Alloy Digest (2014) 63 (2): Ti-151.
Published: 01 February 2014
... Timetal 7-4 is an alpha + beta alloy with excellent creep resistance and high strength. This datasheet provides information on composition, physical properties, and tensile properties as well as creep. It also includes information on forming. Filing Code: Ti-151. Producer or source: Timet...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (2014) 63 (4): Ti-153.
Published: 01 April 2014
... Grade 2 or Grade 7 at room and elevated temperatures allows material and cost saving through use of thinner sections. Grade 12 is approved by ASME Boiler Code for use up to 316 °C (600 °F). See Fig. 4. Products Available: The producer supplies the material in plate, sheet, and tubing forms, although bar...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1992) 41 (11): Ti-101.
Published: 01 November 1992
... Weldmult 180 145 8 QOQ F. 8 hrs.) Table 4 - COLD FORMABIIXI Y COMPARISON TIMETAL@ 15-3 Ti-6AL-4V Bend 2.5t 4.5t Springhack lSO 16O Bead 511 - Driw (Cup) 46% - Joggle L/d 2 6 d/t 5 3 Flange Stretch 209b+ - Flange Shrink 1% - StretchWrap 15% 3.5% Heat Treatment: Forms Avallable: Solution anneal at 145OOF...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (2007) 56 (8): Ti-141.
Published: 01 August 2007
... Timetal 6-2-4-6 is an alpha-beta alloy with greater strength in thicker sections than Timetal 6-4. This datasheet provides information on composition, physical properties, elasticity, and tensile properties as well as creep and fatigue. It also includes information on forming. Filing Code: TI-141...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1998) 47 (7): Ti-112.
Published: 01 July 1998
... Genersl Characteristics: TIMEXAL. 550 is a medium strength, forgeahle alpha beta alloy. ln the solution treated and aged condition the alloy has superior tensile and fatigue properties compared to TIMETAL 6-4. com- bined with good elevated temperamre. tensile strength, and creep properties up to 400 C...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1992) 41 (8): Ti-100.
Published: 01 August 1992
..., including chlorides. Composition,* wt, %: Tiiet Grade Ti-35A Ti-SOA Ti-65A Common DewGrade 1 fiYP 0.18 Iron 0.20 HyQogm 0.015 CdOll 0.10 Nilrogell 0.03 Tiium Bal *Single values are maximum 2 0.25 020 0.015 0.10 0.03 Bal 3 0.35 0.20 0.015 0.10 0.05 Bal Ti-75A Ti-1OOA 4 0.40 0.40 0.30 030 0.015 0.010 0.10...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (2001) 50 (11): Ti-122.
Published: 01 November 2001
... 23 284 41 38 200 392 85 12 219 32 40 300 572 51 7 163 24 48 400 752 36 5 130 19 51 450 842 31 4 117 17 49 Table 3 Fatigue and Tensile Properties Tensile strength Fatigue limit, 107 cycles Condition MPa ksi MPa ksi Fatigue ratio Smooth, Kt = 1 354 51 ±193 ±28 0.55 Notched, Kt = 3 354 51 ±123 ±18 0.35 ...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1993) 42 (2): Ti-104.
Published: 01 February 1993
...@ 1100 Filing Code: Titanium Alloy II-104 FEBRUARY 1993 - DIGEST- DATA ON WORLD WIDE METALS AND ALLOYS rcloyrkEu- -by:A#oyDipsLInc/201%77-S161 -,a Z~C~W~SO~~D,NJ.O~USOIU.SA TIMETAL 1100 (I-1 100, a hbh strength, high temperature alloy) TIMETALe 1100, a near alpha alloy. was developed for elevated...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1998) 47 (10): Ti-105.
Published: 01 October 1998
...-0.100 in.) Fig. 1 Chemical milling hydrogen pickup for solution-heat-treated (as supplied) condition, 0.060 in. gauge Table 7 Skydrol Resistance Test tampen- Hydrotca tora alaorbed. 'C 'F -Y PPm Comments 177 350 llMETAL6-4 0 0.01 mm (O.ow4 in.) Of thinning lTMErAL2IS 12 Noanack 232 450 nMErAL6-4 >I000...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1992) 41 (10): Ti-80.
Published: 01 October 1992
... (1103) 4 40 w 4986 950-1000 (510-538) 4 (10.2) 160 (1103) 145 (998) 6 10 55 (60) 4987 1050-l 100 (566-593) 4 (10.2) 140 (965) 130 (896) 8 20 80 (88) Table 2 -TYPICAL ELEVATED MECHANICAL PROPERTIES Solution Treated then Aged at 950°F for Eight Hours) Test Ultimate 0.2% Reduction Tensile Temperature...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (1992) 41 (9): Ti-66.
Published: 01 September 1992
... (32 to 212 F) (32 to 6OO F) (32 to 1OOOoF) Thermal conductivity. Btu/sq ft/hrpF/ft Electrical resistivity, microhm-cm Specific best, BtWlWF Modulus of elasticity Beta Transus. F T ELI OF T 0.160 4.43 4.9 x lOA 5.1 x lo-6 5.3 x 10 4 170 0.13 See Table 1 1825k25 996ct14 1805&Z 985f14 Table 2 -GUARANTE...
Journal Articles
Publisher: Journals Gateway
Alloy Digest (2020) 69 (5): Ti-166.
Published: 01 May 2020
... strength and good ductil- ity. Heat Treatment See Table 4 for typical heat treatment conditions. ATI 3-2.5 is generally used in the annealed or in the cold worked plus stress relieved condition. However, due to the small amount of stabilizer present, a small age hardening response is possible from...