manufactured by four steel plants in China as well as Sumitomo super304H tubes for comparison. A detailed microstructural analysis of the tubes has been performed by using optical and electron microscope, and mechanical properties of the tubes have been evaluated using hardness testing as well as tensile testing up to 700°C. It was found that the impurity elements, nonmetallic inclusions and grain size of the S30432 tubes were well controlled. TEM observation revealed the microstructural changes for a selected batch of S30432 specimens in condition of hot rolled material, as-extruded tube, solution treated tube and 650°C/1000h aged tube. Most attention was paid to the morphology and distribution of precipitates in the microstructure which should be responsible for the enhanced performance of the steel. Although the hardness of all the evaluated tubes was measured to be similar, they showed more or less differences in tensile properties between each other. Creep rupture testing is still in progress, and the steel might exhibit excellent long-term creep rupture strength at 650°C as was predicted from the currently available testing results.

This content is only available as a PDF.